Search Results

This paper examines some key aspects of the manufacturing process that “ Transformation Induced Plasticity” (TRIP) steels would be exposed to, and systematically evaluate how the forming and thermal histories affect final strength and ductility of the material. We evaluate the effects of in-service temperature variations, such as under hood and hot/cold cyclic conditions, to determine whether these conditions influence final strength, ductility and energy absorption characteristics of several available TRIP steel grades. As part of the manufacturing thermal environment evaluations, stamping process thermal histories are included in the studies. As part of the in-service conditions, different pre-straining levels are included. Materials from four steel suppliers are examined. The thermal/straining history versus material property relationship is established over a full range of expected thermal histories and selected loading modes.

This paper examines the effects of fusion zone size on failure modes, static strength and energy absorption of resistance spot welds (RSW) of advanced high strength steels (AHSS). DP800 and TRIP800 spot welds are considered. The main failure modes for spot welds are nugget pull-out and interfacial fracture. Partial interfacial fracture is also observed. The critical fusion zone sizes to ensure nugget pull-out failure mode are developed for both DP800 and TRIP800 using the limit load based analytical model and the microhardness measurements of the weld cross sections. Static weld strength tests using cross-tension samples were performed on the joint populations with controlled fusion zone sizes. The resultant peak load and energy absorption levels associated with each failure mode were studied using statistical data analysis tools. The results of this study show that the conventional weld size of can not produce nugget pull-out mode for both the DP800 and TRIP800 materials.

This paper examines the effects of failure modes on the static strength and total energy absorption of aluminum spot-welded samples using experimental, statistical, and analytical approaches. The main failure modes for aluminum spot welds are nugget pullout and interfacial fracture. Two populations of aluminum spot welds were studied. Within each population, coupon configurations of lap shear, cross tension and coach peel were considered. Thirty replicate static strength tests were performed for each coupon configuration. The resulted peak load and energy absorption level associated with each failure mode was studied using statistical models. Next, an analytical model was developed to determine the failure mode of an aluminum resistance spot weld based on stress analysis. It is found that weld size, sheet thickness, and level of weld porosity and defects are the main factors determining the cross tension failure mode for an aluminum spot weld.

This paper presents the coupon performance data of friction stir welded tailor welded blanks (TWBs) joined to a monolithic aluminum sheet by self-piercing rivets (SPRs). Uniaxial tensile tests were performed to characterize the joint strength and the total energy absorption capability of the TWB/monolithic sheet joint assemblies. Cyclic fatigue tests were also conducted to characterize the fatigue behavior and failure mechanisms of the jointed assemblies. This study provides data for the automotive designer to determine whether friction stir welded aluminum TWB/monolithic sheet joints are within the target joint strengths for a particular application if it should be pierced during the assembly process.

Automobile body and truck cab structures are composed primarily of stampings formed from monolithic and constant gage blanks. Cost and weight penalties can arise when strength or other requirements in one small area of the part leads to the use of a material or gage that is overmatched to the needs of the rest of the stamping. Tailor Welded Blanks (TWBs) are hybrid sheet products composed of either different materials or different thickness sheets that are joined together, then subjected to a stamping operation to create a formed assembly. The strategy is employed generally to save weight and material costs in the formed assembly by placing higher strength or thicker sections only where needed. The forming or stamping process requires the joint to be severely deformed along with the parent sheets. Aluminum TWBs for automotive applications are particularly problematic because of the low formability of aluminum weld metal.