Resonant frequencies of a resonant bending system with notched crankshaft sections are obtained experimentally and numerically in order to investigate the effect of notch depth on the drop of the resonant frequency of the system. Notches with the depths ranging from 1 to 5 mm, machined by an EDM (Electrical-Discharging Machining) system, were introduced in crankshaft sections at the fillet between the main crank pin and crank cheek. The resonant frequencies of the resonant bending system with the crankshaft sections with various notch depths were first obtained from the experiments. Three-dimensional finite element models of the resonant bending system with the crankshafts sections with various notch depths are then generated. The resonant frequencies based on the finite element computations are in good agreement with those based on the experimental results.

Failure behavior of spot welds is investigated under impact loading conditions. Three different impact speeds were selected to test both HSLA steel and mild steel specimens under combined opening and shear loading conditions. A test fixture was designed and used to obtain the failure loads of spot weld specimens of different thicknesses under a range of combined opening and shear loads with different impact speeds. Accelerometers were installed on the fixtures and the specimens for investigation of the inertia effects. Optical micrographs of the cross sections of failed spot welds were obtained to understand the failure processes in both HSLA steel and mild steel specimens under different combined impact loads. The experimental results indicate that the failure mechanisms of spot welds are very similar for both HSLA steel and mild steel specimens with the same sheet thickness. These micrographs show that the sheet thickness can affect the failure mechanisms.

Sandwich specimens with DP590 steel face sheets and structural epoxy foam cores are investigated under three-point bending conditions. Experimental results indicate that the maximum loads correspond to extensive cracking in the foam cores. Finite element simulations of the bending tests are also performed to understand the failure mechanisms of the epoxy foams. In these simulations, the plastic behavior of the steel face sheets is modeled by the Mises yield criterion with consideration of plastic strain hardening. A pressure sensitive yield criterion is used to model the plastic behavior of the epoxy foam cores. The epoxy foams are idealized to follow an elastic perfectly plastic behavior. The simulation results indicate that the load-displacement responses of some sandwich specimens agree with the experimental results.