Springback is a major concern in stamping of advanced high strength steels (AHSS). The existing computer simulation technology has difficulty predicting this phenomenon accurately even though it is well developed for formability simulations. Great efforts made in recent years to improve springback predictions have achieved noticeable progress in the computational capability and accuracy. In this work, springback simulation studies are conducted using FEA software LS-DYNA®. Various parametric sensitivity studies are carried out and key variables affecting the springback prediction accuracy are identified. Recently developed simulation technologies in LS-DYNA® are implemented including dynamic effect minimization, smooth tool contact and newly developed nonlinear isotropic/kinematic hardening material models. Case studies on lab-scale and full-scale industrial parts are provided and the predicted springback results are compared to the experimental data.

More and more advanced high strength steels (AHSS) such as dual phase steels and TRIP steels are implemented in automotive components due to their superior crash performance and vehicle weight reduction capabilities. Recent trends show increased applications of higher strength grades such as 780/800 MPa and 980/1000 MPa tensile strength for crash sensitive components to meet more stringent safety regulations in front crash, side impact and roll-over situations. Several issues related to AHSS stamping have been raised during implementation such as springback, stretch bending fracture with a small radius to thickness ratio, edge cracking, etc. It has been shown that the failure strains in the stretch bending fracture and edge cracking can be significantly lower than the predicted forming limits, and no failure criteria are currently available to predict these failures.

Advanced high strength steels (AHSS) have been widely accepted as a material of choice in the automotive industry to balance overall vehicle weight and stringent vehicle crash test performance targets. Combined with efficient use of geometry and load paths through shape and topology optimization, AHSS has enabled vehicle manufacturers to obtain the highest possible ratings in safety evaluations by the Insurance Institute for Highway Safety (IIHS) and the National Highway Traffic Safety Administration (NHTSA). In this study, vehicle CAE side impact models were used to evaluate three side impact crash test conditions (IIHS side impact, NHTSA LINCAP and FMVSS 214 side pole) and the IIHS roof strength test condition and to identify several key components affecting the side impact test performance. HyperStudy® optimization software and LS-DYNA® nonlinear finite element software were utilized for shape and gauge optimization.

The issue of cost and weight reduction at optimum car crash safety is a driving force behind the growing use of advanced high strength steels, particularly in Europe and Japan. Recent developments in the availability of high strength steel (HSS) sheets in North America; in particular transformation induced plasticity (TRIP) steels, offer an attractive option to the automotive designer for weight reduction and improved safety performance. For example, the use of TRIP steels, as opposed to more conventional steel products such as high strength low alloy (HSLA), in some applications may result in up to 40% part weight reduction at similar vehicle crash performance. When the excellent formability of TRIP steel is considered at product design stage, it may also lead to reducing part count and tooling cost. In this paper the formability of TRIP steels of various gauges is assessed. Experimental forming limit curves (FLCs) are determined for T600 grade.

The front rail plays a very important role in vehicle crash. Trigger holes are commonly used to control frame crush mode due to their simple manufacturing process and flexibility for late changes in the product development phase. Therefore, a study, including CAE and testing, was conducted on a production front rail to understand the effects of trigger hole shape, size and orientation. The trigger hole location in the front rail also affects crash performance. Therefore, the effect of trigger hole location on front rail crash behavior was studied, and understanding these effects is the main objective of this study. A tapered front rail produced from 1.7 mm thick DP600 steel was used for the trigger hole location investigation. Front rails with different trigger spacing and sizes were tested using VIA sled test facility and the crash progress was simulated using a commercial code RADIOSS. The strain rate, welding and forming effects were incorporated in the front rail modeling.

Because of their excellent crash energy absorption capacity, dual phase (DP) steels are gradually replacing conventional High Strength Low Alloy (HSLA) steels for critical crash components in order to meet the more stringent vehicle crash safety regulations. To achieve optimal axial and bending crush performance using DP steels for crash components designed for crash energy absorption and/or intrusion resistance applications, the cross sections need to be optimized. Correlated crush simulation models were employed for the cross-section study. The models were developed using non-linear finite element code LS-DYNA and correlated to dynamic and quasi-static axial and bending crush tests on hexagonal and octagonal cross-sections made of DP590 steel. Several design concepts were proposed, the axial and bending crush performance in DP780 and DP980 were compared, and the potential mass savings were discussed.

Advanced High Strength Steels (AHSS) are replacing conventional high strength low-alloyed steels (HSLA) in crash sensitive body in white (BIW) applications. Along with innovative product design, they offer superior crash energy management and vehicle weight reduction potential. However, Controlling springback and dimensional accuracy is one of the major concerns in manufacturing AHSS parts. One of the most effective springback control techniques is to design a part with added geometric features such as side stiffening beads, state beads, top hat beads, and embossments, etc. at the product design stage. On the other hand, product design communities tend to believe that the above listed features may result in premature crash initiation in the part. This paper uses an innovative and experimentally verified finite element method (FEM) for crash sensitive component design and optimization.

Advanced High Strength Steels (AHSS) have been implemented in the automotive industry to balance the requirements for vehicle crash safety, emissions, and fuel economy. With lower ductility compared to conventional steels, the fracture behavior of AHSS components has to be considered in vehicle crash simulations to achieve a reliable crashworthiness prediction. Without considering the fracture behavior, component fracture cannot be predicted and subsequently the crash energy absorbed by the fractured component can be over-estimated. In full vehicle simulations, failure to predict component fracture sometimes leads to less predicted intrusion. In this paper, the feasibility of using computer simulations in predicting fracture during crash deformation is studied.

Advanced High Strength Steels (AHSS) along with innovative design and manufacturing processes are effective ways to improve crash energy management. Crash trigger hole is another technology which can been used on front rails for controlling crash buckling mode, avoiding crash mode instability and minimizing variations in crash mode due to imperfections in materials, part geometry, manufacturing, and assembly processes etc. In this study, prototyped crash columns with different trigger hole shapes, sizes and locations were physically tested in frontal crash impact tests. A corresponding crash computer simulation model was then created to perform the correlation study. The testing data, such as crash force-displacement curves and dynamic crash modes, were used to verify the FEA crash model and to study the trigger sensitivity and effects on front rail crash performance.

Forming Limit Diagrams (FLD) have been widely and successfully used in sheet metal stamping as a failure criterion to detect localized necking, which is the most common failure mechanism for conventional steels during forming. However, recent experience from stamping Dual-Phase steels found that, under certain circumstances such as stretching-bend over a small die radius, the sheet metal fails earlier than that predicted by the FLD based on the initiation of a localized neck. It appears that a different failure mechanism and mode are in effect, commonly referred to as “shear fracture” in the sheet metal stamping community. In this paper, experimental and numerical analysis is used to investigate the shear fracture mechanism. Numerical models are established for a stretch-bend test on DP780 steel with a wide range of bend radii for various failure modes. The occurrences of shear fracture are identified by correlating numerical simulation results with test data.

Studies in an Angular Stretch Bend Test (ASBT) have demonstrated that the failure location moves from the side wall to punch nose area. This occurs as the R/T ratio decreases below a certain limit and applies to most low carbon steels with the exception of Dual Phase (DP) steels. Such behavior in DP steels indicates that bending effects have a severe impact on the formability of DP materials. Therefore, the traditional criterion using the forming limit curve (FLC) is not suitable to assess the formability at punch radius areas for DP steels due in part to its uniqueness of unconventional microstructures. In this paper, a new failure criterion, ‘Bending-modified’ FLC (BFLC), is proposed by extending the traditional FLC using the “Stretch Bendability Index” (SBI) concept for the stretch bendability assessment.

Experimental procedures and results of a benchmark test for springback are reported and a complete suite of obtained data is provided for the validation of forming and springback simulation software. The test is usually referred as the Slit-Ring test where a cylindrical cup is first formed by deep drawing and then a ring is cut from the mid-section of the cup. The opening of the ring upon slitting releases the residual stresses in the formed cup and provides a valuable set of easy-to-measure, easy-to-characterize springback data. The test represents a realistic deep draw stamping operation with stretching and bending deformation, and is highly repeatable in a laboratory environment. In this study, six different automotive materials are evaluated.