As the automotive industry becomes more concerned with the crash performance of automobiles, the behavior of used vehicles becomes an interesting subject. In this work, the effect of aging on spot welded joints was simulated by applying fatigue loading to the samples. Samples were then subjected to quasi-static and impact tests to measure the effect of fatigue aging to the strength of the samples. The results show (a) a reduction in the strength of the test samples under impact conditions, (b) no obvious reduction in quasi-static conditions, and (c) significant reduction in strength if cracks in the welds were initiated during the fatigue aging process.

Static and dynamic strength tests were performed on spot welded specimens made of dual-phase (DP) 780 and mild steels (DQSK). Lap-shear (LS) and cross-tension (CT) as well as a new mixed mode specimen were studied using MTS hydraulic universal testing machine for static tests and drop weight tower for dynamic tests. Three weld nugget sizes were made for each steel and CT and LS. DP780 with one weld size was also tested in mixed mode. Load and displacement as functions of time and fracture mode of the spot welds were recorded. Representative data are reported in this paper.