The reduction of greenhouse gas is becoming increasingly important for humankind, and vehicles with low CO₂ emissions have a part to play in any reduction initiatives. Diesel engines emit 30% less CO₂ than gasoline engines, so diesel engines will make an important contribution to the overall decrease. Unfortunately diesel exhaust gas contains particulate matter (PM) which may cause health problems, and such PM emissions are regulated by law. In order to reduce PM, especially soot, diesel particulate filters (DPFs) are widely fitted to diesel vehicles. A DPF can remove more than 99% by weight of soot from exhaust gas under normal operating conditions, and they are one of the most important methods to achieve any regulation targets. But if the system malfunctions, the PM emissions may exceed the regulation limit. To detect such PM leakage, on-board diagnostics (OBD) are required.

While metal fiber filters have successfully shown a high degree of particle retention functionality for various sizes of diesel engines with a low pressure drop and a relatively high filtration efficiency, little is known about the effects of lubricant-derived ash on the fiber filter systems. Sintered metal fiber filters (SMF-DPF), when used downstream from a diesel engine, effectively trap and oxidize diesel particulate matter via an electrically heated regeneration process where a specific voltage and current are applied to the sintered alloy fibers. In this manner the filter media essentially acts as a resistive heater to generate temperatures high enough to oxidize the carbonaceous particulate matter, which is typically in excess of 600°C.

Ceramic honeycomb wall flow diesel particulate filters (DPF) have been investigated for use in exhaust gas control of diesel vehicles. However, before they can be used, prevention of thermal shock failure during combustion regeneration is necessary. Studies were conducted on thermal shock failures on 9-inch diameter large volume DPF during regeneration by finite element analyses (FEA). These studies reveal that, within safe limits, maximum thermal stress is almost constant even at different gas flow rates and oxygen concentrations. Regeneration tests were also conducted on large volume DPF of several materials having different pore size distributions. FEA thermal stress was compared with mechanical strength of the material at safe levels.

Ceramic honeycombs have been used as automotive catalyst supports in US, Japan, Europe and other highly urbanized countries. Now, engine output is a great concern for automanufacturers, and reduction of the wall thickness of honeycomb substrates became indespensable for maintenance of gas flow restriction to a certain low level. To reduce wall thickness, material should be strong to maintain canning strength of substrates. Mechanical strength was improved with high density cordierite. However, isostatic strength of whole substrates was still insufficient with reduced thin walls for canning in spite of the material's high mecanical strength. Discussion is carried out on further possibility of improving canning performance of thin wall substrates as well as flow restriction, and warm up characteristics.

Further stringent emission legislation requires advanced technologies, such as sophisticated engine management and advanced catalyst and substrate to achieve high catalytic performance, especially during the light-off phase. This paper presents the results of calculations and measurements of hydrocarbon and carbon monoxide light-off performance for substrates of different wall thickness, cell density and cell shapes. The experimental data from catalyst light-off testing on an engine dynamometer are compared with theoretical results of computer modeling under different temperature ramps and flow rates. The reaction kinetics in the computer modeling are derived from the best fit for the performance of conventional ceramic substrate (6mil/400cpsi), by comparing the theoretical and experimental results on both HC and CO emissions. The calibrated computer model predicts the effects of different wall thickness, cell density and cell shape.

The future emission limits for gasoline fuelled passenger cars require more and more efficient exhaust gas aftertreatment devices - the catalytic converter being one essential part of the complex system design. The present paper summarizes the results of several basic research programs putting major emphasis on the application of highly sophisticated three-way catalyst technologies being taylored for the utilization on ultra thin-wall ceramic substrates. In the first part of the investigation the following effects were examined in detail: Different washcoat loadings at constant PGM-loadings Different volumes of catalysts for constant amounts of PGM and washcoat Similar washcoat technologies at different ratios of WC-loading to precious metal concentration in the washcoat.

Developing ultra thin wall ceramic substrates is necessary to meet stricter emissions regulations, in part because substrate cell walls need to be thinner in order to improve warm-up and light-off characteristics and lower exhaust system backpressure. However, the thinner the cell wall becomes, the poorer the mechanical and thermal characteristics of the substrate. Furthermore, the conditions under which the ultra thin wall substrates are used are becoming more severe. Therefore both the mechanical and thermal characteristics are becoming important parameters in the design of advanced converter systems. Whereas square cells are used world-wide in conjunction with oxidation and/or three-way catalysts, hexagonal cells, with features promoting a homogeneous catalyst coating layer, have found limited use as a NOx absorber due to its enhanced sulfur desorption capability.

To meet stringent emissions regulations, high conversion efficiency is required. This calls for advanced catalyst substrates with thinner walls and higher cell density. Higher cell density is needed because it brings higher mass transfer from the gas to the substrate wall. Basically, the increase in total surface area (TSA) causes higher mass transfer. However, not only the TSA, but the cell shape also has a great effect on mass transfer. There are two main kinds of substrates. One is the extruded ceramic substrate and the other is the metal foil type substrate. These have different cell shapes due to different manufacturing processes. For the extruded ceramic substrate, it is possible to fabricate various cell shapes such as triangle, hexagon, etc. as well as the square shape. The difference in the cell shape changes not only the mass transfer rate, but also causes pressure loss change. This is an important item to be considered in the substrate design.

Net-shape aluminum matrix composite components and test specimens were produced through an advanced pressure infiltration process where molten alloys are infiltrated into ceramic preforms. Test specimens were cast with 4 aluminum alloys with alumina and SiC reinforcements. Specimens were heat treated to T6 and T7 conditions and to a special condition wherein intermetallic particles are precipitated at internal interfaces. Alumina reinforced materials were generally stronger and tougher than silicon carbide reinforced materials. Maximum flexure strengths of 653 and 683 MPa were achieved through alumina reinforced 520 and 295 alloys, respectively. Fracture toughness and Charpy impact values were also determined.

Catalytic performance can be improved by increasing geometric surface area (GSA) and reducing bulk density (BD), namely heat capacity, using high cell-density / thinwall advanced ceramic substrates. The advanced substrates, such as 3 mil/600 cpsi and 2 mil/900 cpsi have improved the catalytic performance over the conventional substrates, and are expected to help in complying with future emission regulations, as well as catalyst downsizing. This paper describes the effects of GSA and BD using Pd-based catalysts. The reduction of hydrocarbons emissions was demonstrated significantly at close-coupled location, and dual bed design was proven effective. The effectiveness at under-floor location was not as significant as the close-coupled location.

This paper proposes a high temperature manifold converter with a thin wall ceramic substrate, such as; 4mil/400cpsi and 4mil/600cpsi. Double-wall cone insulation design was proposed for close-coupled converters to protect the conventional intumescent mat from high temperature. However, the double wall cone insulation is not applicable when the converter is directly mounted to the exhaust manifold without an inlet cone. The prototype manifold converter was tested under hot vibration test with a non-intumescent ceramic fiber mat and retainer rings as a supplemental support. The converter demonstrated durability for 10 hours under 80G acceleration and 100 hours under 60G acceleration with 1,050 °C catalyst bed temperature. The skin temperature of the heat shield was kept below 400 °C.

Partially stabilized zirconia is an insulating ceramic which offers high strength, high thermal expansion, and wear resistance. Low thermal conductivity provides the required insulation, high strength improves reliability, and high thermal expansion provides a simple means of attachment for ceramic engine components. Pistons, cylinder liners, and cylinder heads have been insulated with PSZ and engine tested in an adiabatic diesel engine.

The high-temperature durability of 85 mm tip diameter silicon nitride ceramic radial turbine rotors was evaluated with a hot gas spin test rig. The rotors withstood up to a turbine tip speed of 700 m/s at TIT of 1300°C under partially loaded conditions and 570 m/s at TIT of 1300°C under fully loaded conditions, respectively. The material of the rotors was a post-HIPed silicon nitride. The basic fatigue properties of the material were measured at high temperatures. In the hot gas spin test, the temperature and stress distributions at the turbine blade were calculated with a finite element method. The results of the hot-gas spin test are discussed by means of a failure prediction analysis on the basis of the Weibull statistics.

Theoretical estimates are made of life time of Ceramic Turbocharger Rotor (CTR) for suitable mechanical design and suitable material selection. Life time of CTR is predicted taking into account the stress-temperature distribution in CTR, required failure probability, volume effect of strength and material properties. Three fatigue failure modes which are slow crack growth, oxidation, and creep failure are considered. The stress-temperature distribution in CTR in operation is estimated by means of Finite Element Method numerical analysis. The probabilistic design map is proposed as a function of turbine inlet temperature and tip speed.

New three-dimensional printing technology (3DP) developed at MIT was tried as a manufacturing method to fabricate ceramic preforms for a discontinuously reinforced metal matrix composites. Minor modifications to the “legacy” 3DP technology allowed to produce such preforms successfully. Preforms were then infiltrated with liquid aluminum resulting in composite materials as strong as produced via conventional methods. Net shape connecting rod preforms were 3D-printed and used to produce composite connecting rods without building any molds or tooling using novel Tool-less Mold™ technology.