The compatibility of plastic materials used in gasoline storage and dispensing applications was determined for test fuels representing neat gasoline (Fuel C), and blends containing 25% ethanol (CE25a), 16% isobutanol (CiBu16a), and 24% isobutanol (CiBu24a). A solubility analysis was also performed and compared to the volume swell results obtained from the test fuel exposures. The plastic specimens were exposed to each test fuel for16 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured for volume and hardness. Dynamic mechanical analysis (DMA), which measures the storage modulus as a function of temperature, was also performed on the dried specimens to determine the temperature associated with the onset of the glass-to-rubber transition (Tg). For many of the plastic materials, the solubility analysis was able to predict the relative volume swell for each test fuel.

The compatibility of elastomer materials used in fuel storage and dispensing applications was determined for an off-highway diesel fuel and a blend containing 20% bio-oil (Bio20) derived from a fast pyrolysis process. (This fuel blend is not to be confused with B20, which is a blend of diesel fuel with 20% biodiesel.) The elastomer types evaluated in this study included fluorocarbon, fluorosilicone, acrylonitrile rubber (NBR), styrene butadiene rubber (SBR), polyurethane, neoprene, and silicone. All of these elastomer types are used in sealing applications, but some, like the nitrile rubbers are also common hose materials. The elastomer specimens were exposed to the two fuel types for 4 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured. A solubility analysis was performed to better understand the performance of plastic materials in fuel blends composed of bio-oil and diesel.

The compatibility of plastic materials used in fuel storage and dispensing applications was determined for an off-highway diesel fuel and a blend containing 20% bio-oil (Bio20) derived from a fast pyrolysis process. Bio20 is not to be confused with B20, which is a diesel blend containing 20% biodiesel. The feedstock, processing, and chemistry of biodiesel are markedly different from bio-oil. Plastic materials included those identified for use as seals, coatings, piping and fiberglass resins, but many are also used in vehicle fueling systems. The plastic specimens were exposed to the two fuel types for 16 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured to determine extent of property change. A solubility analysis was performed to better understand the performance of plastic materials in fuel blends composed of bio-oil and diesel.

The compatibility of elastomeric materials used in fuel storage and dispensing applications was determined for test fuels representing neat gasoline and gasoline blends containing 10 and 17 vol.% ethanol, and 16 and 24 vol.% isobutanol. The actual test fuel chemistries were based on the aggressive formulations described in SAE J1681 for oxygenated gasoline. Elastomer specimens of fluorocarbon, fluorosilicone, acrylonitrile rubber (NBR), polyurethane, neoprene, styrene butadiene rubber (SBR) and silicone were exposed to the test fuels for 4 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 20 hours at 60°C and then remeasured for volume and hardness. Dynamic mechanical analysis (DMA) was also performed to determine the glass transition temperature (Tg). Comparison to the original values showed that all elastomer materials experienced volume expansion and softening when wetted by the test fuels.

The objective of the research presented in this paper was to assess the influence of stamping process on crash response of UltraLight Steel Auto Body (ULSAB) [1] vehicle. Considered forming effects included thickness variations and plastic strain hardening imparted in the part forming process. The as-formed thickness and plastic strain for front crash parts were used as input data for vehicle crash analysis. Differences in structural performance between crash models with and without forming data were analyzed in order to determine the effects and feasibility of integration of forming processes and crash models.

Elastomers are traditionally designed for use in applications that require specific mechanical properties. Unfortunately, these properties change with respect to many different variables including heat, light, fatigue, oxygen, ozone, and the catalytic effects of trace elements. When elastomeric mounts are designed for NVH use in vehicles, they are designed to isolate specific unwanted frequencies. As the elastomers age however, the desired elastomeric properties may have changed with time. This study looks at the variability seen in new vehicle engine mounts and how the dynamic properties change with respect to miles accumulated on fleet and durability test vehicles.

This paper describes how a blend of silicon polymers, mixed with the right combination of fillers, enables the production of durable rubber IC engine head and exhaust gaskets. The resin blend, when mixed with glass fiber reinforcement, produces a liquid sealant suitable for exhaust gasket applications. The exhaust sealant and laminate head gaskets were tested on Ford 460 truck engines at Jasper Engine Company and completed more than 5,000 hours of durability testing without incident. Fabric reinforced polymer (FRP) head and exhaust gaskets can be laser cut from molded laminates, creating a ceramic glass-sealed edge. Thermogravimetric scans of typical gasket laminate material reveal an 88%-yield at 1000°C. FRP head gaskets also enable the cost-effective production of multiple spark ignition (MSI) head gaskets.

Carbon fiber composite use in automobiles and light trucks could dramatically reduce energy use and engine-out emissions. However, worldwide capacity of 28,000 tonnes per year of carbon fiber from polyacrylonitrile (PAN) and petroleum pitch could support limited automotive use. Production of high-volume, industrial-grade fiber from renewable and recycled polymers (lignin, recycled plastics, regenerated cellulosics) could meet automotive demand. Profiles of material volumes, carbon content, and melting points indicate several attractive candidates for production melt-spun carbon fiber feedstocks. Effects on the carbon fiber production cycle and its integration into automotive production are discussed.

The traditional method of dynamic characterization of elastomers used in industry has largely been based on sinusoidal input excitation. Discrete frequency sine wave signals at specified amplitudes are used to excite the elastomer in a step-sine sweep fashion. This paper will examine new methods of characterization using various broadband input excitations. These different inputs include continuous sine sweep (chirp), shaped random, and acquired road profile data. Use of these broadband data types is expected to provide a more accurate representation of conditions seen in the field, while helping to eliminate much of the interpolation that is inherent with the classic discrete step-sine technique. Results of the various input types are compared in this paper with those found using the classic discrete step-sine input.

The research into vibration characteristics of a loaded and rolling tire is essential for the prediction of spindle forces. There are tire vibration characteristics one of which is the first natural frequency of a loaded and rolling tire is lower than that of an unrolling tire. The vibration characteristics, for a loaded and rolling tire, are affected by the effect of rotation, restrictions of the vibration due to road contact, and the behavior of rubber dependent on amplitude strain. The consideration of the degradation of natural frequency is therefore necessary in the tire model for prediction of spindle forces. This paper describes an identification method for the tire equivalent stiffness of a tire model focused on vertical spindle forces. The first mode is dominant in vertical spindle forces. First, the natural frequencies in rolling and unrolling tires are identified by operational impact test.

Three dimensional fabrics have seen increasing use lately as composite reinforcements. Advantages over prepreg or chopped fiber processes can include cost, handling, consistent quality, impact behavior, and resistance to delamination [1]. To gain acceptance in the transportation industry it is imperative that properties including dynamic and fatigue behavior be designable. A Progressive Failure Analysis (PFA) was developed jointly by Alpha Star Corp and NASA to predict fatigue life of composites and determine their damage mechanisms so that the life could be extended. The title of this software package is GENOA™, and it was used to focus on the three dimensional fabric called 3WEAVE™ made by 3TEX, Inc. It was discovered through fatigue testing that void content greatly affected fatigue life for the 3D E-glass fabric reinforcing a polyurethane modified vinyl ester resin called Dion 9800 from Reichhold. This is a common characteristic for most structural materials.

The effects of CNBR (cross-linked acrylonitrile butadiene rubber) modification on the fracture characteristics of epoxy adhesives were investigated under Mode I static loading. Fracture tests were conducted by using DCB (double cantilever beam) specimens. Rubber content, adhesive thickness and loading rate were changed. The crack extension resistance (given by energy release rate) of the epoxy adhesives was much improved by CNBR modification. For the rubber modified epoxy adhesives, the crack extension resistance becomes high with an increase in adhesive thickness as well as loading rate. The reason why the CNBR modification improves the crack extension resistance was explained based on the surface observation and fractal dimension of the fractured surface.

The effects of inclusion of glass beads and rubber modification on the fatigue fracture characteristics of an epoxy adhesive were investigated. Hybrid effects were also investigated when not only the epoxy adhesive was rubber modified but also when glass beads were mixed simultaneously. Fatigue crack growth resistance was greatly increased due to glass beads, CTBN and CNBR modifications at the second stage of crack growth (da/dN=10-4-10-3 mm/cycle). However, the energy release rate at threshold for both CNBR and CTBN modified adhesives were lower than that for the unmodified adhesive. No significant hybrid effects were distinguishable.

The effects of temperature, crack tip opening rate and rubber content on static fracture characteristics of CNBR (Cross-linked acryloNitrile Butadiene Rubber) modified epoxy adhesives were investigated under mode I loading. Loading-unloading tests were statically performed by using DCB (Double Cantilever Beam) specimens. The fracture toughness increased with increasing the rubber content. The fracture toughness of CNBR modified and unmodified epoxy adhesives was much influenced by temperature and crack tip opening rate. The surface topology of fractured surface was changed by temperature and type of adhesive.

Forty-nine plant-wide energy efficiency assessments have been undertaken under sponsorship of the U.S. Department of Energy's Industrial Technologies Program. Plant-wide assessments are comprehensive, systematic investigations of plant energy efficiency, including plant utility systems and process operations. Assessments in industrial facilities have highlighted opportunities for implementing best practices in industrial energy management, including the adoption of new, energy-efficient technologies and process and equipment improvements. Total annual savings opportunities of $201 million have been identified from the 40 completed assessments. Many of the participating industrial plants have implemented efficiency-improvement projects and already have realized total cost savings of more than $81 million annually. This paper provides an overview of the assessment efforts undertaken and presents a summary of the major energy and cost savings identified to date.

In this study the volume and hardness were measured for thermoplastics and thermosetting resins with diesel containing up to 30% of the following blend stocks: biodiesel, renewable diesel, n-undecane, dibutoxymethane, 1-octanol, hexyl hexanoate, and 2-nonanone. Thermoplastics included polyphenylene sulfide (PPS), polyethylene terephthalate (PET), polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), polyoxymethylene (POM), polybutylene terephthalate (PBT), polypropylene (PP), high density polyethylene (HDPE), nylons, acetals, polyetherimide (PEI), polyetheretherketone (PEEK), a PET co-polymer, polyphthalamides (PPAs), polyarylamide (PARA) and ethylene tetrafluoroethylene (ETFE). Three thermosetting resins were also evaluated. The material specimens were exposed to the test fuels under ambient conditions for 16 weeks.

As interest has grown in diesel emissions and diesel engine aftertreatment, so has the importance of analyzing all components of the exhaust. One of the more costly and difficult measurements to make is the collection and analysis of semivolatile organic compounds (SOCs) in the exhaust. These compounds include alkane and alkenes from C12-C24, and the 2-5 ring polycyclic aromatic hydrocarbons (PAH). These compounds can be present in both the particulate (i.e. on the filter) and gaseous phase, and cannot be collected with bag samples. Typically, a sorbent is used downstream of the particulate collection filters to collect these compounds. Sorbent phases include polyurethane foam (PUF), Tenax™, XAD-type resins, and activated carbon. The SOCs are removed from the sorbent either by solvent extraction (PUF and XAD) or thermal desorption (Tenax™ and activated carbon). Each of these methods have advantages and disadvantages.

Several standard methods exist for testing composites, metals and plastics in Mode I fracture. However, these standard test methods have limitations that disqualify them as candidates for testing certain automotive materials. In order to conduct successful fracture toughness tests with these automotive materials, a modified double cantilever beam testing geometry and associated new procedure have been developed. Both the test procedure and the data analysis have been fully documented in a draft standard. Representative SRIM composite, e-coat steel and epoxy were selected to develop and validate the testing procedure.

Polyoxymethylene dimethyl ethers (PODEs) have shown promise as candidates for diesel fuel blendstocks due to their low sooting tendency, high cetane number, and diesel-comparable boiling point range. However, there is a lack of literature regarding compatibility of PODEs with common automotive elastomers, which would be a prerequisite to their adoption into the marketplace. To address this need, an exposure study and complementary solubility analysis were undertaken. A commercially available blend of PODEs with polymerization degree ranging from 3 to 6 was blended with diesel certification fuel at 0, 33, 50, 67, at 100% by mass. Elastomer coupons were exposed to the various blends for a period of 4 weeks and evaluated for volume swell.

The compatibility of key fuel system infrastructure elastomers with promising bio-blendstock fuel candidates was examined using Hansen solubility analysis. Thirty-four candidate fuels were evaluated in this study including multiple alcohols, esters, ethers, ketones, alkenes and one alkane. These compounds were evaluated as neat molecules and as blends with the gasoline surrogate, dodecane and a mix of dodecane and 10% ethanol (E10D). The elastomer materials were fluorocarbon, acrylonitrile butadiene rubber (NBR), styrene butadiene (SBR), neoprene, polyurethane and silicone. These materials have been rigorously studied with other fuel types, and their measured volume change results were found to correspond well with their predicted solubility levels. The alcohols showed probable compatibility with fluorocarbon and polyurethane, but are not likely to be compatible at low blend levels with NBR and SBR.