Establishing a certain maintenance-free time period regarding modern diesel exhaust emission control systems is of major importance nowadays. One of the most serious problems Diesel Particulate Filter (DPF) manufacturers face concerning system's durability is the performance deterioration due to the filter aging because of the accumulation of the ash particles. The evaluation of the effect of the ash aging on the filter performance is a time and cost consuming task that slows down the process of manufacturing innovative filter structures and designs. In this work we present a methodology for producing filter samples aged by accumulating ash produced by the controlled pyrolysis of oil-fuel solutions. Such ash particles bear morphological (size) and compositional similarity to ash particles collected from engine aged DPFs. The ash particles obtained are compared to those from real engine operation.

Although engine emissions per vehicle have been reduced for twenty years with technical developments in the fields of engine, after-treatment technologies and fuels the urban air pollution problem still exists in many cities around the world. Forthcoming emission regulations will require further development of new complex technologies to reach low emissions. On-board driving assessment of such technologies offers significant advantages in the development phase of novel emission reduction. In this paper we present the design, development and commissioning of a mobile laboratory able to monitor on-board along the exhaust line gaseous and particulate pollutants as well as measure these pollutants in the ambient environment around the vehicle.

In this paper a fast DPF screening procedure is proposed using small-scale filter samples of different technologies in a well-controlled environment but under realistic engine exhaust conditions. The DPF samples are evaluated in a specially built Multi-Reactor Assembly (MRA) with respect to their flow resistance, filtration efficiency, soot loading behavior, soot oxidation behavior, as well as their ash induced ageing behavior.

The objective of this study is the design, construction and evaluation of a Selective Particle Size (SPS) sampler able to provide continuous delivery of diesel soot particles of specific size ranges. The design of the sampler combines principles of aerosol transport phenomena and separation technologies. Particles smaller than a given size are removed from the exhaust by diffusional deposition, while removal of particles above a given size is achieved by low pressure inertial impaction. The main application of the developed sampler is the exposure of biological samples such as cell and tissue cultures to selected sizes of diesel exhaust particles. By applying the SPS sampler to diesel exhaust it is demonstrated that it is possible to obtain two aerosol streams with widely separated particle size distributions (of nanometric dimensions), suitable for biological exposure studies.

Novel catalytic coatings with a variety of methods based on conventional and novel synthesis routes are developed for Diesel Particulate Filters (DPFs). The developed catalytic composition exhibits significant direct soot oxidation as evaluated by reacting mixtures of diesel soot and catalyst powders in a thermogravimetric analysis apparatus (TGA). The catalyst composition was further deposited on oxide and non-oxide porous filter structures that were evaluated on an engine bench with respect to their filtration efficiency, pressure drop behavior and direct soot oxidation activity under realistic conditions. The effect of the catalyst amount on the filtration efficiency of non-oxide filters was also investigated. Evaluation of the indirect soot oxidation was conducted on non-oxide catalytic filters coated with precious metal.

A new platform of advanced ceramic composite filter materials for diesel particulate matter and exhaust gas emission control has been developed. These materials exhibit high porosity, narrow pore-size distribution, robust thermo-mechanical strength, and are extruded into high cell density honeycomb structures for wall-flow filter applications. These new high porosity filters provide a structured filtration surface area and a highly connected wall pore space which is fully accessible for multi-phase catalytic reactions. The cross-linked microstructure (CLM™) pore architecture provides a large surface area to host high washcoat/catalyst loadings, such as those required for advanced multi-functional catalysts (4-way converter applications).

Asymmetric and Variable Cell (AVC) geometry Diesel Particulate Filters (DPF) occupy an increasing portion of the DPFs currently offered by various DPF manufacturers, aiming at providing higher filtration area in the same filter volume to meet demanding emission control applications for passenger cars but also for heavy duty vehicles. In the present work we present an approach for designing and optimizing such DPFs by providing a quantitative description of the flow and deposition of soot in these structures. Soot deposit growth dynamics in AVC DPFs is studied computationally, primary and secondary flows over the inlet channels cross-sectional perimeters are analyzed and their interactions are elucidated. The result is a rational description of the observed growth of soot deposits, as the flow readjusts to transport the soot particles along the path of least resistance (which is not necessarily the shortest geometric path between the inlet and outlet channel, i.e. the wall thickness).

The life of DPF would be decided by ash durability because pressure loss of DPF is increased by accumulation of ash that is produced when soot is burnt in the DPF. We could succeed to increase maximum ash capacity and extend the life of the DPF by an approach from the filter design, making inlet cell volume larger than outlet cell. Furthermore, when the inlet cell is designed octagon, we found that slanted wall blocking the inlet cells is functional worked for soot filtration. As the results, we could improve to manage both transient pressure loss while the soot is collected and the ash durability by the cell shape with (inlet cell/outlet cell) = (octagon/square).

Diesel Particulate Filters (DPFs) need to be periodically regenerated in order to achieve efficient and safe vehicle operation. Under typical diesel exhaust conditions, this invariably requires the raising of the exhaust gas temperature by active means, up to the point that particulate (soot) oxidation can be self-sustained in the filter. In the present work the development path of an advanced catalytic filter technology is presented. Full scale optimized Catalytic Diesel Particulate Filters (CDPFs) are tested in the exhaust of a light-duty modern diesel engine in line with a Diesel Oxidation Catalyst (DOC). The management of the DOC-CDPF emission control system is facilitated by a virtual soot sensor in order to ensure energy-efficient operation of the emission control system.

The increasing need for controlled diesel engine emissions and the strict regulations in the abatement of diesel exhaust products lead to an ever increasing use of Diesel Particulate Filters (DPFs) in OEM applications. The periodic regeneration of DPFs (oxidation of soot particles) demands temperatures that rarely appear during engine operation. It is therefore necessary to employ direct or indirect catalytic measures. In the present work, the development and synthesis via aerosol-based routes, of nanostructured base metal oxides for direct soot oxidation, along with their characterization and their evaluation in engine exhaust is described. The synthesized powders were characterized with respect to their phase composition and morphology. XRD, SEM and TEM analysis have shown the nanostructured character of the powders, while Raman spectroscopy was employed for the preliminary characterization of the materials surface chemistry.

Catalysts that have been extensively investigated for direct soot oxidation in Catalyzed Diesel Particulate Filters (CDPFs) are very often based on mixed oxides of ceria with zirconia, materials known to assist soot oxidation by providing oxygen to the soot through an oxidation-reduction catalytic cycle. Besides the catalyst composition that significantly affects soot oxidation, other parameters such as morphological characteristics of the catalyst largely determined by the synthesis technique followed, as well as the reagents used in the synthesis may also contribute to the activity of the catalysts. In the present work, two ceria-zirconia catalyst samples with different zirconia content were subjected to different milling protocols with the aim to shift the catalyst particle size distribution to lower values. The produced catalysts were then evaluated with respect to their soot oxidation activity following established protocols from previous works.

The pore diameter and porosity of SiC-DPF has been increased by elaborating its porous structure. Increasing the porosity of DPF decreases its strength and thermal conductivity. It was clarified how these characteristics affect the performance such as filtration characteristics, low pressure loss, maximum soot loading limit, and thermal response characteristics required for DPF. It was found that the basic characteristics of SiC such as high strength and high thermal conductivity play an important role in its high porosity.

In Europe, where diesel engine cars enjoy widely popularity, the major diesel-engine car manufacturers have already announced that they will equip their diesel engine vehicles with DPF systems. Silicon carbide(SiC) has good fundamental properties. And the crack problem during regeneration could be successfully controlled by using split-type DPF which consists of multiple filter segments. The functional characteristics were focused on. For DPF, a model test by which events that may actually occur on vehicles can be produced is said to have not yet been established. From this point of view, in this study, SiC-DPF functions are characterized and evaluated under a regeneration system, and their correlation is discussed.

We examined a filter structure of a SiC-DPF, and found that the reduction in a wall thickness is effective in decreasing a pressure loss. And we made it clear how this reduction in the wall thickness influences the performances of the DPF, that are the filtration efficiency and the accumulated soot mass limit which are important for the DPF. From the results of this study, it can be seen that the filter structure which is suitable for the catalyzed DPF should be controlled in a porosity and the wall thickness in proportion to an amount of catalyst required.

In the present work we derive analytical solutions for the problem of convection, diffusion and chemical reaction in wall-flow monoliths. The advantage of having analytical instead of numerical treatments is clear as the analytical solutions not only can be exploited to bring full scale simulations of diesel particulate filters to the real time domain, but also they enable efficient implementations on computationally limited engine control units (ECUs) for on-board management and control of emission control systems. The presentation describes the mathematical problem formulation, the governing dimensionless parameters and the corresponding assumptions. Then the analytical solution is derived and several asymptotic (for limiting values of the parameters) and approximating solutions are developed, corresponding to different physical situations. Reactant distributions in the filter are presented and discussed for several values of the parameters.

Diesel emission regulation becomes stringent more and more regarding both particulate matter (PM) and NOx in the worldwide. SCR coated DPF system is considered as one of the promising options for future diesel exhaust after-treatment because it has several benefits such as the downsizing of the system, quick light-off of the catalytic function due to mounting closed-couple position. To integrate the SCR converter into the DPF, it is necessary to design the DPF substrate's porosity higher and pore size larger than conventional DPF to improve SCR catalyst coating capability. However to make the porosity higher will lose the robustness in general. Against these problems, it was studied to improve the high porosity DPF performances by applying the new technology to modify the thermal shock resistance property.

This paper describes the durability of the filtration layer integrated into Diesel Particulate Filters (DPFs) that we have developed to ensure low pressure loss and high filtration efficiency performances which also meet emission regulations. DPF samples were evaluated in regards to their performance deterioration which is brought about by ash loading and uncontrolled regeneration cycles, respectively. Ash was synthesized by using a diesel fuel/lubrication oil mixture and was trapped up to a level which corresponded to a 240,000km run, into the DPFs both with and without the filtration layer. Afterwards, aged-DPFs were measured with respect to their permeability, pressure loss, filtration efficiency, as well as soot oxidation speed using suitable analytical methods. Consequently, it has been confirmed that there was no noteworthy deterioration of the performances in the DPF with the filtration layer.

One technology for removing PM discharged from diesel-powered vehicles is the DPF system. The DPF system brings about increases in pressure loss because PM accumulates in the filter. DPF with a high cell density shows low pressure loss when PM accumulates because of the large filtration area, and in addition, it makes it possible to thin the cell wall because it has a high thermal diffusion ability. For the catalyzation of SiC, the pore size and porosity of the base material were changed. Even when a catalyst is borne, pressure loss which DPF changed pore structure hardly changes. This verification was done based on the theory and by means of experimentation.

Exhaust Gas Recirculation (EGR) is an effective method to reduce Nitrogen Oxide emissions. In recent years the trend of increasing EGR rate in-cylinders is an integral part of most improvements in combustion technology developments. The object of this work is to study the influence of EGR rate on the physical and chemical properties of soot particles. Soot from several operating points of a diesel engine run were collected on a high temperature filters. The pressure drop behavior during the soot loading was monitored then the soot permeability was calculated. Afterwards, the soot primary size was calculated from the obtained data and it showed good correspondence to the actual measurement. It is confirmed that all the soot primary sizes were around 22 nm in diameter. In contrast, the soot aggregate sizes and the soot concentrations were found to increase with increasing EGR rate. Subsequently, Oxidation tests were conducted to evaluate the reactivity of the soot.

In this paper, a methodology is presented to study the influence of thermal aging on catalytic DPF performance using small scale coated filter samples and side-stream reactor technology. Different mixed oxide catalytic coating families are examined under realistic engine exhaust conditions and under fresh and thermally aged state. This methodology involves the determination of filter physical (flow resistance under clean and soot loaded conditions and filtration efficiency) and chemical properties (reactivity of catalytic coating towards direct soot oxidation). Thermal aging led to sintering of catalytic nanoparticles and to changes in the structure of the catalytic layer affecting negatively the filter wall permeability, the clean filtration efficiency and the pressure drop behavior during soot loading. It also affected negatively the catalytic soot oxidation activity of the catalyzed samples.