This paper examines some key aspects of the manufacturing process that “ Transformation Induced Plasticity” (TRIP) steels would be exposed to, and systematically evaluate how the forming and thermal histories affect final strength and ductility of the material. We evaluate the effects of in-service temperature variations, such as under hood and hot/cold cyclic conditions, to determine whether these conditions influence final strength, ductility and energy absorption characteristics of several available TRIP steel grades. As part of the manufacturing thermal environment evaluations, stamping process thermal histories are included in the studies. As part of the in-service conditions, different pre-straining levels are included. Materials from four steel suppliers are examined. The thermal/straining history versus material property relationship is established over a full range of expected thermal histories and selected loading modes.

This paper examines the effects of fusion zone size on failure modes, static strength and energy absorption of resistance spot welds (RSW) of advanced high strength steels (AHSS). DP800 and TRIP800 spot welds are considered. The main failure modes for spot welds are nugget pull-out and interfacial fracture. Partial interfacial fracture is also observed. The critical fusion zone sizes to ensure nugget pull-out failure mode are developed for both DP800 and TRIP800 using the limit load based analytical model and the microhardness measurements of the weld cross sections. Static weld strength tests using cross-tension samples were performed on the joint populations with controlled fusion zone sizes. The resultant peak load and energy absorption levels associated with each failure mode were studied using statistical data analysis tools. The results of this study show that the conventional weld size of can not produce nugget pull-out mode for both the DP800 and TRIP800 materials.

This paper examines the effects of failure modes on the static strength and total energy absorption of aluminum spot-welded samples using experimental, statistical, and analytical approaches. The main failure modes for aluminum spot welds are nugget pullout and interfacial fracture. Two populations of aluminum spot welds were studied. Within each population, coupon configurations of lap shear, cross tension and coach peel were considered. Thirty replicate static strength tests were performed for each coupon configuration. The resulted peak load and energy absorption level associated with each failure mode was studied using statistical models. Next, an analytical model was developed to determine the failure mode of an aluminum resistance spot weld based on stress analysis. It is found that weld size, sheet thickness, and level of weld porosity and defects are the main factors determining the cross tension failure mode for an aluminum spot weld.