Search Results

The use of urea-based selective catalytic reduction (SCR) is a promising method for achieving U.S. Tier 2 diesel emission standards for NOx. To meet the Tier 2 standards for Particulate Matter (PM), a catalyzed diesel particulate filter (CDPF) will likely be present and any ammonia (NH3) that is not consumed over an SCR catalyst would pass over the CDPF to make nitrous oxide (N2O) emissions and/or oxides of nitrogen (NOx), or exit the exhaust system as NH3. N2O is undesirable due to its high greenhouse gas potential, while NOx production from the slipped NH3 would reduce overall system NOx conversion efficiency. This paper reviews certain conditions where NH3 slip past an SCR system may be a concern, looks at what would happen to this slipped NH3 over a CDPF, and evaluates the performance of various supplier NH3 slip catalysts under varied space velocities, temperatures and concentrations of NH3 and NOx.

Selective catalytic reduction (SCR) is a promising technology for diesel aftertreatment to meet NOx emissions targets in several countries. In established markets such as the US and Europe, zeolite SCR systems are expected to be used due to their ability to survive the exhaust gas temperatures seen in an active diesel particulate filter regeneration. In emerging markets where the fuel sulfur level may be as high as 2000 parts per million, zeolite SCR catalysts may have durability issues. In these markets, low sulfur fuel is needed overall to meet emissions standards and to avoid high sulfate emissions, but the aftertreatment system must be durable to high sulfur levels because there is a risk of exposure to high sulfur fuel. Also, emissions standards may be met without a DPF in some applications, so that the exhaust system would not see temperatures of 600°C or higher.

Selective Catalytic Reduction (SCR) catalysts have been designed to reduce NOx with the assistance of an ammonia-based reductant. Diesel Particulate Filters (DPF) have been designed to trap and eventually oxidize particulate matter (PM). Combining the SCR function within the wall of a high porosity particulate filter substrate has the potential to reduce the overall complexity of the aftertreatment system while maintaining the required NOx and PM performance. The concept, termed Selective Catalytic Reduction Filter (SCRF) was studied using a synthetic gas bench to determine the NOx conversion robustness from soot, coke, and hydrocarbon deposition. Soot deposition, coke derived from propylene exposure, and coke derived from diesel fuel exposure negatively affected the NOx conversion. The type of soot and/or coke responsible for the inhibited NOx conversion did not contribute to the SCRF backpressure.

This paper presents the development of an analytical model that complements laboratory based experiments to provide a tool for Selective Catalyst Reduction (SCR) applications. The model calibration is based on measured data from NOx reduction performance tests as well as ammonia (NH3) adsorption/desorption tests over select SCR catalyst formulations in a laboratory flow reactor. Only base metal/zeolite SCR samples were evaluated. Limited validations are presented that show the model agrees well with vehicle data from Environmental Protection Agency Federal Test Procedure (EPA FTP) emission assessments. The model includes energy and mass balances, several different NH3 reactions with NOx, NH3 adsorption and desorption algorithms, and NH3 oxidation.

Diesel aftertreatment systems configured with a diesel oxidation catalyst (DOC) upstream of an urea selective catalytic reduction (SCR) catalyst run the risk of precious metal contamination. During active diesel particulate filter (DPF) regeneration events, the DOC bed temperature can reach up to 850°C. Under these conditions, precious metal (especially Pt) can be volatized and then deposited on a downstream SCR catalyst. In this paper, the impact of ultra-low contamination of platinum group metals (PGM) on the SCR catalyst was studied. A method based on precious metal volatilization of a Pt-rich DOC at 850°C and under lean gas conditions was employed to contaminate downstream FeSCR and CuSCR formulations. The contamination resulted in poor NOx conversion (via NOx remake) and excessive N2O formation. The precious metal volatilization method was employed to screen various Pt/Pd based DOCs to avoid contamination of the downstream FeSCR.

Passenger and light duty diesel vehicles will require up to 90% NOx conversion over the Federal Test Procedure (FTP) to meet future Tier 2 Bin 5 standards. This accomplishment is especially challenging for low exhaust temperature applications that mostly operate in the 200 - 350°C temperature regime. Selective catalytic reduction (SCR) catalysts formulated with Cu/zeolites have shown the potential to deliver this level of performance fresh, but their performance can easily deteriorate over time as a result of high temperature thermal deactivation. These high temperature SCR deactivation modes are unavoidable due to the requirements necessary to actively regenerate diesel particulate filters and purge SCRs from sulfur and hydrocarbon contamination. Careful vehicle temperature control of these events is necessary to prevent unintentional thermal damage but not always possible. As a result, there is a need to develop thermally robust SCR catalysts.

Selective catalytic reduction (SCR) is expected to be used extensively in the U.S. for diesel vehicle NOx control. Much progress has been made on improving performance and reducing complexity of SCR systems for vehicles in the past several years. SCR system complexity can be reduced further by implementation of SCR-coated diesel particulate filters (SCRFs). In this system, a high porosity (> 50%) filter substrate is coated with an SCR formulation, ideally in the pores of the filter walls, so that the DPF and SCR functions can be combined into a single catalyst. Two state-of-the-art Cu/zeolite SCR formulations and three types of high porosity filter substrates were included in this study. Laboratory and engine-dynamometer tests were performed to measure NOx conversion under a variety of conditions to assess the impact of ammonia oxidation, inlet NO2/NOx ratio, ammonia/NOx ratio, oxygen level, space velocity, soot loading, and ammonia loading level.

For diesel applications, cold start accounts for a large amount of the total NOx emissions during a typical Federal Test Procedure (FTP) for light-duty vehicles and is a key focus for reducing NOx emissions. A common form of diesel NOx aftertreatment is selective catalytic reduction (SCR) technology. For cold start NOx improvement, the SCR catalyst would be best located as the first catalyst in the aftertreatment system; however, engine-out hydrocarbons and no diesel oxidation catalyst (DOC) upstream to generate an exotherm for desulfation can result in degraded SCR catalyst performance. Recent advances in vanadia-based SCR (V-SCR) catalyst technology have shown better low temperature NOx performance and improved thermal durability. Three V-SCR technologies were tested for their thermal durability and low-temperature NOx performance, and after 600°C aging, one technology showed low-temperature performance on par with state-of-the-art copper-zeolite SCR (Cu-SCR) technology.