Search Results

Quasi-static tensile properties of TRIP590 steels from three different manufacturers were investigated using digital image correlation (DIC). The focus was on the post-uniform elongation behavior which can be very different for steels of the same grade owing to different manufacturing processes. Miniature tensile specimens, cut at 0°, 45°, and 90° relative to the rolling direction, were strained to failure in an instrumented tensile stage. True stress-true strain curves were computed from digital strain gages superimposed on digital images captured from one gage section surface during tensile deformation. Microstructural phases in undeformed and fracture specimens were identified with optical microscopy using the color tint etching process. Fracture surface analyses conducted with scanning electron microscopy and energy dispersive spectroscopy were used to investigate microvoids and inclusions in all materials.

Accurate material property data in both the elastic and plastic ranges of deformation is essential for accurate material representation in finite element simulations of vehicle systems. Variation of post formed material properties across a part are often of interest in different types of analyses, such as metal forming or fatigue life, for example. Depending on a part's shape it is not always possible to cut standard size tensile test specimens from all areas of interest across the part. Smaller size specimens with curved or tapered gage section may have to be used to promote strain localization and fracture at or near the gage center. This paper presents comparison of quasi-static tensile properties determined using two specimen gage section geometries, straight and tapered. Specifically, the following questions are addressed. How do the engineering strains computed from two-dimensional strain fields obtained by DIC compare to strains measured during standard tensile tests?

Fabric materials have diverse applications in the automotive industry which include upholstery, carpeting, safety devices, and interior trim components. The textile industry has invested substantial effort toward development of standard testing techniques for characterizing mechanical properties of different fabric types (e.g. woven and knitted). However, there are presently no standards for determination of Young's modulus, Poisson's ratio and tensile stress-strain properties required for the detailed modeling of fabric materials in vehicle structural simulations. This paper presents results from uniaxial tensile tests of different automotive seat cover fabric materials. Digital image correlation, a full field optical method for measuring surface deformation, was used to determine tensile properties in both the warp/wale and the weft/course directions. The fabrics were tested with and without the foam backing.

Temperature effects on the deformation and fracture of a commercially produced transformation-induced plasticity (TRIP) steel subject to a two-step quenching and partitioning (Q&P) heat treatment are investigated. Strain field evolution at room temperature is quantified in this 980 MPa grade Q&P steel with a stereo digital image correlation (DIC) technique from quasi-static tensile tests of specimens with 0°, 45°, and 90° orientations. Baseline tensile properties along with the variation of the instantaneous hardening index with strain were computed. Variations of the bake-hardening index were explored under simulated paint bake conditions. Tensile properties were measured at selected temperatures between -100°C and 200°C and the TRIP effect was found to be temperature-dependent due to stress-induced martensitic transformation at lower temperatures versus strain-induced transformation at higher temperatures.

The strain-induced diffusionless shear transformation of retained austenite to martensite during straining of transformation induced plasticity (TRIP) assisted steels increases strain hardening and delays necking and fracture leading to exceptional ductility and strength, which are attractive for automotive applications. A novel technique that provides the retained austenite volume fraction variation with strain with improved precision is presented. Digital images of the gauge section of tensile specimens were first recorded up to selected plastic strains with a stereo digital image correlation (DIC) system. The austenite volume fraction was measured by synchrotron X-ray diffraction from small squares cut from the gage section. Strain fields in the squares were then computed by localizing the strain measurement to the corresponding region of a given square during DIC post-processing of the images recorded during tensile testing.

Tensile behavior of advanced high strength steel (AHSS) grades with strengths up to 980 MPa has been extensively studied. However, limited data is found in literature on the tensile behavior of steels with tensile strengths of the order of 1180 MPa, especially at nominal strain rates up to 500/s. This paper examines tensile flow behavior to fracture of four different 1180 MPa grade steels at strain rates of 0.005/s, 0.5/s, 5/s, 50/s and 500/s using an experimental methodology that combines a servo-hydraulic tester and high speed digital image correlation. Even though the strength increase with the strain rate is consistent between the four different materials, the total elongation increase with the strain rate varies widely. Some insights as to why this occurs from examination of the steel microstructure and variation of retained austenite with strain are offered.

Adiabatic heating during plastic straining can slow the diffusionless shear transformation of austenite to martensite in steels that exhibit transformation induced plasticity (TRIP). However, the extent to which the transformation is affected over a strain rate range of relevance to automotive stamping and vehicle impact events is unclear for most third-generation advanced high strength TRIP steels. In this study, an 1180MPa minimum tensile strength TRIP steel with carbide-free bainite is evaluated by measuring the variation of retained austenite volume fraction (RAVF) in fractured tensile specimens with position and strain. This requires a combination of servo-hydraulic load frame instrumented with high speed stereo digital image correlation for measurement of strains and ex-situ synchrotron x-ray diffraction for determination of RAVF in fractured tensile specimens.