Since the sizes of the flywheel and clutch have been enlarged due to downsizing of diesel engines, the mass and moment of inertia at the crankshaft rear end have increased. Consequently, the serious bending stresses have appeared in the crankshaft rear. This paper describes the characteristics of those serious bending stresses, based on the mechanism for whirl resonance. The whirl resonance is largely impacted by the mass of the flywheel and clutch and by the distance from the crank-journal center of the rear end to the center of gravity of the flywheel and clutch.

Countour Induction Hardening (CIH) method is in the limelight as a new possible surface refining method for gears as it reduces quenching distortion considerably and increases compressive residual stress. Also, Double Shot Peening (DSP) method, especially its advanced technique of using extensively small shots (less than 100 m) at the secondary peening, enables increased compressive residual stress under the surface of the gears. Therefore, the new Compound Surface Refining Method of using CIH + DSP is expected to give much higher compressive residual stress than the conventional methods. On studying the application of this new method, the authors evaluated their surface-refining characteristics and the fatigue limits.

There is ever an increasing need for weight reduction and high performance of engine (clean smoke and improving fuel economy) To achieve this, recently aluminum castings are used for engine parts such as cylinder heads that construct combustion chamber and are required thermal resistance. This paper describes thermal fatigue tests of aluminum castings that are made under various conditions of cooling rate during solidification, heat treatment, and chemical compositions. It further investigates the influence of material (such as cooling rate, chemical conmposition and heat treatment) and mechanical properties (such as σB, δ, E ) on thermal fatigue life of aluminum castings.

There are many methods for case hardening such as conventional induction hardening and newly developed electron beam hardening. Electron beam hardening has been adopted in Isuzu and the reliability of engines has been improved. The beam power of the electron beam hardening equipment used was 6 kW. Various conditions of electron beam were scanned across specimens (SCM435H) in order to investigate the influence on hardening properties. As a result, relation between case depth and beam current and relation between case depth and beam scanning time were confirmed. And when the depth exceeded 1 mm, there were cracks in surface melted area. Electron beam hardening was applied to tappets according to the above fundamental experiments, and uniformly hardened layers were obtained. Durability of engines with electron beam hardened tappets was improved twice as much as those with non-hardened tappets.