Joint stiffness is a major contributor to the vehicle body overall bending and torsional stiffness which in turn affects the vehicle NVH performance. Each joint consists of spot welds which function as load paths between adjacent sheet metal. Spot welds tend to lose structural integrity as a result of fatigue, loosening, aging, wear and corrosion of parts as a vehicle accumulates mileage. Experimental methods are used to identify potential degradation mechanisms associated with a spot weld. A CAE model which simulates a vehicle body joint generically is used to determine the effects of each individual degradation mode of a spot weld on joint stiffness. A real life B-pillar to roof joint CAE model of a production vehicle is then employed to examine the significance of weld distribution on joint stiffness degradation. The knowledge derived from this study can be used as a guidance in designing vehicle body structures with respect to spot weld distribution.

Failure loads of spot welds are investigated under static and impact loading conditions. A test fixture was designed and used to obtain maximum loads of spot welds under a range of combined opening and shear loads with different loading rates. Optical micrographs of the cross sections of spot welds before and after failure were obtained to understand the failure processes under various loading rates and different combinations of loads. The experimental results indicate that under nearly pure opening loads, the failure occurs along the nugget circumferential boundary. Under combined opening and shear loading conditions, the failure starts from the tensile side of the base metal near the nugget in a necking/shear failure mode. The effects of sheet thickness and combined load on the load carrying behavior of spot welds are investigated under static and impact loading conditions based on the experimental results.