THE PURPOSE of this experiment was to determine the role of residual stresses in fatigue strength independent of other factors usually involved when residual stresses are introduced. It consisted of an investigation of the influence of residual stresses introduced by shotpeening on the fatigue strength of steel (Rockwell C hardness 48) in unidirectional bending. Residual stresses were varied by peening under various conditions of applied strain. This process introduced substantially the same amount and kind of surface cold working with residual stresses varying over a wide range of values. It was found that shotpeening of steel of this hardness is beneficial primarily because of the nature of the macro-residual-stresses introduced by the process. There is no gain attributable to “strain-hardening” for this material. An effort was made to explain the results on the basis of three failure criteria: distortion energy, maximum shear stress, and maximum stress.*

PEARLITIC malleable iron crankshafts are being used in the new Pontiac engine as a result of recent developments. This paper discusses the physical properties of pearlitic malleable iron such as elastic modulus, fatigue endurance, and tensile strength. According to the author, definite machining economies result from using pearlitic malleable iron crankshafts.

The purpose of this paper is to illustrate the use of Taguchi experimental methods as a development tool for designing a manufacturing process for inner door panels. Through analysis of experimental results, it was possible to identify critical manufacturing variables, as well as demonstrate inherent process capability.

This study evaluated multi-layer steel and composite head gaskets of various thicknesses (0.43 to 1.5 mm) and fire-ring diameters to determine the influence of head gasket crevices on engine-out hydrocarbon (HC) emissions. The upper limit in the percent reduction in HC emissions from gasket-design modifications is estimated to be about 15%. At part-load conditions, the lowest HC emissions were measured for head-gasket thickness of about 1 mm. Significantly smaller thicknesses of the order of 0.4 mm result in an increase in HC emissions. Substantial hydrocarbon-emissions advantage may be realized by minimizing the gasket-to-cylinder bore offset.

The bulge test in hydroforming is a simple fundamental experiment used to obtain basic knowledge in tube expansion. The results can be used to assist design and manufacturing of hydroformed automotive parts. It also can be used to develop a failure criterion for tubes in hydroforming. For these purposes, a section of a long unsupported tube with fixed ends was simulated numerically to obtain the mechanical states of the tube subjected to internal pressure. Steel and aluminum tubes are used. For the bulge tests, the internal pressure reaches a maximum and then decreases in value without failure while the stress, strain and volume of the tube keep increasing. A failure criterion for the bursting of a tube is proposed based on the stress-strain curve of the material.

This paper describes some methods for greatly reducing or possibly eliminating subjective tuning of suspension parts for ride and handling. Laptop computers can now be used in the vehicle to guide the tuning process. The same tools can be used to select solutions that reduce sensitivity to production and environmental variations. OBJECTIVE Reduce or eliminate time required for tuning of suspension parts for ride characteristics. Improve the robustness of ride performance relative to variations in ambient temperature and production tolerances. PROBLEM REQUIRING SOLUTION AND METHOD OF APPROACH Traditional development programs for new vehicles include time-consuming subjective ride evaluations. One example is shock absorber tuning. Even if sophisticated models define force-velocity curves, numerous hardware iterations are needed to find valvings that will reproduce the curves. Many evaluation rides are needed to modify the valvings to meet performance targets.

Typically, “Reliability and Maintainability (R&M)” is perceived as a tool for products alone. Putting emphasis on reliability only at the cost of maintainability is another archetype. Inclusion of both reliability and maintainability (R&M) in all the phases of the machinery and equipment (M&E) life cycle is required in order to be world competitive in manufacturing. R&M is mainly a design function and it should be a part of any design review. Inclusion of the R&M concept early in the life cycle of M&E is key to cost effective and competitive manufacturing. Neither responsive manufacturing nor preventive maintenance can raise it above the level of inherent R&M.

A rear full overlap car-to-car high speed impact simulation using the DYNA3D Finite Element Software was performed to examine the crush mode for rear structure of a vehicle and to observe the effect of rear bumper system in order to maintain the fuel system integrity. The study was conducted first for two different bumper system configurations, namely: (1) validating the model for struck vehicle with steel rear bumper system, (2) simulating rear end collision with composite rear bumper system attached to the rear rails of struck vehicle. Later a third simulation of the model was conducted with a viable design modification to the composite bumper system for improved crashworthiness. It was identified that a more comprehensive FEA model of the bullet car including front end structure, powertrain components, cooling system and other components which constitute the load paths should be incorporated in the analysis to obtain more meaningful correlation and crashworthiness prediction.

The Auto/Steel Partnership established the Light Truck Frame Project Group in 1996 with two objectives: (a) to develop materials, design and fabrication knowledge that would enable the frames on North American OEM (original equipment manufacturer) light trucks to be reduced in weight, and (b) to improve corrosion resistance of frames on these vehicles, thereby allowing a reduction in the thickness of the components and a reduction in frame weight. To address the issues relating to corrosion, a subgroup of the Light Truck Frame Project Group was formed. The group comprised representatives from the North American automotive companies, test laboratories, frame manufacturers, and steel producers. As part of a comprehensive test program, the Corrosion Subgroup has completed tests on frame coatings. Using coated panels of a low carbon hot rolled and pickled steel sheet and two types of accelerated cyclic corrosion tests, seven frame coatings were tested for corrosion performance.

The performance and production requirements for future passenger vehicles has increased the efforts to replace metal body panels with plastic materials. This has been accomplished, to a large extent on some production vehicles that have been introduced recently. Unfortunately, these plastic body applications have necessitated special off-line handling or low temperature paint processing. However, the advantages of RIM nylon, offer the potential for uniquely new plastic body designs, that can be processed through existing assembly plants, much like the steel panels they are intended to replace. The intent of this paper is to discuss the rationale for future plastic body panel material selection and related nylon RIM development efforts.

A design of experiments is used to study the effect of laser weld parameters on formability of welded blanks for two different material combinations of cold rolled (bare) steel to cold rolled steel and cold rolled steel to hot dipped galvanized steel. Critical weld parameters influencing the formability of welded blanks are identified and the optimum weld set-up condition is obtained based on formability performance and consistency of formability for laser welded blanks. The results are applied to an automotive body side frame. The robustness of welded blank production is also assessed and the final welded set-up condition for the body side frame is obtained based on both the formability of welded blanks and the robustness of welded blank production. The body side frame is successfully made from the welded blanks with this final weld set-up condition.

The Paint Technology Globalization effort is recognized as an important step of accomplishing the leveraging of worldwide resources of both engineering and purchasing in order to improve General Motor's competitiveness. The process used, the benefits derived, the current status of the effort, and the expected results (deliverables) are discussed. These include common materials, processing, and equipment paint specifications to be included in purchasing bid packages.

Over the last five years, the automotive industry has experienced a trend towards niche performance vehicles equipped with high-output powertrains. These high performance vehicles also demand higher output braking systems. One method used to provide enhanced pedal feel and fade performance is to equip vehicles with higher apparent friction linings. The challenge then becomes how to design and manufacture these brake systems without high-frequency disc brake squeal and without paying a significant mass penalty. One alternative is to design disc brake rotors with increased damping. There are several options for increasing rotor damping. The classical approach is to increase the rotor's cast iron carbon content, thus increasing the internal material damping of the rotor. However, this methodology provides only a small increase in rotor damping. Alternatively, the rotor damping can be increased by introducing friction, sometimes referred to as Coulomb damping.

Mechanical properties and welding characteristics of a commercial, dual-phase, low-carbon, cold-rolled steel are described. The new steel, HI-FORM 80d, exhibits a total elongation of about 24% as produced and develops a yield strength of about 625 MPa (91 ksi) in a formed and paint-baked part. Property uniformity is excellent and the weldability essentially equivalent to an AISI 1006 steel. In addition, the aging response of HI-FORM 80d is such that yield strengths near 550 MPa (80 ksi) can be achieved with strains of less than 2% and lower paint-bake temperatures than are currently in use.

The potential of bake hardenable steel as a substitute for SAE 1008 steel to reduce gage and improve dent resistance is investigated in this report. Outer body panels in particular are susceptible to palm printing and other forms of denting. Conventional SAE 1008 steel and a developmental continuous annealed bake hardenable steel from Inland Steel Company are compared for dent performance properties. Bake hardenable (BH) steel is a medium strength (200-350 MPa) steel that receives an increase in yield strength during the heating of the paint bake cycle. An increase in yield strength would result in an increase in dent resistance. The increase in dent resistance is more quantitatively evaluated by comparing the BH steel with the current production material (SAE 1008) of a rear compartment lid outer.

Corrosion resistance has been the major impetus toward increased use of galvanneal and other coated sheet products by the automotive industry. Galvanneal has the additional advantages of good weldability, due to the iron in the coating, and a higher surface porosity which leads to better paint adhesion. The porosity of the galvanneal surface, however, could also lead to reduced cleanability. This paper reports the effects of pretreatment variables on galvanneal phosphatability and resulting painted corrosion performance. The studies showed that the rust preventative oil applied and the alkaline cleaner used to clean samples prior to phosphating had significant effects on carbon residuals after cleaning. The painted corrosion performance of galvanneal panels with various levels of residual carbon showed a much smaller effect within a given cyclic test. The studies also indicated significant differences in performance depending on the type of cyclic test performed.

Casting, machining and structural simulations were completed on a V8 engine block made in Compacted Graphite Iron (CGI) for use in a racing application. The casting and machining simulations generated maps of predicted tensile strength and residual stress in the block. These strength and stress maps were exported to a finite element structural model of the machined part. Assembly and operating loads were applied, and stresses due to these loads were determined. High cycle fatigue analysis was completed, and three sets of safety factors were calculated using the following conditions: uniform properties and no residual stress, predicted properties and no residual stress, and predicted properties plus residual stress.

Electro-Motive Division of GM jointly with HRL Laboratories have developed a software tool, called TechPro, which assists in troubleshooting of diesel locomotives. The tool has been tested extensively in the field for the last two years. It has improved significantly the quality of diagnosis of locomotives. The tool is based on Graphical Probabilistic Models and Case Data Bases. We will discuss the design of the tool, its performance and will show its relevance to diagnosis of automobiles.

Truck driver shin-knee and stomach postion tools have been developed to describe where certain percentages of truck drivers position there knees and stomachs in various workspace arrangements. Separate equations describe the accommodation level for driver populations with male to female ratios of 50/50, 75/25, and a range from 90/10 to 95/5. These equations can be used as a design tool to locate the curves in vehicle space to describe the region behind which the given populations shin-knees, and stomachs would be located. Equations and curves are provided for both the left leg, which operates the clutch, and the right leg, which operates the accelerator.

Truck driver eye and head position tools have been developed to describe where certain percentages of truck drivers position there eyes and heads in various workspace arrangements. Separate equations describe the accommodation level for driver populations with male to female ratios of 50/50, 75/25, and a range from 90/10 to 95/5. These equations can be used as a design tool to locate the curves in vehicle space to describe the region behind which the given populations eyes and heads would be located. Equations and curves are provided for both the drivers eye and head in the side view. It has become increasingly apparent that there is a need for improved methods of accommodating truck drivers in heavy truck cab design. Currently, practices used in the automobile industry for passenger car design are utilized for the design of heavy trucks. These practices.