This specification covers molded or extruded bar, rod, and shapes produced from a polyamide-imide (PAI) polymer filled with 12% graphite and 3% polytetrafluoroethylene (PTFE). This is designated as Grade 3 material per AMS3670.
This specification covers molded or extruded bar, rod, and shapes produced from a polyamide-imide (PAI) polymer filled with 30% glass fiber. This is designated as Grade 4 material per AMS3670.
This specification covers molded or extruded bar, rod, and shapes produced from a polyamide-imide polymer filled with 30% carbon fiber. This is designated as Grade 5 material per AMS3670.
This specification covers an unfilled polyamide-imide plastic in the form of molded or extruded bar, rod, and shapes. This is designated as Grade 2 material per AMS3670.
This SAE Aerospace Standard (AS) covers batch qualification procedure for virgin and compounded polytetrafluoroethylene (PTFE) resins used for compression molding. AS9100 requires virgin and modified PTFE as a testing material be representative of production PTFE and/or parts. The testing specified herein is limited to tensile strength, elongation and specific gravity. Any other tests required by the purchaser must be specified separately.
This SAE Aerospace Standard (AS) covers batch qualification procedure for virgin and compounded polytetrafluoroethylene (PTFE) resins used for compression molding. AS9100 requires virgin and modified PTFE as a testing material be representative of production PTFE and/or parts. The testing specified herein is limited to tensile strength, elongation and specific gravity. Any other tests required by the purchaser must be specified separately.
This specification covers one type of glass cloth impregnated with a heat-reactive, addition-cure, thermosetting, polyimide-resin system, the resin to be supplied in a "B" stage condition for high flow and press cure at 40 - 100 psi (276 - 690 kPa) or vacuum/autoclave processing.
This specification covers one type of glass cloth impregnated with a heat-reactive, addition-cure, thermosetting, polyimide-resin system, the resin to be supplied in a "B" stage condition for high flow and press cure at 40 - 100 psi (275 - 690 kPa) or vacuum/autoclave processing.