Wear resistance is the important characteristics of cast iron materials for automobile components. Because the phenomenon of wear is a highly complicated mechanism involving many factors such as surface conditions, chemical reactions with lubricants, metals, and physics, it has not been fully explained. Therefore, it will be necessary to confirm and explain the wear mechanism to develop effective improvements. The purpose of this study was to investigate the structural change behavior and effects of alloying elements when the material top surface becomes worn, in order to improve the wear resistance of cylinder liners and other cast iron materials. For this purpose, several types of prototype materials were produced, and the relationship between components and wear resistance was investigated by using a laser microscope for quantitative observation of the degree of pearlite microstructure fineness.

The friction pattern on the chamfers of sleeves and dog gears is a combination of peeling and adhesive wear caused by the formation and propagation of fine cracks. The effect of additional elements on wear were checked by making a test apparatus capable of performing evaluations on test pieces equivalent to those using actual parts. The results showed that the addition of B, Ti-Nb helped improve wear resistance. This is attributed to enhanced toughness and reduced peeling due to the formation of a texture. A 45% reduction in wear was achieved in actual parts tests on steel with added B, Ti-Nb.