Nano-silver sintered bonding was carried out at 275°C and under 3MPa pressures, and soldering in a vacuum reflowing oven to reduce voiding. Both joints are subject to large shear stresses due to the mismatch in coefficients of thermal expansion (CTE) between the chip and the substrate. In this study, residual stresses in the chip-on-substrate assemblies were determined by measuring the bending curvatures of the bonded structures. An in-house optical setup measured the bending curvatures using a thin-film stress measurement technique. From the measured bending curvatures and the mechanical properties of the constituent materials, residual stresses were calculated. The thermo-mechanical reliabilities of both joining techniques were tested by thermal cycling. The chip assemblies were cycled between -40°C and 125°C (100 minutes of cycle time, 10 minutes of dwell time) and the changes in their bending curvatures were measured.

Modern fatigue analysis techniques, that can provide reliable estimates of the service performance of components and structures, are finding increasing use in vehicle development programs. A major objective of such efforts is the prediction of the field performance of a fleet of vehicles as influenced by the host of design, manufacturing, and performance variables. An approach to this complex problem, based on the incorporation of probability theory in established life prediction methods, is presented. In this way, quantitative estimates of the lifetime distribution of a population are obtained based on anticipated, or specified, variations in component geometry, material processing sequences, and service loading. The application of this approach is demonstrated through a case study of an automotive transmission component.

The effect of Si-phase on the axial, low-cycle fatigue behavior of Al-Si eutectic alloys was investigated using test specimens prepared from alloys processed either by continuous casting or extrusion. Results indicate that, for continuous casting, all fatigue fractures resulted from shear-type crack initiation and propagation with an attendant shortening of fatigue life. For extruded material, fatigue cracks originated in the Si phase. In both instances, initiation and growth mechanisms were essentially identical to those observed in high-cycle fatigue. Cyclic properties obtained from phenomenological models are presented and discussed.

Binder jetting of sand molds and cores for metal casting provides a scalable and efficient means of producing metal components with complex geometric features made possible only by Additive Manufacturing. Topology optimization software that can mathematically determine the optimum placement of material for a given set of design requirements has been available for quite some time. However, the optimized designs are often not manufacturable using standard metal casting processes due to undercuts, backdraft and other issues. With the advent of binder-based 3D printing technology, sand molds and cores can be produced to make these optimized designs as metal castings.