Search Results

The bending fatigue performance of high temperature (1050 °C) vacuum carburized Nb modified 8620 steel, with niobium additions of 0.02, 0.06 and 0.1 wt pct, was evaluated utilizing a modified Brugger specimen geometry. Samples were heated at two different rates (20 and 114 °C min-1) to the carburizing temperature resulting in different prior austenite grain structures that depended on the specific Nb addition and heating rate employed. At the lower heating rate, uniform fine grained prior austenite grain structures developed in the 0.06 and 0.1 Nb steels while a duplex grain structure with the presence of large (>200 μm grains) developed in the 0.02 Nb steel. At the higher heating rate the propensity for abnormal grain growth was highest in the 0.02 Nb steel and complete suppression of abnormal grain growth was achieved only with the 0.1 Nb steel.

In stamping advanced high strength steels (AHSS), the deviations from desired part geometry caused by springback from a radius, curl, twist, and bow are major impediments to successfully producing AHSS parts. In general, the conventional elastic modulus is used to quantify the strain that occurs on unloading. This unloading strain causes deviations from desired part geometry. Considerable evidence in the literature indicates that for tensile testing, the conventional elastic modulus does not accurately describe the unloading strain. The present study uses new data and results from the literature to examine the average slope of tensile stress strain curves on unloading. This slope is termed the effective unloading modulus. The results from this study quantitatively describe how the effective unloading modulus decreases with increasing strength, prestrain, and unloading time.

High strain rate sheet tensile tests (up to 300s-1) and Ohio State University (OSU) formability tests (up to an estimated strain rate of 10s-1) were performed to examine the effect of strain rate on the mechanical properties and formability of five ferritic stainless steels: HIGH PERFORMANCE-10™ 409 (HP-10 409), ULTRA FORM® 409 (UF 409), HIGH PERFORMANCE-10™ 439 (HP-10 439), two thicknesses of 18 Cr-Cb™ stainless steel, all supplied by AK Steel, and Duracorr®, a ferrite-tempered martensite dual-phase stainless steel supplied by Bethlehem Steel Corporation. Tensile results show that increasing strain rate resulted in increases in yield stress, flow stress, and stress at instability for all alloys tested. In addition, increases in uniform and total elongation were also found for each of the five alloys.

Forging simulations with a 1522 steel microalloyed by additions of 0.25% Mo, 0.13% V and 0.01% Ti were performed on a laboratory thermomechanical processing simulator. The forging conditions included a strain rate of 22s-1, 50% strain, and temperatures in the range from 1200°C to 950°C. The true stress was found to increase with decreasing deformation temperature for all values of instantaneous true strain. The maximum flow stress increased two-fold as deformation temperature decreased from 1200°C to 950°C, and the recrystallized austenite grain size decreased by a factor of two for this same decrease in temperature. Microstructures evolve from bainitic/ferritic at a cooling rate of 1.4°C/s, to fully martensitic at 16.8°C/s, independent of deformation temperature. Room temperature hardnesses depended primarily on cooling rate and were essentially independent of deformation temperature.

Regulated emissions (THC, CO, NOx, and PM) and particulate SOF and sulfate fractions were determined for a 1995 Detroit Diesel Series 50 urban bus engine at varying fuel sulfur levels, with and without catalytic converters. When tested on EPA certification fuel without an oxidation catalyst this engine does not appear to meet the 1994 emissions standards for heavy duty trucks, when operating at high altitude. An ultra-low (5 ppm) sulfur diesel base stock with 23% aromatics and 42.4 cetane number was used to examine the effect of fuel sulfur. Sulfur was adjusted above the 5 ppm level to 50, 100, 200, 315 and 500 ppm using tert-butyl disulfide. Current EPA regulations limit the sulfur content to 500 ppm for on highway fuel. A low Pt diesel oxidation catalyst (DOC) was tested with all fuels and a high Pt diesel oxidation catalyst was tested with the 5 and 50 ppm sulfur fuels.

With the increased use of tubular steel products, especially for automotive hydroforming applications, there is increased interest in understanding the mechanical properties measured by tensile tests from specimens of different orientations in the tube. In this study, two orientations of tensile specimens were evaluated -- axial specimens with and without flattening and flattened circumferential specimens. Three steels were evaluated -- two thicknesses of aluminum killed drawing quality (AKDQ) steel and one thickness of high strength low alloy (HSLA) steel. Mechanical property data were obtained from the flat stock, conventional production tubes and quasi tubes. Quasi tubes were produced from the flat stock on a 3-roll bender, but the quasi tube was not welded or sized.

The Timken Company's Faircrest Steel Plant has numerous automated control systems. The Raw Material Handling System and a grinder application on the Billet Conditioning system needed upgrading; however, to control costs the upgrades had to use the existing I/O. The overall functionality of these two systems is vastly different. Soft control packages proved capable of interfacing with the existing I/O, satisfied the functional needs of the systems, and enhanced the overall functionality of the systems.

Knowledge of the net thinning strain that occurs in a sheet as it is bent over a single radius is an important component in understanding sheet metal formability. The present study extends the initial work of Swift on thinning during plane-strain bending to sheet steels with power law stress-strain behavior and with the inclusion of friction. The experimental data come from studies on the enhanced forming limit curve on DQSK steel and analysis of the curl behavior of 590R and DP600 steels. Results for single radius bending from these studies are used in the present investigation. It has been found that the amount of net thinning strain depends on back tension, initial plane-strain yield strength, and the maximum true bending strain calculated for the neutral plane at the mid-thickness of the sheet.

The influences of laboratory-induced hydrogen on the tensile deformation and fracture behavior of selected sheet steels including conventional DQSK and HSLA steels as well as newer DP and TRIP grades were evaluated. The effects of cold work, simulated paint baking, and natural aging were considered. Hydrogen effects were observable by increased flow stress, decreased ductility, altered neck geometry, and altered fracture mechanisms. Differences among the steels and conditions were observed and interpreted on the basis of microstructure, fracture behavior, and theories of hydrogen embrittlement.

Most environments inhabited by living beings have dust. Much of that dust comes from the continuous flaking of our own skin and atmosphere borne particles of submicron size. Dust mites seem to play an important role in integrating fine scale dust, which they consume to grow, resulting in larger length scale dust. Dust continues to agglomerate and grow. Air filters are designed to remove dust and control dust agglomeration. We report a simple scaling law, based on kinematic simulations of dust filtration through a one dimensional idealized filter. The results reveal insights regarding how filters may clog in time. Our results may be of use to someone interested in designing customized air filters for optimum dust removal in an environment with a known dust distribution.

Aluminum nitride and microalloy carbonitrides have been identified as microstructural features that degrade the ductile fracture resistance of tempered martensitic microstructures. A thermal/thermomechanical process has been developed to optimize the toughness of high-strength steels containing any species of grain-refining precipitate that is soluble in austenite, and the process is particularly effective at improving the impact toughness of aluminum-killed EAF steels. The process affects the mode of unstable fracture in tempered martensitic microstructures, such that at constant strength and austenite grain size, substantial improvements are realized in both longitudinal and transverse toughness over relatively broad ranges of sulfur content and tempering temperature.

Drawbeads in production stamping dies often have insufficient penetration of the male bead into the female cavity. With insufficient penetration, the actual bending radii of the sheet metal are larger than the geometrical radii of the drawbead. The actual bending radii in the sheet directly affect the force that restrains sheet movement. To predict the restraining stress due to a drawbead, it is necessary to know the actual bending radii in the sheet as it passes though the drawbead. Data from a previous study are used to develop empirical regression equations for predicting measured radii of the sheet that is bent around the radii in a drawbead. A physical model for the evolution of the sheet radii as the drawbead closes is proposed. This model is consistent with the empirical equations and the mechanics of the sheet bending process.

The effectiveness of three different techniques, designed to improve the bending fatigue life in comparison to conventionally processed gas-carburized 8620 steel, were evaluated with modified Brugger bending fatigue specimens and actual ring and pinion gears. The bending fatigue samples were machined from forged gear blanks from the same lot of material used for the pinion gear tests, and all processing of laboratory samples and gears was done together. Fatigue data were obtained on standard as-carburized parts and after three special processing histories: shot-peening to increase surface residual stresses; double heat treating to refined austenite grain size; and vacuum carburizing to minimize intergranular oxidation. Standard room-temperature S-N curves and endurance limits were obtained with the laboratory samples. The pinions were run as part of a complete gear set on a laboratory dynamometer and data were obtained at two imposed torque levels.

Prediction of fatigue performance of large structures and components is generally done through the use of a fatigue analysis software, FEA stress/strain analysis, load spectra, and materials properties generated from laboratory tests with small specimens. Prior experience and test data has shown that a specimen size effect exists, i.e. the fatigue strength or endurance limit of large members is lower than that of small specimens made of same material. Obviously, the size effect is an important issue in fatigue design of large components. However a precise experimental study of the size effect is very difficult for several reasons. It is difficult to prepare geometrically similar specimens with increased volume which have the same microstructures and residual stress distributions throughout the entire material volume to be tested. Fatigue testing of large samples can also be a problem due to the limitation of load capacity of the test systems available.

A series of bending fatigue tests were conducted and S-N data were obtained for two groups of 4320 steel samples: (1) carburized, quenched and tempered, (2) carburized, quenched, tempered and shot peened. Shot peening improved the fatigue life and endurance limit. The S-N data exhibited large scatter, especially for carburized samples and at the high cycle life regime. Sample characterization work was performed and scatter bands were established for residual stress distributions, in addition to fracture and fatigue properties for 4320 steel. Moreover, a fatigue life analysis was performed using fracture mechanics and strain life fatigue theories. Scatter in S-N curves was established computationally by using the lower bound and upper bound in materials properties, residual stress and IGO depth in the input data. The results for fatigue life analysis, using either computational fracture mechanics or strain life theory, agreed reasonably well with the test data.

The influence of coatings on fatigue behavior has been examined for the following commercially produced sheet steels: uncoated titanium stabilized interstitial-free (IF); electrogalvanized titanium stabilized IF; hot-dip galvanized aluminum killed, drawing quality (AKDQ); and galvannealed AKDQ. Fully reversed bending fatigue tests were conducted at ambient temperature on Krouse-type flexural fatigue machines. A dependence of crack development was observed and correlated to the microstructure and properties of the different coatings. Furthermore, a functional design relationship for each material was determined through stress-life analysis. The experimentally determined fatigue properties were compared to conventional estimates based on tensile properties which ignore coating effects. The results of this work suggest that ductile coatings may enhance fatigue resistance, while brittle coatings may reduce fatigue life.

The Timken Company performed a detailed study involving topographical imagery and surface mapping. The primary purpose of the study was to develop a direct correlation between surface topography and component durability/life. Through these studies, an optimal surface finish was developed. A production environment was then formed to mass-produce components with this finish on a contact-to-contact component. The results of the study guide us to an increase in durability/life of the Timken product. The paper is divided into three sections. The first section describes the component itself and the testing procedures by which durability/life were determined. The second section describes the analytical work done at the Timken Research facility where topographical imagery and surface mapping were performed. At this time, topographical analysis of several surface finishes paved the way to create an optimal surface texture for increased durability/life.

This study summarizes the development, characterization, and application of nanocomposite tribological coatings on rolling element bearings. Nanocomposite coatings consisting of nanocrystalline metal carbides embedded in amorphous hydrocarbon or carbon matrices (MC/aC:H or MC/aC) have been used to increase the fatigue life under boundary layer lubrication, provide debris tolerance, eliminate false brinelling, increase the operational speed, decrease the friction, and provide oil-out protection to rolling element bearings. MC/aC:H coatings are applied by magnetron sputtering at substrate temperature less than 180 °C, have small friction coefficients, high fracture strength, and can have hardness and modulus values twice and half that of carburized steel, respectively.

The susceptibility of Advanced High Strength Steels (AHSS) to hydrogen embrittlement (HE) was evaluated on selected high strength sheet steels (DP 600, TRIP 780, TRIP 980, TWIP-Al, TWIP, and Martensitic M220) and the results were compared to data on a lower strength (300 MPa tensile strength) low carbon steel. Tensile samples were cathodically charged and then immediately tensile tested to failure to analyze the mechanical properties of the as-charged steel. The effects of hydrogen on deformation and fracture behavior were evaluated through analysis of tensile properties, necking geometry, and SEM images of fracture surfaces and metallographic samples of deformed tensile specimens. The two fully austenitic TWIP steels were resistant to hydrogen effects in the laboratory charged tensile samples.

This work establishes the relationship between core hardness, case hardness, and case depth on susceptibility to hydrogen embrittlement of case hardened steel fasteners. Such fasteners have a high surface hardness in order to create their own threads in a mating hole, and are commonly used to attach bracketry and sheet metal in automotive applications. While case hardened fasteners have been studied previously, there are currently no processing guidelines supported by quantitative data for fastener standards. Through sustained load embrittlement testing techniques, the susceptibility of case hardened steel tapping screws to internal and environmental hydrogen embrittlement is examined. Further characterization of the fastener samples through microhardness testing, microstructure review, and fracture surface examination allows the investigation of susceptibility thresholds. It is shown that core hardness is the primary consideration for susceptibility.