Scuffing is one of the major problems that influence the life cycle and reliability of several auto components, including engine cylinder kits, flywheels, camshafts, crankshafts, and gears. Ferrous casting materials, such as gray cast iron, ductile cast iron and austempered ductile cast iron (ADI) are widely applied in these components due to their self-lubricating characteristics. The purpose of this research is to determine the scuffing behavior of these three types of cast iron materials and compare them with 1050 steel. Rotational ball-on-disc tests were conducted with white mineral oil as the lubricant under variable sliding speeds and loads. The results indicate that the scuffing initiation is due to either crack propagation or plastic deformation. It is found that ADI exhibits the highest scuffing resistance among these materials.

Scuffing is a failure mechanism which can occur in various engineering components, such as engine cylinder kits, gears and cam/followers. In this research, the scuffing behavior of 4140 steel and ductile iron was investigated and compared through ball-on-disk scuffing tests. A step load of 22.2 N every two minutes was applied with a light mineral oil as lubricant to determine the scuffing load. Both materials were heat treated to various hardness and tests were conducted to compare the scuffing behavior of the materials when the tempered hardness of each material was the same. Ductile iron was found to have a consistently high scuffing resistance before tempering and at tempering temperatures lower than 427°C (HRC ≻45). Above 427°C the scuffing resistance decreases. 4140 steel was found to have low scuffing resistance at low tempering temperatures, but as the tempering temperature increases, the scuffing resistance increased.