Thin film sensors are often used for in-situ measuring. They are composed of a sensor/conductor layer and insulation layers on either side. However, delamination often occurs between the insulation layers and the sensor/conductor layer and makes the sensor life span shorter. This problem is found especially when there is continuous stress caused by the cyclic change of temperature, sliding and tension. By observing the microstructure of the sensor with transmission electron microscope (TEM), it was found that the adhesion force at the interface between the insulation layer and the sensor/conductor layer, where delamination occurs, is not strong enough, because the interface is too flat. By deposition a thin insulator layer with rough surface on the normal insulation layer, the delamination was successfully suppressed.

It is experimentally known that the surface color of bearing balls gradually becomes brown during long term operation of the bearings under appropriate lubrication conditions. That exhibits the possibility of an estimation method for residual life of ball bearings without any abnormal wear on the surfaces by precise color measurements. Therefore, we examined what set colors on bearing balls by surface observation using scanning electron microscopy and subsurface analysis using transmission electron microscopy. Results showed that an amorphous carbon layer had gradually covered ball surfaces during operation of the bearings. The layer not only changed ball color but also made overall ball shapes closer to a complete sphere. The report also introduces a uniquely developed color analyzer which enabled color measurements on metallic surfaces, such as the above-mentioned balls.