Search Results

Experimental results on influence of trimming conditions on the shape of the sheared surface are combined with the results of stretching sheared samples after trimming. The objective of the research described in this paper is to study the mechanism of fracture initiation and cracks propagation during half-a-dog bone tensile test representing sheared edge stretching condition. One side of the sample had sheared surface obtained by the trimming process while the other side of the sample had a smooth surface. Significant attention was paid to understanding of fracture sources. An interrupted tensile test approach was employed to track fracture initiation and propagation during stretching of sheared surface. The results of the experimental study indicated that multiple sources of fracture were observed in the burr area for trimming with clearances exceeding 10% of the material thickness.

Experimental results on influence of trimming conditions on the shape of the sheared surface are combined with the results of stretching sheared samples after trimming. The objective of the research described in this paper is to study the mechanism of fracture initiation and cracks propagation during half-a-dog bone tensile test representing sheared edge stretching condition. One side of the sample had sheared surface obtained by the trimming process while the other side of the sample had a smooth surface. Significant attention was paid to understanding of fracture sources. An interrupted tensile test approach was employed to track fracture initiation and propagation during stretching of sheared surface. The results of the experimental study indicated that multiple sources of fracture were observed in the burr area for trimming with clearances exceeding 10% of the material thickness.

In recent years, implementation of dual phase (DP) Advanced High Strength Steels (AHSS) and Ultra High Strength Steels (UHSS) is increasing in automotive components due to their superior structural performance and vehicle weight reduction capabilities. However, these materials are often sensitive to trimmed edge cracking if stretching along sheared edge occurs in such processes as stretch flanging. Tool wear is another major issue in the trimming of UHSS because of higher contact pressures at the interface between cutting tools and sheet metal blank caused by UHSS’s higher flow stresses and the presence of a hard martensitic in the microstructure. The objective of the present paper is to study the influence of trimming conditions and tool wear on quality of trimmed edge of DP980 steel sheet. For this purpose, mechanically trimmed edges were characterized for DP980 steel, sheared with six different cutting clearances (from 4% to 40% of the sheet thickness).

Imposing tensile stress on an edge of a sheet metal blank is a common condition in many sheet metal forming operations, making edge formability a very important factor to consider. Because edge formability varies greatly among different materials, cutting methods (and their control parameters), it is very important to have access to an experimental technique that would allow for quick and reliable evaluation of edge formability for a given case. In this paper, two existing techniques are compared: the hole expansion test and the tensile test. It is shown that the hole expansion test might not be adequate for many cases, and is prone to overestimating the limiting strain, because the burr on the sheared edge is typically smaller than what is observed in production. The tensile test represents an effective alternative to the hole expansion test. Advantages and disadvantages of each case are discussed.