Recently, joining of cast aluminum components with wrought and/or cast similar metals becomes an urgent task for the auto industry to develop light-weight complex and large-scale chassis and body structures for further reduction in vehicle weight. In this study, fusion-joining of vacuum high pressure die cast (VHPDC) alloy A356 subjected to T5 heat treatment and wrought alloy 6061 with the Gas Metal Arc Welding (GMAW-MIG) process was experimented in an effort to understand the effect of the MIG process on the microstructure development and tensile behaviors of the base alloys (T5 A356 and 6061), Heat Affected Zone (HAZ) and Fusion Zone (filler metal ER4043). The results of tensile testing indicated that the ultimate tensile strength (UTS), yield strength (YS) and elongation (Ef) of VHPDC T5 A356 were relatively high, compared to both wrought alloy 6061 and the filler metal (ER 4043).

Quasi-static axial cutting of AA6061-T6 and T4 round extrusions were completed using a specially designed cutter with multiple blades. The round specimens had a length of 200 mm, a nominal outer diameter of 50.8 mm, and a wall thickness of 3.175 mm or 1.587 mm. Four different cutters, constructed from heat-treated 4140 steel, having 3, 4, 5 and 6 blades on each cutter with a nominal tip width of 1.0 mm were used to penetrate through the round extrusions. A clean cutting mode was observed for the AA6061-T6 and T4 extrusions with wall thickness of 3.175 mm with an almost constant steady state cutting force. A braided cutting mode was observed for extrusions with both tempers with wall thickness of 1.587 mm, which resulted in a slightly oscillating steady state cutting force. For all extrusions with a wall thickness of 3.175 mm, the steady state cutting force increased with an increase in the number of cutter blades.