Forging simulations with a 1522 steel microalloyed by additions of 0.25% Mo, 0.13% V and 0.01% Ti were performed on a laboratory thermomechanical processing simulator. The forging conditions included a strain rate of 22s-1, 50% strain, and temperatures in the range from 1200°C to 950°C. The true stress was found to increase with decreasing deformation temperature for all values of instantaneous true strain. The maximum flow stress increased two-fold as deformation temperature decreased from 1200°C to 950°C, and the recrystallized austenite grain size decreased by a factor of two for this same decrease in temperature. Microstructures evolve from bainitic/ferritic at a cooling rate of 1.4°C/s, to fully martensitic at 16.8°C/s, independent of deformation temperature. Room temperature hardnesses depended primarily on cooling rate and were essentially independent of deformation temperature.

The effects of elevated testing temperature on the fatigue behavior of carburized steel were evaluated by testing modified Brügger bending fatigue specimens at room temperature, 90 °C and 150 °C. SAE 4023, SAE 4320, and SAE 9310 steel were studied to assess the influence of alloy content and stability of retained austenite. Fatigue samples were gas-carburized and tested in air at 30 Hz with a stress ratio of 0.1. An infrared spot lamp was used to heat samples to 90 °C (150 °F) or 150 °C (302 °F) during testing. S-N curves were developed for the room temperature baseline tests as well as elevated temperature tests. The endurance limits determined are as follows: SAE 4023-RT (1170 MPa), SAE 4023-90°C (1140 MPa), SAE 4320-RT (1210 MPa), SAE 4320-90°C (1280 MPa), SAE 9310-RT (1380 MPa), SAE 9310-90°C (1240 MPa).