Search Results

The design of a canned ceramic oval converter, 77mm by 146.8mm, is described along with subsequent demonstration of its high temperature (1050°C) durability. A new mat deterioration phenomenon was recognized, and will be described. The mat deterioration results from sintering of the vermiculite and glass fiber structure when exposed to temperatures greater than approximately 1000°C. Due to the extremely high temperature experienced in the supporting mat of an oval converter exposed to 1050°C, an alternative mat configuration was utilized to eliminate potential mat sintering. An inner layer of non-intumescent mat (1500g/m2) was used in conjunction with an outer layer of intumescent mat (3100g/m2). The inner mat provided sufficient thermal protection to the outer intumescent mat, maintaining considerable holding pressure on the ceramic substrate. A tourniquet closure technique was developed to uniformly compress a hybrid mat system around the entire perimeter of the oval converter.

Stringent emissions standards with 95+% conversion efficiency requirements call for advanced ceramic catalyst supports with thinner walls, higher cell density and optimum cell shape. The extrusion technology for cellular ceramics has also made significant progress which permits the manufacture of advanced catalyst supports. Similarly, modifications in cordierite chemistry and the manufacturing process have led to improved microstructure from coatability and thermal shock points of view. The design of these supports, however, requires a systems approach to balance both the performance and durability requirements. Indeed as the wall gets thinner, the contribution of washcoat becomes more significant in terms of thermal mass, heat transfer, thermal expansion, hydraulic diameter and structural stiffness - all of which have an impact on performance and durability. For example, the thinner the wall is, the better the light-off performance will be.

This paper provides elastic analysis of compressive stresses in the matrix and skin regions of automotive substrates during 3D- and 2D-isostatic strength testing. The matrix region is treated as transversely isotropic material and the skin region as isotropic material, each with their independent elastic properties. Such a solution helps quantify load sharing by the matrix and skin regions which, in turn, affect compressive stresses in each region. The analysis shows that the tangential compressive stresses in the skin and matrix differ significantly at the interface due to high stiffness ratio of skin versus matrix. The resulting strain in the skin is more severe for thin and ultrathin wall substrates and may lead to localized bending of interfacial cells thereby inducing premature failure. Methods to reduce compressive strain in both the matrix and skin without affecting performance-related advantages are discussed.

The present work intends to examine the selective NOx reduction efficiency of a current commercial Titanium-Vanadium washcoated catalyst and to develop a transient numerical model capable of describing the SCR process while using a wide range of inlet conditions such as space velocity, oxygen concentrations, water concentration and NO2/NO ratio. The concentrations of different components (NO, NO2, N2O, NH3, H2O and HNO3) were analyzed continuously by a FT-IR spectrometer. A temperature range from 150°C up to 650°C was examined and tests were carried out using a model exhaust gas comparable to the real diesel exhaust gas composition. There is a very good correlation between experimental and calculated results with the given chemical kinetics.