The influence of cell geometries on the quasi-static crush behaviors of aluminum honeycombs is explored by experiments. Aluminum 5052-H38 honeycomb specimens with different in-plane orientation angles, cell wall thicknesses and cell sizes were tested under compression dominant combined loads. The load histories of these specimens were obtained. A quadratic and a linear phenomenological yield criteria are used to fit the obtained experimental normal crush and shear strengths for three types of honeycomb specimens under compression dominant combined loads. The quadratic yield criterion is used to fit the experimental results for two types of honeycomb specimens with low relative densities. The linear yield criterion is used to fit the experimental results for one type of honeycomb specimens with a high relative density.

Sandwich specimens with DP590 steel face sheets and structural epoxy foam cores are investigated under three-point bending conditions. Experimental results indicate that the maximum loads correspond to extensive cracking in the foam cores. Finite element simulations of the bending tests are also performed to understand the failure mechanisms of the epoxy foams. In these simulations, the plastic behavior of the steel face sheets is modeled by the Mises yield criterion with consideration of plastic strain hardening. A pressure sensitive yield criterion is used to model the plastic behavior of the epoxy foam cores. The epoxy foams are idealized to follow an elastic perfectly plastic behavior. The simulation results indicate that the load-displacement responses of some sandwich specimens agree with the experimental results.

Failure behavior of spot welds is investigated under impact loading conditions. Three different impact speeds were selected to test both HSLA steel and mild steel specimens under combined opening and shear loading conditions. A test fixture was designed and used to obtain the failure loads of spot weld specimens of different thicknesses under a range of combined opening and shear loads with different impact speeds. Accelerometers were installed on the fixtures and the specimens for investigation of the inertia effects. Optical micrographs of the cross sections of failed spot welds were obtained to understand the failure processes in both HSLA steel and mild steel specimens under different combined impact loads. The experimental results indicate that the failure mechanisms of spot welds are very similar for both HSLA steel and mild steel specimens with the same sheet thickness. These micrographs show that the sheet thickness can affect the failure mechanisms.