This paper describes the scuffing tests performed to understand the effect of surface roughness and lubrication on scuffing behavior for austempered ductile iron (ADI) material. As the scuffing tendency is increased, metal-to-metal interaction between contacting surfaces is increased. Lubrication between sliding surfaces becomes the boundary or mixed lubrication condition. Oil film breakdown leads to scuffing failure with the critical load. Hence, the role of surface roughness and lubrication becomes prominent in scuffing study. There are some studies in which the influence of the surface roughness and lubrication on scuffing was evaluated. However, no comprehensive scuffing study has been found in the literature regarding the effect of surface roughness and lubrication on scuffing behavior of ADI material. The current research took into account the inferences of surface roughness and lubrication on scuffing for ADI.

Fretting is an important phenomenon that happens in many mechanical parts. It is the main reason in deadly failures in automobiles, airliners, and turbine engines. The damage is noticed between two surfaces clamped together by bolts or rivets that are nominally at rest, but have a small amplitude oscillation because of vibration or local cyclic loading. Fretting damage can be divided into two types. The first type is the fretting fatigue damage where a crack would initiate and propagate at specific location at the interface of the mating surfaces. Cracks usually initiate in the material with lower strength because of the local cyclic loading conditions which eventually lead to full failure. The second type is the fretting wear damage because of external vibration. Researchers have investigated this phenomenon by theoretical modeling and experimental approaches. Although a lot of research has been done on fretting damage, some of the parameters have not been well studied.