The ability to evaluate the bending fatigue behavior of carburized low alloy steels in a laboratory and relate these measurements to performance of high contact ratio helical gears is important to the design and development of transmissions. Typical methods of evaluating bending fatigue performance of carburized gear steels do not directly represent helical planetary gears because they lack the geometric and loading conditions of planetary pinions. The purpose of this study is twofold; 1) development of a lab fatigue test to represent the fatigue performance of planetary pinion gears tested in a dynamometer and 2) evaluation of the influence of alloy content on bending fatigue performance of two steel alloys. The steels under evaluation were modified 8620M and 4615M alloys machined into bend bars with a notch representing a gear root and carburized to a case depth of approximately 0.35 mm (using the same carburizing cycle as the planetary pinion gears).

Systems of alloys for liquid phase alloying during sintering were investigated. The solidification range of alloys of Mn-Ni-Cr-Mo-Fe and Mn-Cu-Ni was determined. Alloys with the lowest and narrowest melting range were prepared and atomized in nitrogen. Admixtures of master alloys to water-atomized, forging grade, pure iron powder were sintered at 1232°C (2250°F). After hot forging, these P/M steels exhibited hardenabilities which were 75%-90% of theoretical hardenability, as calculated from the factors for conventional steels. Alloying efficiency was further improved to 85%-100% of theoretical hardenability when additions of approximately 2% silicon and 1% rare earth misch-metal were made to the master alloys. The silicon and rare earth misch-metal additions were used to enhance diffusion and sintering.