Search Results

A new state of the art DOC (Diesel Oxidation Catalyst) having superior light-off and exothermic activity for forced regeneration compared to conventional Pt base passive DOC, was investigated for LDD application. The DOC uses the latest Pt/Pd technology resulting cost effective DPF system. The newly developed DOC demonstrated improved catalytic activities from Pt only DOC in model gas or engine bench tests. In this study, DOC at early development stage showed excellent light-off activity in model gas and engine bench test compared to conventional Pt only DOC, however, it showed “extinction” phenomenon which is one of the deactivation mode while the post injection and it was observed when post injection operation was done at lower DOC inlet temperatures, e.g. below 250 C. Temperature profiles along diameter and length into DOC bed while active regeneration suggested extinction would be caused by fouling of supplied hydrocarbons derived from diesel fuel.

Since 2000, an Aluminum Cosmetic Corrosion task group within the SAE Automotive Corrosion and Protection (ACAP) Committee has existed. The task group has pursued the goal of establishing a standard test method for in-laboratory cosmetic corrosion evaluations of finished aluminum auto body panels. A cooperative program uniting OEM, supplier, and consultants has been created and has been supported in part by USAMP (AMD 309) and the U.S. Department of Energy. Prior to this committee's formation, numerous laboratory corrosion test environments have been used to evaluate the performance of painted aluminum closure panels. However, correlations between these laboratory test results and in-service performance have not been established. Thus, the primary objective of this task group's project was to identify an accelerated laboratory test method that correlates well with in-service performance.

There is an increasing global realization about the need for fuel efficient vehicles. An inexpensive way to accomplish this is through mass reduction, and one of the most effective ways that this can occur is through substituting current materials with magnesium, the lightest structural metal. This document describes the results of a U.S. Automotive Materials Partnership (USAMP) sponsored study [1] that examines why magnesium use has only grown 10% per year and identifies how to promote more widespread commercial applications beyond the 5-6 kg of component currently in vehicles. The issues and concerns which have limited magnesium use are discussed via a series of research and development themes. These address concerns associated with corrosion, fastening, and minimal metalworking/non-traditional casting processing. The automotive and magnesium supplier industries have only a limited ability to develop implementation-ready magnesium components.

A new single-brick Ba + alkali metals NOx-Trap catalyst has been developed to replace a two-brick NOx-Trap system containing a downstream three-way catalyst. Major development efforts include: 1) platinum group metals selection for higher HC oxidation with potassium-containing washcoat, 2) alumina and ceria selection, and Rh architecture design for more efficient NOx reduction and 3) NiO to suppress H2S odor. Mitsubishi Motors' 1.8L GDI™ with this Delphi new NOx-Trap catalyst with H2S control achieves J-LEV standard with less cost and lower backpressure compared to the previous model. It is further discovered that incorporation of NiO into the NOx-Trap washcoat is effective for H2S control during sulfur purge but has a negative impact on thermal durability and sulfur resistance. Further study to improve this trade-off has been made and preliminary results of an advanced washcoat design are presented in this paper. Details will be reported in a future publication.

The International Lubricant Standardization and Approval Committee (ILSAC) ATF subcommittee members have compared the two oxidation bench test methods, Aluminum Beaker Oxidation Test (ABOT) and Indiana Stirring Oxidation Stability Test (ISOT), using a number of factory-fill and service-fill ATFs obtained in Japan and in the US. In many cases, the ATFs were more severely oxidized after the ABOT procedure than after the same duration of the ISOT procedure. The relative severity of these two tests was influenced by the composition of the ATFs. The bench test oxidation data were compared with the transmission and the vehicle oxidation test data.

The Automotive Aluminum Alliance in conjunction with SAE ACAP founded a corrosion task group in 2000 with a goal to establish an in-laboratory cosmetic corrosion test for finished aluminum auto body panels, which provides a good correlation with in-service performance. Development of this test involves a number of key steps that include: (1) Establishing a reservoir of standard test materials to provide a well-defined and consistent frame of reference for comparing test results; (2) Defining a real-world performance for the reference materials through on-vehicle tests conducted in the U.S. and Canada; (3) Evaluating existing laboratory, proving ground, and outdoor tests; (4) Conducting statistically designed experiments to evaluate the effects of cyclic-test variables; (5) Comparing corrosion mechanisms of laboratory and on-vehicle tests; and (6) Conducting a round robin test program to determine the precision of the new test. Several of these key steps have been accomplished.

As automobile power needs increase 42-volt electrical systems are being proposed for use in consumer vehicles. One concern when using these new systems is the corrosion resistance of these components, especially in underhood environments. Corrosion is an electrochemical phenomenon and as such can be altered (increased or decreased) by the application of an external current or voltage. Although unintentional, the use of a higher voltage electrical system has the ability to increase corrosion through its normal use. This program evaluated the impact of corrosion on electrical components powered by 14 and 42-volt DC systems. Accelerated corrosion test findings suggested that 42-volt systems may be more susceptible to corrosion, but without proper environmental shielding both supply system can have unacceptable degradation.

Durability requirements for exhaust materials have resulted in the increased use of stainless steels throughout the exhaust system. The conversion of carbon steel exhaust flanges to stainless steel has occurred on many vehicles. Ferritic stainless steels are commonly used for exhaust flanges. Flange construction methods include stamped sheet steel, thick plate flanges and powder metal designs. Flange material selection criteria may include strength, oxidation resistance, weldability and cold temperature impact resistance. Flange geometry considerations include desired stiffness criteria, flange rotation, gasket/sealing technique and vehicle packaging. Both the material selection and flange geometry are considered in terms of meeting the desired durability and cost. The cyclic oxidation performance of the material is a key consideration when selecting flange materials.

A co-operative program initiated by the Automotive Aluminum Alliance and supported by USAMP continues to pursue the goal of establishing an in-laboratory cosmetic corrosion test for finished aluminum auto body panels that provides a good correlation with in-service performance. The program is organized as a task group within the SAE Automotive Corrosion and Protection (ACAP) Committee. Initially a large reservoir of test materials was established to provide a well-defined and consistent specimen supply for comparing test results. A series of laboratory procedures have been conducted on triplicate samples at separate labs in order to evaluate the reproducibility of the various lab tests. Exposures at OEM test tracks have also been conducted and results of the proving ground tests have been compared to the results in the laboratory tests. Outdoor tests and on-vehicle tests are also in progress. An optical imaging technique is being utilized for evaluation of the corrosion.

The Corrosion Task Force of the Automotive/Steel Partnership has developed the SAE J2334 cyclic laboratory test for evaluating the cosmetic corrosion resistance of auto body steel sheet. [Ref. 1] Since the publishing of this test in 1997, further work has improved the precision of J2334. In this paper, the results of this work along with the revisions to the J2334 test will be discussed.