Search Results

The design of a canned ceramic oval converter, 77mm by 146.8mm, is described along with subsequent demonstration of its high temperature (1050°C) durability. A new mat deterioration phenomenon was recognized, and will be described. The mat deterioration results from sintering of the vermiculite and glass fiber structure when exposed to temperatures greater than approximately 1000°C. Due to the extremely high temperature experienced in the supporting mat of an oval converter exposed to 1050°C, an alternative mat configuration was utilized to eliminate potential mat sintering. An inner layer of non-intumescent mat (1500g/m2) was used in conjunction with an outer layer of intumescent mat (3100g/m2). The inner mat provided sufficient thermal protection to the outer intumescent mat, maintaining considerable holding pressure on the ceramic substrate. A tourniquet closure technique was developed to uniformly compress a hybrid mat system around the entire perimeter of the oval converter.

Wall-flow filter technology has been used for many years to remove particulate emissions from a select number of diesel engine exhaust systems. Significant implementation of diesel particulate filters will require the definition of regeneration strategies that permit the filters to be regularly and durably purged of accumulated non-volatile particulates. This paper will examine the laboratory-bench characterization of filter responses to the wide variety of input conditions to which they may be exposed in practice. The lab-bench filter characterization will be done as a function of generic independent variables such as flow rate, inlet temperature, oxygen content and soot loading. The testing will be conducted on uncatalyzed filters for this preliminary study. The characterization approach will examine such dependent variables as completeness of regeneration and maximum exotherm temperatures.

Characterization of diesel particulate filters requires test methods that permit rapid and accurate assessment of important performance requirements. The operation of the filter is comprised of two primary functions, particle filtering and filter soot regeneration. One challenge facing implementation of diesel filter technology lies with the difficult process of regenerating the filter after accumulating a full complement of soot. This paper will primarily focus on laboratory bench testing methods developed to study the regeneration characteristics of filters under a variety of test conditions. To rapidly assess the performance of many filters it was important to develop laboratory techniques that approximate engine exposure conditions. A simulated soot loading process and a well-controlled regeneration test method were developed.

To meet tightening emissions standards, alternate pollution abatement technologies are necessary, such as an In-Line Adsorber (ILA) system. The ILA has a first catalyst, an adsorber, and a second catalyst. A diverter directs exhaust gas through the adsorber to capture unconverted hydrocarbons until the first catalyst reaches light-off temperature. The ILA system was designed so that the second catalyst becomes active concurrent with the adsorber hydrocarbon desorption. The system was evaluated using the FTP test with two different secondary air strategies on 3.8 liter V6 and 4.0 liter V8 vehicles. The ILA system performance consistently reduced ∼50-60% of cold start hydrocarbon emissions. This study examined a simplified ILA system designed to operate with a commercial secondary air pump powered by the engine.

In this study quantitative techniques were established to assess the low temperature durability of commercially available mat systems. A new low temperature dynamic resistive thermal exposure (LT-RTE) test method was developed. The mats were evaluated in thermal cycling with maximum substrate skin temperatures from 280°C to 450°C. Results indicate that at low use temperatures the residual shear strength of the mat fell to ∼5-15KPa following 280°C cycling. Under the same LT-RTE exposure conditions an equivalent mat system, following thermal preconditioning to 500°C for 3 hours, possessed a residual shear strength of ∼30KPa. An alternative mat system with a lower shot content fiber was also evaluated, following the same thermal preconditioning previously described. This alternative mat was found to exhibit substantially higher residual shear strengths following LT-RTE aging. A residual shear strength of ∼95KPa was observed for this alternative mat following 280°C LT-RTE aging.

Driven by the worldwide automotive emission regulations, ceramic substrates were developed to serve as catalyst support. Since the introduction of Standard wall substrates in 1974, substrates with thinner walls and higher cell densities have been developed to meet the tighter emission requirements; Worldwide, the amount of Thinwall and Ultrathinwall substrates in series applications is increasing continuously. The properties of the substrates determine their performance regarding pressure drop, heat-up and conversion efficiency. These properties are analyzed, as well as the packaging process for Thinwall and Ultrathinwall substrates; A new packaging technique with lower pressure load is described.