Search Results

For this latest SAE Fatigue Design and Evaluation project, fatigue tests were run by loading, in bending, both welded and machined T-Joint specimens that have the same geometry. The test rig setup consisted of a horizontally mounted actuator, with pinned joints at both ends, where the load is applied to the top of the vertical leg of the “upside down T” of a T-Joint specimen, while the horizontal legs of the “upside down T” were clamped to the bedplate. Specimens were tested until failure or until the specimen was unable to carry the commanded load. They were cycled under constant amplitude (at several load levels and R ratios), block cycle, and variable amplitude loadings. Welded and machined T-Joint specimens of the same geometry were included in the test plan such that fatigue life predictions could be compared to test lives for each case. Those comparisons would demonstrate the methodology’s relative predictive ability to manage welds, residual stress, etc...

General corrosion protection of sheet materials such as steel used in automobile construction has reached a high level of performance, due primarily to the incorporation of mill-applied treatments such as electrogalvanizing, galvannealing and other coil-coating processes developed over the last half century. While such treatments have greatly extended the corrosion resistance of steel and its various body constructs, attention is now focused on aspects of the manufacturing process wherein these intended protections are compromised by such features as weldments, joins, cut edges and extreme metal deformations such as hems. A novel metal deposition process, based on high-velocity impact fusion of solid metal particles, has been used to extend the corrosion resistance of base steel and pre-galvanized sheet, by selectively placing highly controlled depositions of zinc and other sacrificial materials in close proximity to critical manufacturing details.

Smaller locomotives often use mechanical transmissions instead of diesel-electric drive systems typically used in larger locomotives. This paper discusses how Model Based Design was used to develop the complete drive train control system for a 24 ton sugar cane locomotive. A complete MATLAB Simulink machine model was built to fully test and verify the shift control logic, traction control, vehicle speed limiting, and braking control for this locomotive application before it was commissioned. The model included the engine, torque converter, planetary transmission, drive line, and steel on steel driving surface. Simulation was used to debug all control code and test and refine control strategies so that the initial field commissioning in remote Australia was executed very quickly with minimal engineering support required.

In lightweight structures with dissimilar metal designs, structural adhesive joining is a potential joining method. Adhesives help in reducing galvanic corrosion by minimizing physical contact between two dissimilar metals. Along with adhesives, fasteners are often used as a secondary joining method to hold the assembly together during adhesive curing. Therefore, a hybrid joint which is a combination of adhesives and mechanical fasteners is potential joining method to join dissimilar metals. However, when two dissimilar metals such as aluminum to steel are joined with hybrid joint by adhesive curing at elevated temperature, the distortion of assembly is observed when cooled at room temperature. This is due to the mismatch between coefficients of thermal expansion of aluminum vs steel. The adhesive may also experience residual stress and fracture. In this study, adhesive curing induced distortion is studied using 1.1 meter-long specimens of aluminum to steel hybrid joint assembly.

The induction hardening process involves a complex interaction of electromagnetic heating, rapid cooling, metallurgical phase transformations, and mechanical behavior. Many factors including induction coil design, power, frequency, scanning velocity, workpiece geometry, material chemistry, and quench severity determine a process outcome. This paper demonstrates an effective application of a numerical analysis tool for understanding of induction hardening. First, an overview of the Caterpillar induction simulation tool is briefly discussed. Then, several important features of the model development are examined. Finally, two examples illustrating the use of the computer simulation tool for solving induction-hardening problems related to cracking and distortion are presented. These examples demonstrate the tool's ability to simulate changes in process parameters and latitude of modeling steel or cast iron.

The presence of residual stresses affects the fatigue response of welded components. In the present study of thick welded cantilever specimens, residual stresses were measured in two A36 steel samples, one in the as-welded condition, and one subjected to a short history of bending loads where substantial local plasticity is expected at the fatigue hot-spot weld toe. Extensive X-Ray Diffraction (XRD) measurements describe the residual stress state in a large region above the weld toe both in an untested as-welded sample and in a sample subjected to a short load history that generated an estimated 0.01 strain amplitude at the stress concentration zone at the weld toe. The results show that such a test will significantly alter the welding-induced residual stresses. Fatigue life prediction methods need to be aware that such alterations are possible and incorporate the effects of such cyclic stress relaxation in life computations.

Thermal batteries are normally constructed using pressed-powder anode, separator, and cathode pellets (discs). However, parts less than 0.010” thick are difficult to press from the starting powders. The use of plasma spraying to deposit thin pyrite films onto a stainless steel substrate was examined as an alternative to pressed-powder cathodes. The electrodes were tested under isothermal conditions and constant-current discharge over a temperature range of 400°C to 550°C using a standard LiSi anode and a separator based on the LiCIKCI eutectic. The plasma-sprayed cathodes were also evaluated in similar 5-cell thermal batteries. Cells and batteries using pressed-powder cathodes were tested under the same conditions for comparative purposes.

Calorimetric measurements of the net heat input to the workpiece have been made to determine the effect of very high travel speeds on laser weld melting efficiency. Very high welding speeds are required in welding applications such as automotive where lasers are now applied extensively. Travel speeds as fast as 530 mm/s for continuous wave CO2 laser welding on 304 stainless steel have been examined in this study. Melting efficiency indicates what fraction of the laser power absorbed is used to produce melting rather than undesirable base metal heating. It was found that melting efficiency initially increased then slowly decreased as fusion zone dimensions changed. Dimensionless parameter correlations for melting efficiency based on heat flow theory have been presented for both 2D and 3D heat flow geometries. The levels of melting efficiency observed are close to the maximum values that are predicted with these correlations.

A new total fatigue life methodology was utilized to make fatigue life predictions, where total fatigue life is defined as crack initiation and subsequent crack propagation to a crack of known size or the component’s inability to carry load. Fatigue life predictions of an A36 steel T-joint geometry were calculated using the same total fatigue life methodology for both welded and machined test specimens that have the same geometry. The only significant difference between the two analyses was the inclusion of the measured weld residual stresses in the welded specimen life predictions. Constant amplitude tests at several load levels and R ratios were analyzed along with block cycle and variable amplitude loading tests. The accuracy of the life predictions relative to experimental test lives was excellent, with most within a factor of +/- two.

The bending fatigue performance of gears, cantilever beam specimens, and notched-axial specimens were evaluated and compared. Specimens were machined from a modified SAE-4118 steel, gas-carburized, direct-quenched and tempered. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray analysis for residual stress and retained austenite measurements, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. The case and core microstructures, prior austenite grain sizes and case hardness profiles from the various types of specimens were similar. Endurance limits were determined to be about 950 MPa for both the cantilever beam and notched-axial fatigue specimens, and 1310 MPa for the single gear tooth specimens.