The susceptibility of Advanced High Strength Steels (AHSS) to hydrogen embrittlement (HE) was evaluated on selected high strength sheet steels (DP 600, TRIP 780, TRIP 980, TWIP-Al, TWIP, and Martensitic M220) and the results were compared to data on a lower strength (300 MPa tensile strength) low carbon steel. Tensile samples were cathodically charged and then immediately tensile tested to failure to analyze the mechanical properties of the as-charged steel. The effects of hydrogen on deformation and fracture behavior were evaluated through analysis of tensile properties, necking geometry, and SEM images of fracture surfaces and metallographic samples of deformed tensile specimens. The two fully austenitic TWIP steels were resistant to hydrogen effects in the laboratory charged tensile samples.

This paper reviews the bending fatigue endurance limits reported in the literature for carburized steels. Almost an order of magnitude difference in fatigue limits (210-1950 MPa) is reported. The reasons for this wide range are not clear because of the complexity of interactions between the microstructural, testing and manufacturing systems associated with carburized components. In well characterized specimens, two types of microstructures and fatigue crack mechanisms associated with moderate and high levels of fatigue performance have been identified and are described here. Finally, the effects of selected engineering parameters on the measurement of bending fatigue limits are discussed. The need for more complete experimental characterization of fatigue performance is stressed as a critical step to produce consistent bending fatigue performance at the upper end of that attainable in carburized steels.

In recent years, microalloying has been advocated as a means for producing direct cooled forging steels. Microalloyed steels benefit from vanadium and niobium additions, but the carbonitrides formed by these elements are not stable at high temperatures. Micro-additions of titanium, which form a fine dispersion of carbonitrides that are stable at high temperature, have been promoted as an approach fox maintaining a fine austenite grain size at high forging temperatures. In this work two microalloyed steels were examined, 1522MoV and 1522MoV with 0.011 titanium addition. The effect of the titanium additions on the grain size and high temperature flow strength were studied. The titanium addition has a significant effect on maintaining a small austenite grain size at temperatures up to 1300°C. High temperature stress-strain data indicate that titanium causes an increased flow strength at 1100°C and 1200°C especially at higher strain rates.

The influence of coatings on fatigue behavior has been examined for the following commercially produced sheet steels: uncoated titanium stabilized interstitial-free (IF); electrogalvanized titanium stabilized IF; hot-dip galvanized aluminum killed, drawing quality (AKDQ); and galvannealed AKDQ. Fully reversed bending fatigue tests were conducted at ambient temperature on Krouse-type flexural fatigue machines. A dependence of crack development was observed and correlated to the microstructure and properties of the different coatings. Furthermore, a functional design relationship for each material was determined through stress-life analysis. The experimentally determined fatigue properties were compared to conventional estimates based on tensile properties which ignore coating effects. The results of this work suggest that ductile coatings may enhance fatigue resistance, while brittle coatings may reduce fatigue life.

The bending fatigue performance of high temperature (1050 °C) vacuum carburized Nb modified 8620 steel, with niobium additions of 0.02, 0.06 and 0.1 wt pct, was evaluated utilizing a modified Brugger specimen geometry. Samples were heated at two different rates (20 and 114 °C min-1) to the carburizing temperature resulting in different prior austenite grain structures that depended on the specific Nb addition and heating rate employed. At the lower heating rate, uniform fine grained prior austenite grain structures developed in the 0.06 and 0.1 Nb steels while a duplex grain structure with the presence of large (>200 μm grains) developed in the 0.02 Nb steel. At the higher heating rate the propensity for abnormal grain growth was highest in the 0.02 Nb steel and complete suppression of abnormal grain growth was achieved only with the 0.1 Nb steel.

A series of bending fatigue tests were conducted and S-N data were obtained for two groups of 4320 steel samples: (1) carburized, quenched and tempered, (2) carburized, quenched, tempered and shot peened. Shot peening improved the fatigue life and endurance limit. The S-N data exhibited large scatter, especially for carburized samples and at the high cycle life regime. Sample characterization work was performed and scatter bands were established for residual stress distributions, in addition to fracture and fatigue properties for 4320 steel. Moreover, a fatigue life analysis was performed using fracture mechanics and strain life fatigue theories. Scatter in S-N curves was established computationally by using the lower bound and upper bound in materials properties, residual stress and IGO depth in the input data. The results for fatigue life analysis, using either computational fracture mechanics or strain life theory, agreed reasonably well with the test data.

The effect of B and Si additions on fracture and fatigue performance of vacuum carburized 4320 steel and modifications of 4320 steel containing additions of Si (1.0 and 2.0 wt pct) and B (0 and 17 ppm) was evaluated by bending fatigue testing. Three rates of gas quenching, in 10 bar nitrogen and 15 and 20 bar helium, were used to cool specimens after carburizing. The B, protected by Ti additions, together with the Si additions, increased core hardenability. The B/Si modified steels showed no improvement in fatigue resistance, as measured by endurance limits established by 10 million cycle runouts without fracture. However, scanning electron microscopy showed that Si reduced sensitivity to intergranular fracture or quench embrittlement, a major cause of bending fatigue crack initiation, and contributed to variable fatigue performance, with both low-cycle failures and runout performance at applied stresses significantly above measured endurance limits.

High strain rate test methods to obtain strain-rate dependent sheet steel tensile properties are considered. A tensile test method for sheet steels was developed to obtain accurate stress-strain data over the strain rate range from 0.001 s-1 to 500 s-1 using a servo-hydraulic test machine and tensile samples instrumented with strain gages. Results on several different automotive sheet steels, including interstitial free (IF), high strength low alloy (HSLA), dual phase (DP), and transformation induced plasticity (TRIP) steels, are presented. The results show that strain rate response differs between the various alloy systems. These results are compared with previously published data on strain-rate dependent steel properties. The importance of stress-strain curve shapes, which depend on alloy system, on energy absorption calculations using areas under stress-strain curves are also described.

Knowledge of high strain-rate deformation behavior of automotive body structural materials is of importance for design of new vehicles with improved crash-energy management characteristics. Since a large range of plastic strains is encountered during the forming process prior to assembly, the mechanical behavior of sheet steels under high strain rate deformation conditions must be understood after pre-straining, in addition to the as-produced condition. This paper presents the compression testing methodology employed to examine these properties, and focuses on the effects of quasi-static pre-strains (from 0 to 20%) on the subsequent behavior of a low carbon interstitial free steel tested over a broad range of strain rates (from 10−2 to 103s−1). The results suggest that the increase in yield stress associated with increasing strain rate is not substantially influenced by prior cold work.

The effects of deep rolling were evaluated by reviewing the fatigue performance of three medium-carbon (0.4 C) bar steels representing microstructural classes characteristic of forging steels used for crankshaft and other automotive applications. Deep rolling is a surface deformation process whereby a radially symmetric work piece undergoes a surface deformation operation. The steel grades included a quenched and tempered alloy steel (4140) that demonstrated a high yield stress and low strain hardening rate, a non-traditional bainitic experimental grade (1.2 Mn, 0.72 Si) containing high amounts of retained austenite with low yield stress and high strain hardening rate, and a ferritic/pearlitic grade (1.3 Mn, 0.56 Si) with a low yield stress and medium strain rate hardening rate. A reproducible test methodology to assess fatigue behavior was developed, based on flex-beam, fully reversed, S-N type laboratory fatigue testing.

The effectiveness of three different techniques, designed to improve the bending fatigue life in comparison to conventionally processed gas-carburized 8620 steel, were evaluated with modified Brugger bending fatigue specimens and actual ring and pinion gears. The bending fatigue samples were machined from forged gear blanks from the same lot of material used for the pinion gear tests, and all processing of laboratory samples and gears was done together. Fatigue data were obtained on standard as-carburized parts and after three special processing histories: shot-peening to increase surface residual stresses; double heat treating to refined austenite grain size; and vacuum carburizing to minimize intergranular oxidation. Standard room-temperature S-N curves and endurance limits were obtained with the laboratory samples. The pinions were run as part of a complete gear set on a laboratory dynamometer and data were obtained at two imposed torque levels.

Crack initiation and propagation in an SAE 4320 steel gas carburized to a 1.0 mm case depth was examined in specimens subjected to bending fatigue. Cellulose acetate replicas of incrementally loaded specimens showed that small, intergranular cracks were initiated during static loading to stress levels just above the endurance limit. The intergranular cracks arrest and serve as initiation sites for semi-elliptical, transgranular fatigue crack propagation. The maximum depth of stable crack propagation was between 0.17 and 0.23 mm, a depth which corresponds to the maximum hardness of the carburized case. Three equations which provide approximations to the stress distribution in the fatigue specimens were used to calculate KIC for the carburized case with values of maximum applied stress and measured stable crack geometry.

Three heats of 0.40% carbon microalloyed steel, containing either 0.03 % or 0.10% sulfur, and with and without a 0.09% vanadium addition, were subjected to metallographic analysis and mechanical property testing. Bars were heated to austenitizing temperatures, between 1000°C and 1300°C. Significant amounts of intragranular ferrite, which has been associated with improved toughness, formed only in specimens containing vanadium and high sulfur which were austenitized above 1100°C. The balance of the microstructure consisted of ferrite which formed at prior austenite grain boundaries and large amounts of pearlite. High densities of manganese sulfide particles in the steels with high sulfur content effectively retarded austenite grain growth. The formation of significant amounts of intragranular ferrite decreased mean free ferrite spacing, effectively refined the pearlite structure, and lowered the Charpy V-notch impact transition temperature.

Quenching & Partitioning (Q&P) is receiving increased attention as a novel Advanced High Strength Steel (AHSS) processing route as promising tensile properties of the “third generation” have been reported. The current contribution reports hole expansion ratios (HER) of Q&P steels and compares the values with HERs obtained for “conventional” AHSS processing routes such as austempering and Quench & Tempering (Q&T). Intercritically annealed C-Mn-Al-Si-P and fully austenitized C-Mn-Si microstructures were studied. Optimum combinations of tensile strength and HER were obtained for fully austenitized C-Mn-Si Q&P samples. Higher HER values were obtained for Q&P than for Q&T steels for similar tempering/partitioning temperatures. Austempering following intercritical annealing results in higher HER than Q&P at similar tensile strength levels. In contrast, Q&P following full austenitization results in higher hole expansion than austempering even at higher strength levels.

Five heats of vanadium-microalloyed steel with carbon contents from 0.29% to 0.40% and sulfur contents from 0.031% to 0.110% were forged into automotive spindles and air cooled. Three of the steels were continuously cast whereas the other two were ingot cast. The forged spindles were subjected to microstructural analysis, mechanical property testing, full component testing and machinability testing. The microstructures of the five steels consisted of pearlite and ferrite which nucleated on prior austenite grain boundaries and predominantly on intragranularly dispersed sulfide inclusions of the resulfurized grades. Ultimate tensile strengths and room temperature Charpy V-notch impact toughness values were relatively insensitive to processing and compositional variations. The room temperature tensile and room-temperature impact properties ranged from 820 MPa to 1000 MPa (120 to 145 ksi) and from 13 Joules to 19 Joules (10 to 14 ft-lbs), respectively, for the various steels.

The bending fatigue performance of four heats of carburized, commercially-produced SAE 4320 steel was evaluated. Simulated gear tooth in bending (SGTB) cantilever beam specimens from each heat were identically carburized and fatigue tested in the direct quenched condition after carburizing. The microstructure and fracture surfaces of all specimens were characterized with light and electron microscopy. The four direct quenched sets of specimens performed similarly in low cycle fatigue. Endurance limits among the direct quenched specimens ranged between 1100 and 1170 MPa (160 and 170 ksi) and intergranular cracking dominated fatigue crack initiation. An additional set of specimens from one of the heats was reheated after carburizing. The fatigue performance of the reheated specimens was superior to that of the direct quenched specimens in both the low and high cycle regions. The effects of inclusion content, microstructure, and residual stresses on fatigue performance are discussed.

The paint deformation behavior in fully prepainted sheet steel intended for outer automobile body panels is examined in three categories: paint sliding behavior during forming, paint surface roughening during straining leading to loss of coating reflectivity, and dry heat cracking (i.e. time and temperature dependent post-forming paint cracking resulting from viscoelastic strain relaxation). The main findings are: frictional behavior is dictated by the outer coating while pigment particles tend to decrease the measured coefficient of friction; the loss of distinctiveness of image with strain is a result of shear band formation, an inherent deformation mechanism within the polymer coatings; and, dry heat cracks evolve in a two step process where crack nuclei develop during forming and grow as a result of viscoelastic strain relaxation in the coating upon subsequent exposure to heat.

The bending fatigue performance of gears, cantilever beam specimens, and notched-axial specimens were evaluated and compared. Specimens were machined from a modified SAE-4118 steel, gas-carburized, direct-quenched and tempered. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray analysis for residual stress and retained austenite measurements, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. The case and core microstructures, prior austenite grain sizes and case hardness profiles from the various types of specimens were similar. Endurance limits were determined to be about 950 MPa for both the cantilever beam and notched-axial fatigue specimens, and 1310 MPa for the single gear tooth specimens.

The effects of subzero treatments on the bending fatigue performance of carburized gear steels were investigated by cantilever bending fatigue testing. Specimens were machined from SAE-4320 and SAE-9310 bar stock steel, gas-carburized, quenched, tempered at 175°C, subzero cooled to -73°C and -196°C, and tempered at 175°C. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray diffraction for residual stress and retained austenite contents, microhardness testing, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. Refrigeration treatments caused additional transformation of retained austenite and increased surface hardness and compressive residual stresses. Bending fatigue endurance limits for the SAE-4320 specimens were determined to be 1310 MPa for the as-carburized condition, 1170 MPa for the -73°C condition, and 1280 MPa for the -196°C condition.

Prediction of fatigue performance of large structures and components is generally done through the use of a fatigue analysis software, FEA stress/strain analysis, load spectra, and materials properties generated from laboratory tests with small specimens. Prior experience and test data has shown that a specimen size effect exists, i.e. the fatigue strength or endurance limit of large members is lower than that of small specimens made of same material. Obviously, the size effect is an important issue in fatigue design of large components. However a precise experimental study of the size effect is very difficult for several reasons. It is difficult to prepare geometrically similar specimens with increased volume which have the same microstructures and residual stress distributions throughout the entire material volume to be tested. Fatigue testing of large samples can also be a problem due to the limitation of load capacity of the test systems available.