Search Results

This paper describes a newly developed steel composition and surface modification methods for improving the rolling contact fatigue strength of parts used in transmission systems, especially continuously variable transmissions (CVTs) to increase their torque capacity. The mechanisms of two types of typical rolling contact fatigue phenomenon in case hardening steel were examined with the aim of improving rolling contact fatigue strength. One concerned white etching constituents (WEC) and the other one concerned peculiar microstructural changes caused by hydrogen originating from decomposition of the lubrication oil as a result of repeated rolling contact stress cycles. The rolling contact fatigue strength limit due to WEC has been improved markedly by dispersing fine M23C6 alloy carbides in the martensite matrix at the subsurface layer of parts.

Although shot peening is an old technology, it has been revived in the Japanese automotive industry as a means to enhance the fatigue durability of steel components. Particular emphasis is on the application of “hard shot peening”. “Hard shot peening” is a high intensity peening technology which results in a higher magnitude of compressive residual stress and, therefore, greater fatigue resistance than conventional shot peening. The first area of development was in high performance carburizing steels suitable for hard shot peening. Desirable traits were enhanced by reducing the carburizing anomalies resulting from intergranular oxidation and by the enhancing case toughness. Further improvement of fatigue resistance has been accomplished by dual peening, first with hard shot followed by smaller diameter steel shot at a lower intensity. This paper also describes the development of long life shot media for hard shot peening.

Based on fundamental research about the influence of chemical composition on rolled bar hardness, hardenability, case hardenability, cold formability, and mechanical properties, a new case hardening steel has been developed which can be cold forged without spheroidizing annealing. The steel contains boron and the Si and Mn contents are less than conventional steels. The steel shows fatigue strength equivalent to the conventional steels and better toughness and machinability.

Based on fundamental study about the toughness of hot rolled microalloyed steels, a new steel composed of 0.4 % carbon, 1.10 % manganese, 0.5 % chromium and 0.15 % vanadium was developed. The steel shows high toughness and high proof stress after well-controlled hot rolling. The newly designed steering racks for passenger cars using the steel bar have properties equivalent to the racks of conventional quenched and tempered carbon steels.

JIS SCM440M (SAE4140H), heat treated to the strength level of 120 to 140 kgf/mm2(171 to 199 ksi) -ISO 12.9 class-, is currently used for cylinder head bolts of Japanese passenger cars. Lower alloy steels, such as SAE 1541 for example, have not been substituted for JIS SCM440H so far because of their high susceptibility to delayed fracture. Daido Steel has tackled this problem and succeeded in applying the lower alloy SAE 1541 steel to 12.9 class cylinder head bolts by enhancing the resistance to delayed fracture by reducing impurities, especially sulphur. In this paper mechanical properties and delayed fracture characteristics of SAE 1541-ULS (Ultra Low Sulphur) steel are reported. 1541-ULS (S<0.005%, S+P< 0.020%) shows outstanding resistance to delayed fracture compared to conventional steel. Furthermore, the amount of MnS inclusions decreases remarkably in ULS steel, which results in high toughness.

A new variable compression turbo (VC-Turbo) engine, which has a multi-link system for controlling the compression ratio from 8:1 to 14:1, requires high axial force for fastening the multi-links because of high input loads and the downsizing requirement. Therefore, it was necessary to develop a 1.6-GPa tensile strength bolt with plastic region tightening. One of the biggest technical concerns is delayed fracture. In this study, quenched and tempered alloy steels were chosen for the 1.6-GPa tensile strength bolt.