Search Results

In order to examine the compatibility of improvement of crashworthiness with weight saving of automobiles by using high strength steel, a combination analysis of Finite Element Method and Dynamic Mechanical Properties has been established. Material properties used in this analysis have been measured by “one bar method” high velocity tensile tests, which can examine the deformation behavior of materials at a bend crush speed range (∼55km/h). It was confirmed that the strength of steel measured by one bar method was raised remarkably after press and hydro forming of high strength steels. It was also confirmed by FEM analysis and load drop test that absorbed energy of bend crush was improved by pre-strain effect. Further, we proved that absorbed energy of bend crush was also improved by appropriate design of thickness and the ratio of bend span and plate length. These effects are applicable to respective high strength steels.

The influence of tensile strength on fatigue strength and the effect of strengthening mechanism on fatigue notch factor were investigated into conventional mild steels, HSLA steels, DP steels and TRIP steels. The grade of studied steels was altered from 440MPa to 780MPa. Not only smooth fatigue specimens with side surface ground and smooth fatigue specimens with laser-cut side surface but also fatigue specimens with a pierced hole were prepared for each of steel sheets. Fatigue tests were conducted in an axial load method. These experiments made it clear that the fatigue limits of smooth specimen increase along the tensile strength approximately independent of strengthening mechanism but those of notched specimen do not necessarily increase along the tensile strength. Namely, fatigue limits of DP steels and TRIP steels with notch increase in proportion to tensile strength although those of HSLA steels with notch do not increase.

Weight reduction of automobiles is one of the most highlighted subjects in automobile industry from the energy saving and clean environment points of view. A typical approach for the purpose is to use high strength steel sheets as well as optimizing designs and using low density materials. It is not, however, easy to apply high strength steel sheets to automotive panels because of their strict requirement for the shape-fixability although a high dent resistance is also required. Besides the use of bake hardening steels, two different high strength steel sheets, which are a continuously annealed extra-low carbon titanium-added IF steel and a low carbon TRIP steel which contains about six volume% of austenite, were assessed for the application to automotive panels in combination with a tension-controled press-forming technique and showed as good shape-fixability as a conventional box-annealed aluminum-killed DDQ steel sheet when high blank-holding-forces were applied.

Extremely formable cold sheet steel with an ultra-high Lankford value of more than 2.5 and an n value of more than 0.27 has been developed. This steel is obtained due to the following factors; using extremely pure IF (Interstitial free) steel, immediate rapid cooling upon completion of rolling in the hot rolling process, a high reduction in the cold rolling process, and a high soaking temperature in the continuous annealing process. This steel sheet shows excellent deep drawability and stretch formability compared with conventional steel sheet (former IF steel and low carbon aluminum-killed steel) as a result of evaluating the limiting drawing ratio and limiting dome height, respectively. This excellent formability is also shown by the model forming tests for simulating the actual stamping of an oilpan and a side-panel. Furthermore, this steel shows the same spot-weldability as that of former IF steel, and zinc phosphatability similar to that of low carbon aluminum-killed steel.

Improvement of material characteristic values, adjustment of forming conditions as well as introduction of new forming technics are necessary to promote wide application of aluminum alloy sheets into automotive parts. 5000 series and 6000 series aluminum alloy sheets are concerned about the relationship between material characteristic values and fundamental forming ability required to apply them to automobile body parts as well as the effect of lubricant on their formability. The hardening parameters, n values, of them are larger than those of cold-rolled steel sheets. However, the r values and the local elongations are extremely small. The improvement of stretch formability owing to increase of n value is smaller than that of the steel sheets. Inferior deep drawability of the aluminum alloy sheets is due to low fracture resistance force caused by low r value.