Spot Welding is now widely used in the fabrication of sheet metals, mainly due to the cost and time considerations. Spot welds are found in nearly all products where sheet metal is joined. Examples range from a single metal toolbox to nearly 10,000 spot welds found in a typical passenger car. Obviously the quality of the spot weld has a direct impact on the quality of the product. The problem of estimating the spot-weld quality is an important component in quality control. If the weld nuggets are improperly or incompletely formed, or the area surrounding the nugget is smaller than required, the structural integrity of the entire part may be uncertain. Furthermore these inconsistencies are usually internal and are seldom visible to Optical Inspection. This study is focused on the non-destructive evaluation of the spot welds using “Digital Shearography”.

Two popular critical plane models developed by Fatemi-Socie and Smith-Watson-Topper were derived from the experimental observations of the nucleation and growth of cracks during loading. The Fatemi-Socie critical plane model is applicable for the life prediction of materials for which the dominant failure mechanism is shear crack nucleation and growth, while the Smith-Watson-Topper model, for materials that fail predominantly by crack growth on planes perpendicular to the planes of maximum tensile strain or stress. The two critical plane models have been validated primarily by in-phase and 90° out-of-phase loading, and few, on the complex, non-proportional loading paths. A successful critical plane model should be able to predict both the fatigue life and the dominant failure planes. However, some experimental studies indicate the 304 stainless steel has the two possible failure modes, shear and tensile failure dominant, depending on the loading mode and stress and strain states.