The SP-100 reactor will operate at temperatures up to 1500K in high vacuum. Development of bearing coatings is necessary to avoid self welding and/or galling of moving components. No experience base exists for these conditions-the early SNAP (Space Nuclear Auxiliary Power) program requirements were over 400K lower with shorter lifetime requirements. To address the SP-100 needs, a tribology development program has been established at GE to investigate candidate coating materials. Materials were selected based on their high thermodynamic stability, high melting point, compatibility with the substrate, and coefficients of thermal expansion similar to niobium-1% zirconium - the candidate structural material for SP-100. An additional requirement was that the deposition processes should be commercially available to coat large components.

Initial preliminary development phases of two distinct SP-100 control drive assembly bearing test programs were successfully completed at elevated temperature in vacuum. The first was for the reflector drive line spherical self-aligning bearings. Each bearing consisted of a carbon-graphite ball mounted on an aluminum oxide-coated Ta-10%W shaft, captured by an aluminum oxide-coated Ta-10%W socket. One set of these bearings was exposed to temperatures up to 1180K (1665°F) at 1.33x10-6 Pa (1x10-8 torr) and subjected to 38000 cycles of motion. Friction coefficients were found to be between 0.11 and 0.25 over the full range of operation. Overall performance of the bearings was excellent, with only slight wear observed. The second test program was for the safety rod slider bearing. Zirconium carbide coated Nb-1%Zr bearing pads were stroked inside a molybdenum tube at temperatures up to 1422K (2100°F) at ∼1.33x10-6 Pa with a normal load of 1.02 Kg between each sliding surface.