Search Results

Abstract One of the most important aluminum (Al) alloys among the 7XXX series is 7075 in the T6 temper condition. However, 7075 T6 alloy is proven to be susceptible to stress corrosion cracking (SCC) and has caused many service failures of airplanes. In this research, the susceptibility of 7075 T6 alloys to SCC is approached according to many variables of stress, sodium chloride (NaCl) concentration, pH variation, and aeration. The testing method selected was the three-point bending under complete immersion for a period of 40 days. The results indicate that the threshold for SCC in 7075 T6 alloy lies between 220 and 340 MPa in environments containing as low as 0.5% NaCl concentrations in both neutral and acid solutions. The cracking direction found was different from the expected using other techniques such as tensile or notched specimens, which opens a new gate for testing and monitoring SCC in the 7XXX series.

Abstract In this article, Al-Mg-Si-Mn alloy (AA6082) is butt joined by employing friction stir welding (FSW). The mechanical and metallurgical properties of joints are analyzed by conducting tensile and microhardness testing, respectively. To measure the temperature at different locations, eight thermocouples (L-shaped k-type) are placed at equal distance from the centerline. Least square method attempts to calculate the temperature at the centerline of joints. The process parameters are also optimized using Taguchi’s five-level experimental design. The optimum process parameters are determined, employing ultimate tensile strength (UTS) as a response parameter. A statistical test “analysis of variance” is used to check the adequacy of the model. It has been observed that rotational speed and feed rate are the predominant factors for UTS and microhardness.

Abstract The supersession of metallic alloys with lightweight, high-strength composites is popular in the aircraft industry. However, aviation electronic enclosures for large format batteries and high power conversion electronics are still primarily made of aluminum alloys. These aluminum enclosures have attractive properties regrading structural integrity for the heavy internal parts, electromagnetic interference (EMI) suppression, electrical bonding for the internal cells, and/or electronics and failure containment. This paper details a lightweight carbon fiber composite chassis developed at Meggitt Sensing Systems (MSS) Securaplane, with a copper metallic mesh co-cured onto the internal surfaces resulting in a 50% reduction in weight when compared to its aluminum counterpart. In addition to significant weight reduction, it provides equal or improved performance with respect to EMI, structural and flammability performance.

Abstract The present investigation has been conducted to study the tribological and adhesion properties of X10CrNi18-8 austenitic stainless steel (ASTM 301) coatings deposited on aluminum alloys such as AU4G by using the arc-spraying process. These coatings were made with and without a bond-coat layer, which is constituted by NiAl. The structure of the phases that are present in coatings was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The measurements of microhardness and tribological behavior at different loads were also performed on the surface of the coatings. Adherence test was also carried out using four-point bending tests. The SEM showed that the dense microstructures of coatings have a homogeneous lamellar morphology with the presence of porosities and unmelted particles. The main phase of coating corresponds to a solid solution as a face-centered cubic (fcc).