In automotive body manufacturing the dies for blanking/trimming/piercing are under most severe loading condition involving high contact stress at high impact loading and large number of cycles. With continuous increase in sheet metal strength, the trim die service life becomes a great concern for industries. In this study, competing trim die manufacturing routes were compared, including die raw materials produced by hot-working (wrought) vs. casting, edge-welding (as repaired condition) vs. bulk base metals (representing new tools), and the heat treatment method by induction hardening vs. furnace through-heating. CaldieTM, a Uddeholm trademarked grade was used as trim die material. The mechanical tests are performed using a WSU developed trimming simulator, with fatigue loading applied at cubic die specimen’s cutting edges through a tungsten carbide rod to accelerate the trim edge damage. The tests are periodically interrupted at specified cycles for measurement of die edge damage.

Hat-sections, single and double, made of steel are frequently encountered in automotive body structural components. These components play a significant role in terms of impact energy absorption during vehicle crashes thereby protecting occupants of vehicles from severe injury. However, with the need for higher fuel economy and for compliance to stringent emission norms, auto manufacturers are looking for means to continually reduce vehicle body weight either by employing lighter materials like aluminum and fiber-reinforced plastics, or by using higher strength steel with reduced gages, or by combinations of these approaches. Unlike steel hat-sections which have been extensively reported in published literature, the axial crushing behavior of hat-sections made of fiber-reinforced composites may not have been adequately probed.

A unified approach has been developed and applied to solder joint life prediction in this paper, which indicates a breakthrough for solder joint reliability simulation. It includes the material characterization of solder alloys, the testing of solder joint specimens, a unified viscoplastic constitutive framework with damage evolution, numerical algorithm development and implementation, and experimental validation. The emphasis of this report focuses on the algorithm development and experimental verification of proposed viscoplasticity with damage evolution.

Natural fiber-reinforced composites are currently gaining increasing attention as potential substitutes to pervasive synthetic fiber-reinforced composites, particularly glass fiber-reinforced plastics (GFRP). The advantages of the former category of composites include (a) being conducive to occupational health and safety during fabrication of parts as well as handling as compared to GFRP, (b) economy especially when compared to carbon fiber-reinforced composites (CFRC), (c) biodegradability of fibers, and (d) aesthetic appeal. Jute fibers are especially relevant in this context as jute fabric has a consistent supply base with reliable mechanical properties. Recent studies have shown that components such as tubes and plates made of jute-polyester (JP) composites can have competitive performance under impact loading when compared with similar GFRP-based structures.

An attractive strategy for joining metallic as well as non-metallic substrates through adhesive bonding. This technique of joining also offers the functionality for joining dissimilar materials. However, doubts are often expressed on the ability of such joints to perform on par with other mechanical fastening methodologies such as welding, riveting, etc. In the current study, adhesively-bonded single lap shear (SLS), double lap shear (DLS) and T-peel joints are studied initially under quasi-static loading using substrates made of a grade of mild steel and an epoxy-based adhesive of a renowned make (Huntsman). Additionally, single lap shear joints comprised of a single spot weld are tested under quasi-static loading. The shear strengths of adhesively-bonded SLS joints and spot-welded SLS joints are found to be similar. An important consideration in the deployment of adhesively bonded joints in automotive body structures would be the performance of such joints under impact loading.

Recent experimental studies on the behavior of adhesively-bonded steel double-hat section components under axial impact loading have produced encouraging results in terms of load-displacement response and energy absorption when compared to traditional spot-welded hat- sections. However, it appears that extremely limited study has been carried out on the behavior of such components under transverse impact loading keeping in mind applications such as automotive body structures subject to lateral/side impact. In the present work, lateral impact studies have been carried out in a drop-weight test set-up on adhesively-bonded steel double-hat section components and the performance of such components has been compared against their conventional spot-welded and hybrid counterparts. It is clarified that hybrid components in the present context refer to adhesively-bonded hat-sections with a few spot welds only aimed at preventing catastrophic flange separations.

This paper introduces a new method to assist deep drawing of tailor-welded blanks with combined restraining force control and binder temperature control. The effect of variable flange temperature and blank holding force on the formability and weld-line displacement of aluminum tailor-welded blank was studied through Finite Element Analysis using LS-DYNA PC.

The Isodamp damping material (also known as Navy Damp) used in the ribs of current crash test dummies provides human-like damping to the thorax under impact. However, the range of temperature over which it can be used is very small. A new rib design using laminates of steel, fiberglass, and commercially available viscoelastic material has been constructed. Load-deflection response and hysteresis of the laminated ribs were compared with corresponding conventional ribs fabricated from steel and Isodamp. Impact tests were conducted on laminated and conventional ribs at 18.5° C, 22.2° C and 26.6° C. Results indicate that the response of the laminated ribs is essentially the same as that of the ribs with Isodamp at 22.2° C, which is the operating temperature of the conventional ribs. The variation in the impact response of the newly developed laminated ribs in the temperature range of 18.5° C to 26.6° C was less than 10%.

Additive manufacturing (AM) of metals is finding numerous applications in automotive industry. In 21st century, aluminum is second to steel in automotive sector, because of its high strength to weight ratio. Hence developing AM for aluminum alloys become necessary to make sure industry gains maximum benefit from AM. This study specifically deals with the manufacturing of Al 7050 alloy, which is quite hardest alloy to manufacture using AM. The ultimate goal is to optimize the laser deposition parameters to deposit defect free Al 7050 alloy on rolled aluminum alloy substrate. Parameter optimization (laser power, powder flow rate, and scanning speed) gets difficult with the presence of various low melting and boiling point alloying elements such as Zn, Mg etc. Numerous other challenges faced while depositing Al 7050 alloy, are also briefly discussed in this article. Microstructural investigation using optical and scanning electron microscopy confirms greater than 99% component density.

There has been a keen interest in recent times on implementation of lightweight materials in vehicles to bring down the unladen weight of a vehicle for enhancing fuel efficiency. Fiber-reinforced composites comprise a class of such materials. As sustainability is also a preoccupation of current product development engineers including vehicle designers, bio-composites based on natural fibers are receiving a special attention. Keeping these motivations of lower effective density, environment friendliness and occupational safety in mind, woven jute fabric based composites have been recently studied as potential alternatives to glass fiber composites for structural applications in automobiles. In the past, mechanical characterization of jute-polyester composites were restricted to obtaining their stress-strain behaviors under quasi-static conditions.

Enhanced protection against high speed crashes requires more aggressive passive safety countermeasures as compared to what are provided in vehicle structures today. Apart from such collision-related scenarios, high energy explosions, accidentally caused or otherwise, require superior energy-absorbing capability of vehicle body subsystems. A case in point is a passenger vehicle subjected to an underbody blast emanating shock wave energy of military standards. In the current study, assessment of the behavior of a “hollow” countermeasure in the form of a depressed steel false floor panel attached with spot-welds along flanges to a typical predominantly flat floor panel of a car is initially carried out with an explicit LS-DYNA solver. This is followed up with the evaluation of PU (polyurethane) foam-filled and liquid-filled false floor countermeasures. In all cases, a charge is detonated under the false floor subjecting it to a high-energy shock pressure loading.

The short NiTi fiber-reinforced NiTi/Al6061-SiC composite was recently developed through the U.S. Army SBIR Phase-II program [1]. The objectives of this project are to use short NiTi fiber reinforcement to induce compressive stress through shape memory effect, to use silicon carbide (SiC) particulate reinforcement to enhance the mechanical properties of the aluminum matrix, to gain fundamental knowledge of short NiTi fiber-reinforced aluminum matrix composite, and eventually to improve fatigue resistance, impact damage tolerance and fracture toughness of the composite. The fatigue life, damage and fracture behavior of TiNi/Al6061-SiC, TiNi/Al6061, Al6061-SiC composites as well as monolithic Al6061 alloy were investigated under fully reversed cyclic loading. It was found that fatigue life of NiTi/Al6061-SiC composite, in term of the cycles, increased by two orders of magnitude, compared to monolithic Al6061 alloy

A series of rear impact tests of varying severity was performed using a mini pick-up truck with an instrumented Hybrid III dummy at the driver position. Head, neck and chest loads were monitored. The severities of these loads from an injury standpoint were assessed using biomechanically based reference criteria that are particularly suitable for the Hybrid III. The glass Installation performed well as a head restraint. Glass fracture from head impact was achieved only when the glass was predamaged, with surface scratches on the outer (tensile) side. The amazing strength and flexibility of tempered glass and the dramatic reduction in strength caused by small surface scratches are demonstrated.

Adhesively bonded steel hat section components have been experimentally studied in the past as a potential alternative to traditional hat section components with spot-welded flanges. One of the concerns with such components has been their performance under axial impact loading as adhesive is far more brittle as compared to a spot weld. However, recent drop-weight impact tests have shown that the energy absorption capabilities of adhesively bonded steel hat sections are competitive with respect to geometrically similar spot-welded specimens. Although flange separation may take place in the case of a specimen employing a rubber toughened epoxy adhesive, the failure would have taken place post progressive buckling and absorption of impact energy.

Children riding on the bed over the cab in campers can be injured in forward force collisions from striking the glazing material and/or being ejected through the opening. The two types of glazing commonly used are acrylic and laminated. A comparison of the performance of the two types of glazing in simulated forward force collisions at velocities up to 30 mph showed the acrylic material to pose threats of neck and back injury and the laminated material to result in lacerations. Ejections occurred with the acrylic that were not present with the laminated windshields when correct glazing techniques were used. With poor installation procedures, ejections occurred in both types of glazing materials. It is concluded that the best way to avoid injury is to prevent the child from riding in the over-the-cab bunk. If the child does ride there, his body axis should be positioned at an angle to the longitudinal axis of the vehicle.

Conventional 30 mil HPR laminated and wide-zone monolithic tempered windshields are compared on a safety performance basis from the stand-points of occupant injuries from frontal force collisions and injury or loss of control from breakage from high speed external impact of stones. All experiments were conducted with the windshields installed by conventional methods in an automobile. Occupant injury potential as measured by the Severity Index for brain damage at a 30 mph barrier impact simulation was approximately two times as high for the tempered as for the laminated windshields, although only one tempered windshield exceeded the recommended maximum value of 1,000. Severe lacerations resulted in all impacts in which the tempered glass broke. Less severe lacerations were found for the laminated windshield impacts at comparable speeds.

An improved windshield with a special, thin, plastic inner surface attached to the inner surface of a three layer windshield similar to those used in the United States minimizes lacerations from occupant impact to the windshield during a collision. The plastic coats the sharp edges of the broken glass preventing or minimizing laceration. It was evaluated by comparing its laceration performance with that of a standard windshield in simulated barrier crashes at velocities up to 65 km/h. No lacerations resulted from impact to the Securiflex windshield at Barrier Equivalent Velocities up to 65 km/h. Substantial laceration resulted at velocities above 20 km/h with the standard windshield. It is concluded that the Securiflex windshield essentially eliminates lacerations in the particular vehicle involved at velocities up to at least 65 km/h.

Safety performance of an experimental windshield with a thin, chemically tempered inner pane is compared with the standard windshield and other experimental windshields. The chemically tempered windshield has a penetration velocity of 35 mph compared with 26 mph penetration velocity for the standard windshield and has lower peak head accelerations than other types used in the experiments. The windshield tested produces a bulge on impact, which decelerates the head over a long distance with low accelerations. The bulge or pocket is lined with particles that are less lacerative than the standard annealed glass.

A composite of an aluminum matrix reinforced by short TiNi shape memory alloy (SMA) fibers was fabricated. The processing and thermomechanical behaviors of the composite TiNi/Al6061 were investigated experimentally and analytically. Optimal hot-pressing conditions of TiNi/Al6061 processing were identified. The shape memory effect (SME) was activated by prestraining the composite at the temperature between Ms and As, followed by heating up to Af. SME on mechanical properties, such as microhardness, yield stresses of the composite, were investigated. A computational model for the strengthening mechanism of the short fiber metal matrix composite was utilized to analyze SME on yield stress of the composite. Yield stress of the composite as a function of prestrain was predicted numerically and verified experimentally.