A novel processing method for fabricating high porosity microcellular ceramic foams for sound absorption applications has been developed. The strategy for fabricating the ceramic foams involves: (i) forming some shapes using a mixture of preceramic polymer and expandable microspheres by a conventional ceramic forming method, (ii) foaming the compact by heating, (iii) cross-linking the foamed body, and (iv) transforming the foamed body into ceramic foams by pyrolysis. By controlling the microsphere content and that of the base elastomer, it was possible to adjust the porosity with a very high open-cell content (ranging between 43 - 95%), high microcellular cell densities (9 × 108 - 1.6 × 109 cells/cm3) and desired expansion ratios (3 - 6 folds). Sound absorption testing has been performed using ASTM C-384 standard test. The preliminary results show that ceramic foams are candidate sound absorption materials.

This paper presents an experimental study on the foaming behavior of recyclable high-melt-strength (HMS) branched polypropylene (PP) with CO2 as a blowing agent. The foamability of branched HMS PP has been evaluated using a tandem foaming extruder system. The effects of CO2 and nucleating agent contents on the final foam morphology have been thoroughly investigated. The low density (i.e., 12~14 fold), fine-celled (i.e., 107–109 cells/cm3) PP foams were successfully produced using a small amount of talc (i.e., 0.8 wt%) and 5 wt% CO2.