In order to simulate the perforation corrosion of an automobile, hem model samples made of various kinds of coated steel sheets were set inside of the door outer panel and the door was exposed in the open air with once a week 5% salt spraying. After two years, the model samples were disassembled for investigation. Perforation corrosion occurred most severely just above the lapped portion of outer and inner specimens. Red rust samples taken from the hem model and from a field vehicle run in Detroit did not show clear pearks of spectra by X-ray diffraction analysis, whearas the one formed by a conventional cyclic corrosion test showed peaks of Fe3O4. These facts indicate that this new test well simulates the corrosion environment of an actual automobile hem portion. Corrosion resistance of many kinds of coated steel sheets was studied by this new test method. Perforation depth became smaller as a coating weight of pure zinc electroplated steel sheet increased.

A thin organic coated steel sheet (HI-SUPER-DN) has been recently developed for automotive body panel applications. The steel sheet consists of a Zn-Ni alloy-plated layer, a chromate film and a thin organic coated layer, which is composed of colloidal silica, organic polymer and an organic additive. Corrosion resistance, formability of the coated layer, weidability and electropaintability of the steel sheet required for automotive body panel were studied. An increase in the colloidal silica in the organic coated layer improves corrosion resistance. However, the formability of the organic coated layer deteriorates with such as increase in the colloidal silica. We have optimized the ratio of colloidal silica to organic polymer so as to balance both the corrosion resistance and the formability of the organic coated layer. Futhermore, the bake-hardenability of the steel sheet was maintained by a relatively low temperature baking of the chromate film and the organic coated layer.