A simple testing method is proposed in order to investigate ductile fracture in crashed automotive components made from advanced high strength steels. This type of fracture is prone to occur at spot-welded joints and flange edges. It is well known that the heat affected zone (HAZ) is a weak point in high strength steel due to the formation of annealed material around the spot-welded nugget, and the flange edge also has low ductility due to the damage caused by shearing. The proposed method is designed to simulate a ductile fracture which initiates from a spot-welded portion or a sheared edge in automotive components which are deformed in a crash event. Automotive steel sheets with a wide range of tensile strengths from 590MPa to 1470MPa are examined in order to investigate the effect of material strength on fracture behavior. The effects of material cutting methods, namely, machining and shearing, are also investigated.

Vibration damping steel sheets (VDSS), which have sandwich structures with intermediate layers of resin, have been studied. The most important characteristics of VDSS for inner panels of automotive vehicles are the vibration damping properties, press formability and spot weldability. Vibration damping properties, which are quantified by loss factor,η, were influenced by both tanδ, which indicates damping capacity of resins, and elastic modulus of core resin. From a view point of vibration damping properties, resins with larger tanδ and relatively lower elastic modulus were favorable. Because these mechanical characteristics vary considerably with temperature, it is important to select the most suitable resin for the service temperature range. The relationship between noise reduction effect and loss factor of VDSS were also studied. It was experimentally confirmed that noise reduction effect of VDSS is proportional to the logarithm of their loss factor.

In order to develop a new carburizing steel material that realizes an intermediate heat treatment-free process in parts manufacturing, the cold forgeability of the as-rolled steel and suppression of abnormal grain growth of austenite were studied. It was shown that adjustment of addition amount of Si, Mn and Cr, suppression of dynamic strain aging during cold forging, and an increase of ferrite fraction by controlled rolling contribute to the reduction of deformation resistance. However, Nb precipitation control by fully utilizing mill manufacturing processes was also necessary for suppression of abnormal grain growth of austenite. A new steel for carburizing was developed by integrating these technologies, making it possible to eliminate annealing before cold forging and normalizing before carburizing simultaneously. Thus, the developed steel is an important innovation in the parts manufacturing process.

This paper describes the lap welding of Zinc-coated steel sheet using a high power continuous wave YAG laser. The well-known problem of welding the Zinc-coated sheet is related to the low boiling point of zinc compared with the melting point of steel. During lap welding, zinc coating at the interface vaporize rapidly and causes defects1)2). In this study, therefore, lap welding was performed by YAG laser. The effects of type of coating layer, welding conditions, tensile strength and corrosion resistance after electro-deposition was examined. It was found that the weldability of coated steel is different by type of coating. Zn-Ni coated steel showed good weldability, but galvanealed steel inevitably pore pits with no gap set up. These defects not only lower the strength of joint, but also produce irregular bead where easily corroded after electro-deposition.

With society demanding automobiles that provide higher fuel efficiency, safety of occupants in collisions and that at the end of their service life can be recycled with low environmental impact, the steel industry is tackling the needs of the automobile industry by developing ever-higher performance steel materials and simulation technologies that can demonstrate the performance of steel materials at the development stage without the need for costly prototype testing. In this paper, weight reduction of automobile body in Japan will be discussed. The main items will be as follows: (1) Development of Automobile Steel Sheets, (2) Materials for Automobile Bodies, (3) Materials and Technologies (Tailored Blanks, Hydroforming and Locally Quenching) for Reducing the Weight of Panels and Reinforcing members, (4) Future Prospects.

A method of fatigue life prediction of spot welded joint under multi-axial loads has been developed by fatigue life estimation working groups in the committee on fatigue strength and structural reliability of JSAE. This method is based on the concept of nominal structural stress ( σ ns) proposed by Radaj and Rupp, and improved so that D value is not involved in stress calculation. The result of fatigue life estimation of actual vehicle with nominal structural stress which was calculated through newly developed method had very good correlation with the result of multi-axial loads fatigue test carried out with test piece including high strength steel.

Galvannealed steel sheet (GA) is very extensively used for vehicle panels. However ζ-phase (FeZn13) in GA coat causes poor stamping formability. Previously, there were no easy methods to evaluate the influence of ζ-phase on the frictional characteristics other than the X-ray diffraction method. This study will discuss the development of a new testing method: Dr. STAMP Method that is both efficient and convenient with pin-on-disc tester.

New 440MPa class high-strength steel, which had high r-value(1.6) and elongation(38%), was applied to outer-panel for the first time in the world. In this development FEM simulation was carried out to clarify the necessary steel properties, and the production conditions in strip mill were established. 10-kg weight reduction was realized by using this steel.

Tensile testing technique for the small sample was newly developed. Small tensile specimens with gage length of 1mm were taken from spot welds of high tensile strength steel sheets, and stress-strain relationships and ductility of base metal, heat affected zone including corona bond and nugget were individually measured. Finite element analyses of spot-welded joints under the conditions of static and dynamic tensile-shear loading were carried out with these local mechanical properties to predict the fracture mode and strength of the joints. It was clarified that the effects of both nugget diameter and class of steels were evaluated with good accuracy.

In this paper the fatigue life of welded steel sheet structures is predicted by using FE-Fatigue, which is one of fatigue analysis software tools on the market, and these predicted results are evaluated by reference to corresponding experimental results. Also, we try to predict these structures by using two fatigue life prediction theories established by the JSAE fatigue and reliability committee to compare prediction results. It was confirmed that spot welds fatigue life predictions agree qualitatively with corresponding experimental results and arc welds fatigue life predictions are in good agreement with corresponding experimental results in cases where the SN curve database is modified appropriately.

In order to examine the compatibility of improvement of crashworthiness with weight saving of automobiles by using high strength steel, a combination analysis of Finite Element Method and Dynamic Mechanical Properties has been established. Material properties used in this analysis have been measured by “one bar method” high velocity tensile tests, which can examine the deformation behavior of materials at a bend crush speed range (∼55km/h). It was confirmed that the strength of steel measured by one bar method was raised remarkably after press and hydro forming of high strength steels. It was also confirmed by FEM analysis and load drop test that absorbed energy of bend crush was improved by pre-strain effect. Further, we proved that absorbed energy of bend crush was also improved by appropriate design of thickness and the ratio of bend span and plate length. These effects are applicable to respective high strength steels.

The influence of tensile strength on fatigue strength and the effect of strengthening mechanism on fatigue notch factor were investigated into conventional mild steels, HSLA steels, DP steels and TRIP steels. The grade of studied steels was altered from 440MPa to 780MPa. Not only smooth fatigue specimens with side surface ground and smooth fatigue specimens with laser-cut side surface but also fatigue specimens with a pierced hole were prepared for each of steel sheets. Fatigue tests were conducted in an axial load method. These experiments made it clear that the fatigue limits of smooth specimen increase along the tensile strength approximately independent of strengthening mechanism but those of notched specimen do not necessarily increase along the tensile strength. Namely, fatigue limits of DP steels and TRIP steels with notch increase in proportion to tensile strength although those of HSLA steels with notch do not increase.

The newly developed sheet steel lightly coated with an organic composite is as follows. Zn-Ni alloy plated sheet steel with a coating weight of 30 g/m2 and average Ni concentration of 11.5 ∼12.0 % is chromated through electrolysis. The coating weight of chromate film is 50 ∼90 mg/m2 in Cr. Furthermore, emulsified olefin-acrylic acid copolymer resin mixed with colloidal silica of particle size 7 ∼8 nm applied to a thickness of 1.0 ∼1.8 μm. Olefin-acrylic acid copolymer resin and colloidal silica are mixed at the rate of 100 and 30 (parts by weight). It maintains excellent corrosion resistance even after forming, C-ED paint corrosion resistance and paint adhesion. Furthermore, it has excellent perforation resistance. The product has excellent weldability and is well suited to continuous forming, too.

For the automotive exposed panels, several types of 350N/mm2 grade bake-hardenable sheet steel have been developed and actually applied. However for further weight reduction of automotive body panels, especially inner panels, a 450N/mm2 grade sheet steel with excellent formability has been required. For this demand a new 450N/mm2 grade sheet steel has been developed. As the result it was found, that by the co-addition of Mn and P to ultra-low carbon interstitial free steel the recrystallization texture favorable for deep drawability can be formed, accompanied with the increase in tensile strength, when hot band coiled temperature is lower than 773K. In order to improve the property of the 450N/mm2 grade steel, the effect of Si content has been studied. It was found that the deep drawability is not deteriorated by the addition of Si into the Mn and P co-added ultra-low carbon IF-steel.

As a demand for vehicles of higher functionality grows, automakers and material suppliers are devoting increasing efforts to develop technologies for greater safety, lighter weight, higher corrosion resistance, and enhanced quietness. The resin-sandwiched vibration damping steel sheet (VDSS), developed as a highly functional material for reducing vehicle vibration and noise, has been used for oil pans1) and compartment partitions2). First applied for a structural dash panel of the new Mazda 929, a Zn-Ni electroplated VDSS which allows direct electric welding has contributed to greater weight reduction as well as improved quietness.

Weight reduction of automobiles is one of the most highlighted subjects in automobile industry from the energy saving and clean environment points of view. A typical approach for the purpose is to use high strength steel sheets as well as optimizing designs and using low density materials. It is not, however, easy to apply high strength steel sheets to automotive panels because of their strict requirement for the shape-fixability although a high dent resistance is also required. Besides the use of bake hardening steels, two different high strength steel sheets, which are a continuously annealed extra-low carbon titanium-added IF steel and a low carbon TRIP steel which contains about six volume% of austenite, were assessed for the application to automotive panels in combination with a tension-controled press-forming technique and showed as good shape-fixability as a conventional box-annealed aluminum-killed DDQ steel sheet when high blank-holding-forces were applied.

Two types of TS 450 to 600 MPa grade hot rolled high strength steels have been developed whose strength increases by a post-deformation heat treatment. One is a nitrogen added steel, produced by a low temperature coiling method. This steel shows an increase in tensile strength by about 60 to 90 MPa after a conventional baking treatment. The other is a Cu-bearing steel, produced also by a low temperature coiling method. This steel shows much larger increase in tensile strength by about 200 MPa due to the precipitation hardening of copper, but it requires an additional heat treatment at a relatively high temperature such as 600° C.

Since galvannealed steel sheets (GA) are widely used for automobile body parts, they require excellent features such as press formability, resistant spot weldability and phosphatability. We have focused on improving the press formability of GA since the late 1990s, and have developed a new type of surface modified GA which has a lower friction coefficient than conventional GA. The developed surface modified GA based on mild steel is now used by all automakers in Japan, especially for those parts such as side panels that are difficult to form. This paper describes the features of the surface modified GA.

Sheet hydro-forming was applied to hydro-form a door outer panel using different steel grades. The effect of mechanical properties and the forming conditions on panel properties such as thickness profile and cross-sectional shape accuracy were investigated by both experimental sheet hydro-forming and FEM forming analysis. 590MPa T.S. steel grade was successfully formed with improved dent resistance compared to the conventional 340MPa T.S. steel grade. On the other hand, the results of the FEM forming process analysis showed that the pre-forming conditions were important in controlling the fracture formation during forming and to improve dent resistance, which successfully led to the best forming condition.

A new topology analysis method was developed to optimize part shapes and the configuration of automotive components. Only solid elements are used in the conventional topology optimization method. The key point of the new method is to embed solid elements in a model made of shell elements. In this study, stiffness optimizations were carried out for a simple cylindrical model, automotive floor model and full vehicle model. Specifically, optimized automotive components were a center tunnel, a side-sill and a joint linking a side-member and a cross-member, which are made of steel sheets and have rectangular cross sections. The results show that the newly-developed topology optimization method is valuable in the optimization of automotive components which are made of steel sheets and have rectangular cross sections.