In order to simulate the perforation corrosion of an automobile, hem model samples made of various kinds of coated steel sheets were set inside of the door outer panel and the door was exposed in the open air with once a week 5% salt spraying. After two years, the model samples were disassembled for investigation. Perforation corrosion occurred most severely just above the lapped portion of outer and inner specimens. Red rust samples taken from the hem model and from a field vehicle run in Detroit did not show clear pearks of spectra by X-ray diffraction analysis, whearas the one formed by a conventional cyclic corrosion test showed peaks of Fe3O4. These facts indicate that this new test well simulates the corrosion environment of an actual automobile hem portion. Corrosion resistance of many kinds of coated steel sheets was studied by this new test method. Perforation depth became smaller as a coating weight of pure zinc electroplated steel sheet increased.

Trivalent chromate coating is replacing the conventional hexavalent chromate coating applied on zinc plating. Zinc plating uses one of three types of plating baths (zincate, cyanide and chloride) according to the characteristics required of subject parts. It has been recognized that trivalent chromate coating provides different corrosion resistance depending on the type of zinc plating bath used. Zinc plating with chromate coating were analyzed to clarify the cause of the corrosion resistance variation with the type of zinc plating bath. It has been revealed that the chromate coating thickness and the condition of top SiO2 layer vary with the type of zinc plating bath, resulting in corrosion resistance variation.

The influence of additional elements of aluminum alloy, especially of the elements other than conventional low melting point metals on machinability was investigated. Namely, the respective influences of Si, Ni, Mn and Fe on the machinability of AA6061 alloy used as base material were investigated. With the increase in the amount of each element the machinability of the alloy was improved. Si was the most effective among them, and Ni, Mn and Fe followed it in this order. It was found by microscopic observation that machinability was improved in proportion to the dispersion density of the second phase particles formed by the respective additional elements.

In an evaluation of crashworthiness for the cars made of aluminum alloys, the evaluation considering fracture phenomenon comes to be needed because conventional aluminum alloys have low fracture strain (10-20%). In case of the development of a B-Pillar made by die cast, if crack occurrence, furthermore, separation of a part can be estimated by using CAE in crashworthiness evaluations, we can reduce the number of prototype makings and the cost of development using expensive dies. Therefore, we performed crashworthiness evaluations by CAE using some sort of a damage & fracture material model. It is known as “Orthotropic damage & fracture model”.

Aisin AW (AW) and Toyota Motor Corporation (TMC) have developed a new RWD 6 speed automatic transmission, AWR6B45(AC60), suitable for SUV’s and LDT’s in the worldwide market, not only for North America but also for other countries including emerging nations. This 6 speed automatic transmission has achieved low cost, equivalent to AW and TMCs’ current 5 speed automatic transmission, while realizing improvement in both fuel economy and driving performance against current in-house 5-speed automatic transmissions, in addition to satisfying both toughness against various usage and light weight/compactness. They are accomplished by using a compact gear train structure, the latest efficiency improvement technologies, and a high-response, compact hydraulic control system. In addition, the compactness of this 6 speed automatic transmission enables it to replace current 4 speed and 5 speed automatic transmissions for various engine applications.

It has been reported that engine oils containing magnesium detergents gel under special conditions. The authors have previously reported on the mechanism by which magnesium detergents form needle crystals, which is the main cause of the gelation[1]. For this article, the authors conducted tests in actual vehicles using several types of engine oils containing magnesium detergents, including oils for which gelation problems have been reported in the market. The gelation was reproduced, and the test oils were ranked by their propensity to gel. In addition, a laboratory test method was used in which water and CO2 were mixed into engine oil under controlled conditions, then left stored in a bottle for twenty days, after which the kinematic viscosity and the quantity of insolubles of the mixture were measured. The study demonstrated the correlation between the laboratory test method and the actual vehicle tests.

In order to achieve good adhesive properties, typical decorative plastic plating technology uses a chromic acid process that creates an anchor effect. Due to environmental concerns with hexavalent chromium, there is a need to find alternative processes. Pretreatment using highly concentrated ozonized water was investigated as a novel approach to achieving this goal. In the conventional chromic acid process, strong adhesion between plating membranes is achieved by roughing the ABS (acrylonitrile-butadiene-styrene) resin surface by approximately 1 um. On the other hand, the highly concentrated ozonized water process achieves good adhesion with a smooth resin by changing the resin from ABS to ASA (acrylate-styrene-acrylonitrile). It was discovered that the difference in this strength of adhesion was the difference in resin surface strength (existence of deterioration or otherwise).

The development of an alternative oxygen reduction electrocatalyst to platinum based electrocatalysts is critical for practical use of the polymer electrolyte membrane fuel cell (PEMFC). Transition metal sulfide chalcogenides have recently been reported as a possible candidate for Pt replacement. Our work focused on chalcogenides composed of ruthenium, molybdenum, and sulfur (RuMoS). We elucidate the factors affecting electrocatalytic activity of carbon supported RuXMoY SZ catalyst. This was demonstrated through a correlation of oxygen reduction reaction (ORR) activity of the catalysts with structural changes resulting from designed changes in sulfur composition in the catalysts.

In the 1st generation Toyota "MIRAI" fuel cell stack, carbon protective surface coating is deposited after individual Ti bipolar plate being press-formed into the desired shape. Such a process has relatively low production speed, not ideal for large scale manufacturing. A new coating concept, consisting of a nanostructured composite layer of titanium oxide and carbon particles, was devised to enable the incorporation of both the surface treatment and the press processes into the roll-to-roll production line. The initial coating showed higher than expected contact resistance, of which the root cause was identified as nitrogen contamination during the annealing step that inhibited the formation of the composite film structure. Upon the implementation of a vacuum furnace chamber as the countermeasure, the issue was resolved, and the improved coating could meet all the requirements of productivity, conductivity, and durability for use in the newer generation of fuel cell stacks.

This paper reports a method to evaluate structural performance of extruded aluminum thin-walled box section beams for automobile bumper reinforcement. According to U. S. Federal safety performance requirements for automobile bumper systems, the systems should be able to bear the dynamic load of pendulum impact. To evaluate performance of the bumper system, two stages of research were executed: (1) Bending tests and analyses under quasi-static loading, and (2) Dynamic pendulum tests and their simulation using the finite element method. As a result of these investigations, the relationship between the collapse moment of the beam and the permanent set caused by pendulum test, the effect of absorbers, and the effect of torsional force are discussed.

Replacing the metal car roof with conventional solar modules results in the increase of total car weight and change of center of mass, which is not preferable for car designing. Therefore, weight reduction is required for solar modules to be equipped on vehicles. Exchanging glass to plastic for the cover plate of solar module is one of the major approaches to reduce weight; however, load bearing property, impact resistance, thermal deformation, and weatherability become new challenges. In this paper a new solar module structure that weighs as light as conventional steel car roofs, resolving these challenges is proposed.

Test and verification procedures are a vital aspect of the development process for embedded control systems in the automotive domain. Formal requirements can be used in automated procedures to check whether simulation or experimental results adhere to design specifications and even to perform automatic test and formal verification of design models; however, developing formal requirements typically requires significant investment of time and effort for control software designers. We propose Signal Template Library (ST-Lib), a uniform modeling language to encapsulate a number of useful signal patterns in a formal requirement language with the goal of facilitating requirement formulation for automotive control applications. ST-Lib consists of basic modules known as signal templates. Informally, these specify a characteristic signal shape and provide numerical parameters to tune the shape.

The effect of cross-section and type of alloy on the performance of aluminum extrusions as door beams was investigated. As a result, aluminum door beams were developed which have bending properties comparing favorably with those of door beams made of high tensile strength steel with a tensile strength of 1470 N/mm2. Furthermore, a technology to design door beams with the required performance and bending properties dealing with various car models was developed by making the most of the versatility of aluminum extrusions produced in various types of cross-sections.

We have tried to improve damping capacity of an aluminum alloy by means of dispersing ceramic particles (low damping SiC and high damping NdNbO4) of different sizes and volume fractions in the aluminum alloy by powder metallurgy. It is shown that the damping capacity is increased in every case accompanying an increase of Young's modulus. It is also shown that the intrinsic damping capacity of dispersed particles does not play a role in improving the damping capacity. The increase of the damping capacity seems to be attributed to dislocations breakaway, interaction of fine particles and dislocations, and relaxation of interface between ceramic particles and aluminum matrix.

The details of Di-Air, a new NOx reduction system using continuous short pulse injections of hydrocarbons (HC) in front of a NOx storage and reduction (NSR) catalyst, have already been reported. This paper describes further studies into the deNOx mechanism, mainly from the standpoint of the contribution of HC and intermediates. In the process of a preliminary survey regarding HC oxidation behavior at the moment of injection, it was found that HC have unique advantages as a reductant. The addition of HC lead to the reduction or metallization of platinum group metals (PGM) while keeping the overall gas atmosphere in a lean state due to adsorbed HC. This causes local O₂ inhibition and generates reductive intermediate species such as R-NCO. Therefore, the specific benefits of HC were analyzed from the viewpoints of 1) the impact on the PGM state, 2) the characterization of intermediate species, and 3) Di-Air performance compared to other reductants.

The International Lubricant Standardization and Approval Committee (ILSAC) ATF subcommittee members have compared the two oxidation bench test methods, Aluminum Beaker Oxidation Test (ABOT) and Indiana Stirring Oxidation Stability Test (ISOT), using a number of factory-fill and service-fill ATFs obtained in Japan and in the US. In many cases, the ATFs were more severely oxidized after the ABOT procedure than after the same duration of the ISOT procedure. The relative severity of these two tests was influenced by the composition of the ATFs. The bench test oxidation data were compared with the transmission and the vehicle oxidation test data.

A thin organic coated steel sheet (HI-SUPER-DN) has been recently developed for automotive body panel applications. The steel sheet consists of a Zn-Ni alloy-plated layer, a chromate film and a thin organic coated layer, which is composed of colloidal silica, organic polymer and an organic additive. Corrosion resistance, formability of the coated layer, weidability and electropaintability of the steel sheet required for automotive body panel were studied. An increase in the colloidal silica in the organic coated layer improves corrosion resistance. However, the formability of the organic coated layer deteriorates with such as increase in the colloidal silica. We have optimized the ratio of colloidal silica to organic polymer so as to balance both the corrosion resistance and the formability of the organic coated layer. Futhermore, the bake-hardenability of the steel sheet was maintained by a relatively low temperature baking of the chromate film and the organic coated layer.

In an effort to reduce mass, future automotive bodies will feature lower gage steel or lighter weight materials such as aluminum. An unfortunate side effect of lighter weight bodies is a reduction in sound transmission loss (TL). For barrier based systems, as the total system mass (including the sheet metal, decoupler, and barrier) goes down the transmission loss is reduced. If the reduced surface density from the sheet metal is added to the barrier, however, performance can be restored (though, of course, this eliminates the mass savings). In fact, if all of the saved mass from the sheet metal is added to the barrier, the TL performance may be improved over the original system. This is because the optimum performance for a barrier based system is achieved when the sheet metal and the barrier have equal surface densities. That is not the case for standard steel constructions where the surface density of the sheet metal is higher than the barrier.

Galvannealed steel sheet (GA) is very extensively used for vehicle panels. However ζ-phase (FeZn13) in GA coat causes poor stamping formability. Previously, there were no easy methods to evaluate the influence of ζ-phase on the frictional characteristics other than the X-ray diffraction method. This study will discuss the development of a new testing method: Dr. STAMP Method that is both efficient and convenient with pin-on-disc tester.

Two types of new conceptual lead free overlays are developed for automotive internal combustion(IC) engine bearings. The overlays are consisted of molybdenum disulfide(MoS2) and polyamideimide(PAI) resin for binding. One of the overlays is suitable for diesel engines with higher unit load and the other overlay is suitable for gasoline engines with higher sliding velocity. Both overlays indicate good corrosion resistance and wear resistance comparing with conventional lead base overlay. Moreover, higher fatigue resistance is obtained in combination with high performance lead free bearing alloy. These new bearings have the potential to become alternative materials to conventional copper lead bearings with lead base overlay.