Search Results

Due to the recent trend emphasizing on environmental friendly, engine supercharger downsizing technology has been under development globally. In this report, the technical knowledge for high performance and high quality water-cooled CAC development is provided. For higher cooling performance, the optimum fin and tube core matrix water-cooled CAC, delivering best performance and quality have been developed. For higher reliability against thermal stress, the detail specifications of water-cooled CAC based on the transient analysis and the simulation technology have been established.

This paper describes the reliability of silicon carbide (SiC) MOSFET. We clarified the relation between the lifetime of the gate oxide and the crystal defects. We fabricated MOS diodes using thermal oxidation and measured their lifetimes by TDDB (Time Dependent Dielectric Breakdown) measurement. The wear-out lifetime is sufficient for hybrid vehicle but many MOS diodes broke in shorter time. The breakdown points were defined by Photo-emission method. Finally, we classified the defects by TEM (Transmission Electron Microscopy). A TSD (Threading Screw Dislocation) plays the most important role in the lifetime degradation of the gate oxide. The lifetime of the gate oxide area, in which a TSD is included, is shorter by two orders of magnitude than a wear-out breakdown. The mechanism by which threading dislocations degrade the gate oxide lifetime was not discovered. To explain the degradation, we assumed two models, the shape effect and the oxide quality degradation.

PBT (polybutylene terephthalate) and epoxy adhesive, which both have superior heat resistance and environmental resistance, are a representative combination now being applied to many parts. Generally, PBT is annealed after molding at a temperature above the glass transition temperature to ensure dimensional stability when in use. But in this case, this process decreases the adhesive strength between PBT and epoxy. This study analyzes the adhesion degradation mechanism in this system and a countermeasure technology is proposed. Regarding this PBT-epoxy adhesion degradation mechanism, focus is placed on changes in the fracture surface, which is analyzed before and after annealing. From this analysis it becomes clear that generation of a WBL (weak boundary layer) is caused by non-crystallization and a migration of the PBT functional group on the adhesion surface layer.

In recent years, the powertrain system is becoming bigger and more sophisticated than ever, and it is very important that new powertrain systems shall be timely developed just when the market required. In this kind of new system, the quality in particular will be an important factor on the vehicle evaluation issue. With this objective in mind, DENSO has been working on the following challenges, such as the development of key technology, the improvement of quality assurance system, and engineer education to realize them. This reports a general idea on these quality management activities.

The growing functionality and complexity of recent vehicle electronic systems have made inter-device communication (on-board LAN) technology vital to vehicle design. By field of application, the LAN (Local Area Network) systems currently in use are LIN (Local Interconnect Network) used for body systems, CAN (Controller Area Network) used for control systems, and MOST (Media Oriented Systems Transport ) used for multimedia and camera systems, and work to standardize the next-generation communication technology for each of those fields is underway. This paper provides a technical overview of the CXPI (Clock Extension Peripheral Interface) communication protocol, which satisfies the body system requirements (rapid response, system extensibility, high reliability, and low cost). It also presents the progress made on standardization at SAE and other organizations.

Trivalent chromium passivation is used after zinc plating for enhancing corrosion resistance of parts. In the passivating process, the amount of dissolved metal ions (for example zinc and iron) in the passivation solution increases the longer the solution is used. This results in a reduced corrosion resistance at elevated temperatures. Adding a top coat after this process improves the corrosion resistance but has an increased cost. To combat this, we strove to clarify the mechanism of decreased corrosion resistance and to develop a trivalent chromium passivation with a higher corrosion resistance at elevated temperatures. At first, we found that in parts produced from an older solution, the passivation layer has cracks which are not seen in parts from a fresh/new solution. These cracks grow when heated at temperatures over 120 degrees Celsius.

In recent years, due to a growing demand for improvement in the performance and reliability of automotive fuel pumps and the advancement of globalization, automotive fuel pumps are being used with inferior gasolines that include more sulfur, organic acids or compounds, compared to gasolines used in general regions. Conventionally, bearings in these fuel pumps have mainly been made of sintered bronze alloy. With this bronze alloy, however, it is difficult to achieve a significant improvement in the tribology characteristics of bearings, in order to meet the demands for performance improvement, etc., and corrosion is severe in inferior gasolines that contain highly-concentrated organic acids or sulfur and the corrosion products that accompany them. Therefore, in order to obtain fine tribology characteristics and superior corrosion resistance in gasolines with highly-concentrated organic acids and sulfur, various copper-based alloys were studied using the powder metallurgy process.

In automobiles, Integrated Starter Generators (ISGs) are important components since they ensure significant fuel economy improvements. With motors that operate at high voltage such as ISGs, it is important to accurately know partial discharge inception voltages (PDIVs) for the assured insulation reliability of the motors. However, the PDIVs vary due to various factors including the environment (temperature, atmospheric pressure and humidity), materials (water absorption and degradation) and voltage waveforms. Consequently, it is not easy either empirically or analytically to ascertain the PDIVs in a complex environment (involving, for example, high temperature, low atmospheric pressure and high humidity) in which many factors vary simultaneously, as with invehicle environments. As a well-known method, PDIVs can be analyzed in terms of two voltage values, which are the breakdown voltage of the air (called “Paschen curve”) and the shared voltage of the air layer.