The prediction of residual stresses due to manufacturing is of high importance in product development. For the accurate prediction of residual stresses in metallic components, an understanding of the quenching process that occurs in many heat treatments is required. In this paper, the experimental techniques developed to quantify the temperature fields during quenching and to quantify the residual stresses in the quenched part are presented. The temperature fields were quantified using thermocouples embedded in the components. The residual stresses were quantified using a newly developed strain gauging, sectioning and dynamic data acquisition technique. The techniques were verified using thermal histories and residual stresses for an engine cylinder head quenched at two different quenchant temperatures. The measurements obtained were incorporated into an analytical program (finite element) to study the residual stresses produced during the quenching process.

In the current work, unidirectional (UD) carbon fiber composite hatsection component with two different layups are studied under dynamic three-point bending loading. The experiments are performed at various impact velocities, and the effects of impactor velocity and layup on acceleration histories are compared. A macro model is established with LS-DYNA for a more detailed study. The simulation results show that the delamination plays an important role during dynamic three-point bending test. Based on the analysis with a high-speed camera, the sidewall of hatsection shows significant buckling rather than failure. Without considering the delamination, the current material model cannot capture the post-failure phenomenon correctly. The sidewall delamination is modeled by assumption of larger failure strain together with slim parameters, and the simulation results of different impact velocities and layups match the experimental results reasonably well.

Weld lines occur when melt flow fronts meet during the injection molding of plastic parts. It is important to investigate the weld line because the weld line area can induce potential failure of structural application. In this paper, a weld line factor (W-L factor) was adopted to describe the strength reduction to the ultimate strength due to the appearance of weld line. There were two engineering thermoplastics involved in this study, including one neat PP and one of talc filled PP plastics. The experimental design was used to investigate four main injection molding parameters (melt temperature, mold temperature, injection speed and packing pressure). Both the tensile bar samples with/without weld lines were molded at each process settings. The sample strength was obtained by the tensile tests under two levels of testing speed (5mm/min and 200mm/min) and testing temperatures (room temperature and -30°C). The results showed that different materials had various values of W-L factor.