The use of a soy-based diesel fuel (biodiesel) has potential advantages over the use of a conventional petroleum diesel fuel including: Reduced dependence on foreign petroleum Lowering of greenhouse gas emissions Less air pollution and related public health risks in urban areas A life cycle study performed by the U.S. Department of Energy's National Renewable Energy Laboratory, the U.S. Department of Agriculture's Office of Energy and Ecobalance (completed in May 1998) helped to quantify the environmental benefits of the “cradle-to-grave” production and use of biodiesel. The study showed, for example, that substituting 100% biodiesel for petroleum diesel in urban buses reduced the life cycle emissions of carbon dioxide (CO2) by 78%. The study also pointed out some trade-offs of using biodiesel including increased life cycle hydrocarbon and NOx emissions.

The bending fatigue performance of high temperature (1050 °C) vacuum carburized Nb modified 8620 steel, with niobium additions of 0.02, 0.06 and 0.1 wt pct, was evaluated utilizing a modified Brugger specimen geometry. Samples were heated at two different rates (20 and 114 °C min-1) to the carburizing temperature resulting in different prior austenite grain structures that depended on the specific Nb addition and heating rate employed. At the lower heating rate, uniform fine grained prior austenite grain structures developed in the 0.06 and 0.1 Nb steels while a duplex grain structure with the presence of large (>200 μm grains) developed in the 0.02 Nb steel. At the higher heating rate the propensity for abnormal grain growth was highest in the 0.02 Nb steel and complete suppression of abnormal grain growth was achieved only with the 0.1 Nb steel.

High strain rate sheet tensile tests (up to 300s-1) and Ohio State University (OSU) formability tests (up to an estimated strain rate of 10s-1) were performed to examine the effect of strain rate on the mechanical properties and formability of five ferritic stainless steels: HIGH PERFORMANCE-10™ 409 (HP-10 409), ULTRA FORM® 409 (UF 409), HIGH PERFORMANCE-10™ 439 (HP-10 439), two thicknesses of 18 Cr-Cb™ stainless steel, all supplied by AK Steel, and Duracorr®, a ferrite-tempered martensite dual-phase stainless steel supplied by Bethlehem Steel Corporation. Tensile results show that increasing strain rate resulted in increases in yield stress, flow stress, and stress at instability for all alloys tested. In addition, increases in uniform and total elongation were also found for each of the five alloys.

The effects of austenite grain size on the bending fatigue crack initiation and fatigue performance of gas carburized, modified 4320 steels were studied. The steels were identical in composition except for phosphorus concentration which ranged between 0.005 and 0.031 wt%. Following the carburizing cycle, specimens were subjected to single and triple reheat treatments of 820°C for 30 minutes to refine the austenite grain structure, and oil quenched and tempered at 150°C. Specimens subjected to bending fatigue were characterized by light metallography to determine microstructure and grain size, X-ray analysis for retained austenite and residual stress measurements, and scanning electron microscopy for examination of fatigue crack initiation and propagation. The surface austenite grain size ranged from 15 μm in the as-carburized condition to 6 and 4 μm diameter grain size for the single and triple reheat conditions, respectively.

Regulated emissions (THC, CO, NOx, and PM) and particulate SOF and sulfate fractions were determined for a 1995 Detroit Diesel Series 50 urban bus engine at varying fuel sulfur levels, with and without catalytic converters. When tested on EPA certification fuel without an oxidation catalyst this engine does not appear to meet the 1994 emissions standards for heavy duty trucks, when operating at high altitude. An ultra-low (5 ppm) sulfur diesel base stock with 23% aromatics and 42.4 cetane number was used to examine the effect of fuel sulfur. Sulfur was adjusted above the 5 ppm level to 50, 100, 200, 315 and 500 ppm using tert-butyl disulfide. Current EPA regulations limit the sulfur content to 500 ppm for on highway fuel. A low Pt diesel oxidation catalyst (DOC) was tested with all fuels and a high Pt diesel oxidation catalyst was tested with the 5 and 50 ppm sulfur fuels.

With the increased use of tubular steel products, especially for automotive hydroforming applications, there is increased interest in understanding the mechanical properties measured by tensile tests from specimens of different orientations in the tube. In this study, two orientations of tensile specimens were evaluated -- axial specimens with and without flattening and flattened circumferential specimens. Three steels were evaluated -- two thicknesses of aluminum killed drawing quality (AKDQ) steel and one thickness of high strength low alloy (HSLA) steel. Mechanical property data were obtained from the flat stock, conventional production tubes and quasi tubes. Quasi tubes were produced from the flat stock on a 3-roll bender, but the quasi tube was not welded or sized.

The influences of laboratory-induced hydrogen on the tensile deformation and fracture behavior of selected sheet steels including conventional DQSK and HSLA steels as well as newer DP and TRIP grades were evaluated. The effects of cold work, simulated paint baking, and natural aging were considered. Hydrogen effects were observable by increased flow stress, decreased ductility, altered neck geometry, and altered fracture mechanisms. Differences among the steels and conditions were observed and interpreted on the basis of microstructure, fracture behavior, and theories of hydrogen embrittlement.

Methane emissions from lean-burn natural gas engines can be relatively high. As natural gas fueled vehicles become more prevalent, future regulations may restrict these emissions. Preliminary reports indicated that conventional, precious metal oxidation catalysts rapidly deactivate (in less than 50 hours) in lean-burn natural gas engine exhaust. This investigation is directed at quantifying this catalyst deactivation and understanding its cause. The results may also be relevant to oxidation of lean-burn propane and gasoline engine exhaust. A platinum/palladium on alumina catalyst and a palladium on alumina catalyst were aged in the exhaust of a lean-burn natural gas engine (Cummins B5.9G). The engine was fueled with compressed natural gas. Catalyst aging was accomplished through a series of steady state cycles and heavy-duty transient tests (CFR 40 Part 86 Subpart N) lasting 10 hours. Hydrocarbons in the exhaust were speciated by gas chromatography.

The effectiveness of three different techniques, designed to improve the bending fatigue life in comparison to conventionally processed gas-carburized 8620 steel, were evaluated with modified Brugger bending fatigue specimens and actual ring and pinion gears. The bending fatigue samples were machined from forged gear blanks from the same lot of material used for the pinion gear tests, and all processing of laboratory samples and gears was done together. Fatigue data were obtained on standard as-carburized parts and after three special processing histories: shot-peening to increase surface residual stresses; double heat treating to refined austenite grain size; and vacuum carburizing to minimize intergranular oxidation. Standard room-temperature S-N curves and endurance limits were obtained with the laboratory samples. The pinions were run as part of a complete gear set on a laboratory dynamometer and data were obtained at two imposed torque levels.

Prediction of fatigue performance of large structures and components is generally done through the use of a fatigue analysis software, FEA stress/strain analysis, load spectra, and materials properties generated from laboratory tests with small specimens. Prior experience and test data has shown that a specimen size effect exists, i.e. the fatigue strength or endurance limit of large members is lower than that of small specimens made of same material. Obviously, the size effect is an important issue in fatigue design of large components. However a precise experimental study of the size effect is very difficult for several reasons. It is difficult to prepare geometrically similar specimens with increased volume which have the same microstructures and residual stress distributions throughout the entire material volume to be tested. Fatigue testing of large samples can also be a problem due to the limitation of load capacity of the test systems available.

A series of bending fatigue tests were conducted and S-N data were obtained for two groups of 4320 steel samples: (1) carburized, quenched and tempered, (2) carburized, quenched, tempered and shot peened. Shot peening improved the fatigue life and endurance limit. The S-N data exhibited large scatter, especially for carburized samples and at the high cycle life regime. Sample characterization work was performed and scatter bands were established for residual stress distributions, in addition to fracture and fatigue properties for 4320 steel. Moreover, a fatigue life analysis was performed using fracture mechanics and strain life fatigue theories. Scatter in S-N curves was established computationally by using the lower bound and upper bound in materials properties, residual stress and IGO depth in the input data. The results for fatigue life analysis, using either computational fracture mechanics or strain life theory, agreed reasonably well with the test data.

A revolutionary interplanetary rapid transit concept for transporting scientists and explorers between Earth and Mars is presented by Global Aerospace Corporation under funding from the NASA Institute for Advanced Concepts (NIAC) with support from the Colorado School of Mines, and Science Applications International Corporation. We describe an architecture that uses highly autonomous spaceships, dubbed Astrotels; small Taxis for trips between Astrotels and planetary Spaceports; Shuttles that transport crews to and from orbital space stations and planetary surfaces; and low-thrust cargo freighters. In addition we discuss the production of rocket fuels using extraterrestrial materials; aerocapture to slow Taxis at the planets; and finally describe a number of trade studies and their life-cycle cost results.

The influence of coatings on fatigue behavior has been examined for the following commercially produced sheet steels: uncoated titanium stabilized interstitial-free (IF); electrogalvanized titanium stabilized IF; hot-dip galvanized aluminum killed, drawing quality (AKDQ); and galvannealed AKDQ. Fully reversed bending fatigue tests were conducted at ambient temperature on Krouse-type flexural fatigue machines. A dependence of crack development was observed and correlated to the microstructure and properties of the different coatings. Furthermore, a functional design relationship for each material was determined through stress-life analysis. The experimentally determined fatigue properties were compared to conventional estimates based on tensile properties which ignore coating effects. The results of this work suggest that ductile coatings may enhance fatigue resistance, while brittle coatings may reduce fatigue life.

The objective of the work described here is to test the performance of closed-loop controlled, heavy-duty CNG engines in-use, on fuels of different methane content; and to compare their performance with similar diesel vehicles. Performance is measured in terms of pollutant emissions, fuel economy, and driveability. To achieve this objective, three buses powered by closed-loop controlled, dedicated natural gas engines were tested on the heavy-duty chassis dynamometer facility at the Colorado Institute for Fuels and High Altitude Engine Research (CIFER). Emissions of regulated pollutants (CO, NOx, PM, and THC or NMHC), as well as emissions of alde-hydes for some vehicles, are reported. Two fuels were employed: a high methane fuel (90%) and a low methane fuel (85%). It was found that the NOx, CO, and PM emissions for a given cycle and vehicle are essentially constant for different methane content fuels.

The susceptibility of Advanced High Strength Steels (AHSS) to hydrogen embrittlement (HE) was evaluated on selected high strength sheet steels (DP 600, TRIP 780, TRIP 980, TWIP-Al, TWIP, and Martensitic M220) and the results were compared to data on a lower strength (300 MPa tensile strength) low carbon steel. Tensile samples were cathodically charged and then immediately tensile tested to failure to analyze the mechanical properties of the as-charged steel. The effects of hydrogen on deformation and fracture behavior were evaluated through analysis of tensile properties, necking geometry, and SEM images of fracture surfaces and metallographic samples of deformed tensile specimens. The two fully austenitic TWIP steels were resistant to hydrogen effects in the laboratory charged tensile samples.

This work establishes the relationship between core hardness, case hardness, and case depth on susceptibility to hydrogen embrittlement of case hardened steel fasteners. Such fasteners have a high surface hardness in order to create their own threads in a mating hole, and are commonly used to attach bracketry and sheet metal in automotive applications. While case hardened fasteners have been studied previously, there are currently no processing guidelines supported by quantitative data for fastener standards. Through sustained load embrittlement testing techniques, the susceptibility of case hardened steel tapping screws to internal and environmental hydrogen embrittlement is examined. Further characterization of the fastener samples through microhardness testing, microstructure review, and fracture surface examination allows the investigation of susceptibility thresholds. It is shown that core hardness is the primary consideration for susceptibility.

Punch-stretch tests to determine formability of type 304 stainless steel sheet were conducted using a hemispherical dome test. Sheets of 19.1 mm width and 177.8 mm width were stretched on a 101.6 mm diameter punch at punch rates between 0.042 to 2.12 mm/sec with three lubricant systems: a mineral seal oil, thin polytetrafluoroethelyne sheet with mineral seal oil, and silicone rubber with mineral seal oil. The resulting strain distributions were measured and the amount of martensite was determined by magnetic means. Increasing lubricity resulted in more uniform strain distributions while increased punch rates tended to decrease both strain and transformation distributions. High forming limit values were related to the formation of high and uniformly distributed martensite volume fractions during deformation. The results of this study are interpreted with an analysis of the effects of strain and temperature on strain induced martensite formation in metastable austenitic stainless steels.

The fatigue behavior of five microalloyed steels, processed with hardnesses between 25-28 HRC containing microstructures ranging from precipitation-hardened ferrite-pearlite to bainite, were evaluated in both low cycle (strain controlled) and high cycle (stress controlled fatigue. The vanadium-bearing steels included, 15R30V, 1522 MoVTi, 1522 MoVTiS, 1534 MoVTi, and 1534 MoVTiSi. Conventional quench and tempered 4140 steel was used as a reference. Low cycle fatigue (LCF) data for all steels were similar. Subtle microstructural-dependent differences in the high-strain amplitude region of the LCF curves were attributed to the effects of retained austenite, present in some of the non-traditional bainitic steels. In high cycle fatigue, all steels exhibited similar properties, except for the ferrite-pearlite steel (15R30V) which exhibited the lowest endurance limit, an observation which was attributed to crack nucleation in coarse-grained ferrite.

The response of HSLA steel, 590R, and dual-phase steel, DP-600, to non-uniform deformation imposed in a laboratory Bending-Under-Tension (BUT) test apparatus was evaluated. Samples were deformed with both low and high back tension forces at bend angles of 45 and 90 degrees, and evaluated to determine the “side-wall curl”, i.e. the curvature in the sheet section in contact with the die. The results indicate that there are no consistent differences between the two steels, 590R and DP-600. It was found that back tension, tensile strength and sheet thickness were the primary factors affecting curl. The bend angle has an influence on curl, with the curl radius at a 90° bend angle being greater than the curl radius at a 45° bend angle.

This paper reports the development of new fuel ignition quality and combustion experiments performed using the Ignition Quality Tester (IQT). Prior SAE papers (961182, 971636, 1999-01-3591, and 2001-01-3527) documented the development of the IQT constant volume combustion chamber experimental apparatus to measure ignition qualities of diesel-type fuels. The ASTM International test method D6890 was developed around the IQT device to allow the rapid determination of derived cetane number (DCN). Interest in chemical kinetic models for the ignition of diesel and biodiesel model compounds is increasing to support the development of advanced engines and fuels. However, rigorous experimental validation of these kinetic models has been limited for a variety of reasons. Shock tubes and rapid compression machines are typically limited to premixed gas-phase studies, for example.