Search Results

Fuel tank in vehicle must hold the fuel in a stable way under any driving condition. However, the fuel tank might not conserve the fuel firmly in case a crack emerged while the fuel tank is exposed to different driving condition. Basically, when the engine is in purging at a normal ambient temperature before fuel boiling, the pressure inside the fuel tank decreases. However, the pressure inside a fuel tank increases while a vehicle is driven at extreme hot ambient temperature as fuel is boiling. This repetitive pressure change in the fuel tank comes with fuel tank’s physical expansion and shrink, which would cause a damage to the fuel tank. The main purpose of this research is to investigate the root cause of why fuel tank cracks at a fatigue point. We also aim to set up the method of how to test durability of the fuel tank in association with the pressure inside the tank.

Aluminum steering knuckles are widely employed for weight reduction and improvement of ride & handling performance. In this study, a high strength aluminum alloy for cast-forged knuckle was designed to achieve higher mechanical properties than those of the conventional foundry alloy. Using this alloy, high strength knuckles were manufactured and performed test of mechanical properties, suspension module strength and durability. The strength and the elongation of the developed knuckle were increased by 20% and 40%, respectively, as compared with the conventional alloy. Also this knuckle passed the static strength and durability test of the front suspension module.

There have been strong moves in recent years to introduce the metal matrix composites concept into higher volume applications, notably the automotive field where large volume production and lower material costs are required. The wettability between reinforcing materials and base material is one of important factors for the strength of composites and its manufacture. The main objective of this paper is to establish a basic understanding of wetting phenomena in SiC/liquid aluminum and aluminum alloy systems. In the present paper, results from the sessile drop method are reported for the effects on the wetting angle, θ, of free silicon in the silicon carbide substrate and of alloying additions of silicon, copper or magnesium to the aluminum drop for the temperature range 700-900 or 1400°C in the titanium-gettered vacuum (1.3 x 10-2 / 1.3 x 10-3 Pa).

Al matrix composites containing alumina (Al2O3) fibers are fabricated by the low pressure (25MPa) squeeze infiltration process which is suitable for the low cost mass production. Mechanical properties at room temperature as well as elevated temperatures (250°C, 350°C) are improved due to the presence of reinforcements. Upto 350°C, composites maintain a reasonable strength, which is much better than strength of the conventional Al alloy. Composites have equivalent wear rates to those of Ni - resist cast iron. Wear behavior is changed with the sliding speed. At low sliding speed, wear proceeds by the excessive failure of matrix and fiber, whilst, at higher sliding speed, matrix fracture near fiber plays a major role in wear. Wear resistance of 125°C is inferior to that of room temperature due to the reduction of mechanical properties followed by matrix softening and poor bonding.

The objective of this study is to investigate mechanical properties and fatigue crack propagation behavior in hybrid metal matrix composites by squeeze infiltration method (15% Al2O3 + SiCw/6061Al). The mechanical properties of Al2O3+SiCw/Al composites including tensile strength, yield strength, Young's modulus, were improved compared with those of unreinforced alloy and Al203/Al composites. The hybrid composites were more ductile than Al2O3/Al composites. Fatigue crack propagation rates of both Al2O3/Al and Al2O3+SiCw/Al composites showed a similar behavior in region II. Their propagation rates were higher in entire ▵K region compared with that of 6061 Al alloy. From the crack path morphology, fatigue cracks propagated linearly and smoothly in 6061 Al alloy. However, in the metal matrix composites cracks tend to avoid the reinforcements promoting crack deflection. It was observed that crack deflection enhanced crack closure due to wedging phenomenon.

The effects of tempering on carburized Cr-Mo gear steel were investigated through mechanical and fatigue tests. Specimens were carburized at 900°C for 180 minutes, and then oil quenched at 150°C for 10 minutes of holding time and cooled to room temperature. The subsequent tempering process was performed to 160°C for 90 minutes. Surface hardness and residual compressive stress were decreased by tempering treatment, whereas tensile strength, yield strength and impact energy were increased. Bending fatigue endurance limits for both tempered and untempered specimens were same as 779MPa. The strength of roller contact fatigue is also not greatly influenced by tempering treatment. Thermal distortion for carburized transfer driven gear before and after tempering exhibited a similar distribution. Microstructural changes during tempering were also discussed.

The banded microstructure of pearlite and ferrite in normalized alloy steel is susceptible to thermal distortion during carburizing process due to its unidirectional orientation parallel to rolling direction. The planetary gears with material of banded microstructure have been experienced in high thermal distortion during carburizing and quenching process and result in uneven surface hardness and effective case depth at the inside of pinion gear after honing. These defects played failure initiation site roles in durability test during development of new automatic transmission. The galling between the contacting components in severe lubricating system was the main failure mechanism. Double normalizing at 920 °C was designed to resolve the banded microstructure of normalized alloy steel. The microstructure and grain size of the double heated steel became equiaxed and fine due to homogenizing and recrystallization through double heat treatment.

In the latest paper [10], we presented our work based on experiments studying MPU (Metal Pick Up) of the pad and scoring(scratching) of the disc. The main component of MPU was iron “Fe”. If the roughness of the disc was small, the content of iron “Fe” was increased and the segregation of that was decreased especially in initial condition. In this study, we extended our study based on the results by adding some additional factors such as the location of the roughness of the disc, the coefficients brake pad friction, and disc slots. We made various discs of different roughness boundaries and slots, and pads of pad friction coefficients; and conducted two types of tests for whether a slot is present or not with the other same conditions to confirm the impact of the scoring. We find and believe that our experimental data should serve a useful guideline for reducing MPU of the pad and scoring of the disc.

Reducing unsprung mass of the car is a representative method to enhance the ride & handling performance and fuel efficiency. In this study, brake disc weight is reduced 15∼20% using a hybrid type material. The basis for this study is the separation of the friction surface and HAT(mounting part). Aluminum material is applied in the HAT for a light weight effect. Gray iron is applied in the friction surface section to maintain braking performance. Two types of joining between aluminum and cast iron are developed. One is the aluminum casting method utilizing a gray iron insert and the other is a bolted assembly method. Detailed structure, process and material are optimized using try-out & dynamometer experiments. The Reliability of this development is proved through durability (dynamometer and vehicle) testing.