Search Results

One of the issues in stamping of advanced high strength steels (AHSS) is the stretch bending fracture on a sharp radius (commonly referred to as shear fracture). Shear fracture typically occurs at a strain level below the conventional forming limit curve (FLC). Therefore it is difficult to predict in computer simulations using the FLC as the failure criterion. A modified Mohr-Coulomb (M-C) fracture criterion has been developed to predict shear fracture. The model parameters for several AHSS have been calibrated using various tests including the butter-fly shaped shear test. In this paper, validation simulations are conducted using the modified (M-C) fracture criterion for a dual phase (DP) 780 steel to predict fracture in the stretch forming simulator (SFS) test and the bending under tension (BUT) test. Various deformation fracture modes are analyzed, and the range of usability of the criterion is identified.

Low carbon steels are being replaced by advanced high strength steels (AHSS) due to high demand of the future lighter weight vehicle, while still maintaining good or even better crash performance. However, sidewall curl and springback (section opening) have been found to increase as the strength of the sheet metal increases. Experiments have been conducted on the bending under tension (BUT) test to seek an effective control methodology regarding the applications of the advanced high strength steels (AHSS) in this study. Steels that were studied included a low carbon steel (DQSK), two dual phase steels (DP) and a transformation induced plasticity (TRIP) steel. Two different gauges of each AHSS were also included for a gauge sensitivity study. Different processing variables (four different diameter pins combining with five different back tension forces) were applied to the tests, and the springback angle and sidewall curl were measured for bend and bend-unbend areas of the specimen.

This paper presents an investigation into the behavior of spot-welded steel connections based on a DOE approach. This work is a part of spot-weld modeling methodology development work being performed at Ford. Control factors such as material, coating, gage size, and noise factors such as loading direction (angle), and speed are considered in this study. Different levels of each variable are included to cover a wide range of practical applications. The test methodology used to generate the responses for the spot-weld coupons have been discussed in a companion paper [1]. From the force-displacement curves obtained from the test, the responses such as peak force, displacement at peak force, and rupture displacement are identified. These responses are then statistically analyzed to identify the relative importance and effect of the design factors. Finally, response surface models are developed to determine responses across different levels of each variable.

In the North American automotive industry, various advanced high strength steels (AHSS) are used to lighten vehicle structures, improve safety performance and fuel economy, and reduce harmful emissions. Relatively thick gages of AHSS are commonly joined to conventional high strength steels and/or mild steels using Gas Metal Arc Welding (GMAW) in the current generation body-in-white structures. Additionally, fatigue failures are most likely to occur at joints subjected to a variety of different loadings. It is therefore critical that automotive engineers need to understand the fatigue characteristics of welded joints. The Sheet Steel Fatigue Committee of the Auto/Steel Partnership (A/S-P) completed a comprehensive fatigue study on GMAW joints of both AHSS and conventional sheet steels including: DP590 GA, SAE 1008, HSLA HR 420, DP 600 HR, Boron, DQSK, TRIP 780 GI, and DP780 GI steels.

To improve the energy absorption capacity of front-end structures during a vehicle crash, a novel 12-sided cross-section was developed and tested. Computer-aided engineering (CAE) studies showed superior axial crash performance of the 12-sided component over more conventional cross-sections. When produced from advanced high strength steels (AHSS), the 12-sided cross-section offers opportunities for significant mass-savings for crash energy absorbing components such as front or rear rails and crush tips. In this study, physical crash tests and CAE modeling were conducted on tapered 12-sided samples fabricated from AHSS. The effects of crash trigger holes, different steel grades and bake hardening on crash behavior were examined. Crash sensitivity was also studied by using two different part fabrication methods and two crash test methods. The 12-sided components showed regular folding mode and excellent energy absorption capacity in axial crash tests.

To evaluate vehicle crash performance in the early design stages, a reliable fracture model is needed in crash simulations to predict material fracture initiation and propagation. In this paper, a generalized incremental stress state dependent damage model (GISSMO) in LS-DYNA® was calibrated and validated for a 780-MPa third generation advanced high strength steels (AHSS), namely 780 XG3TM steel that combines high strength and ductility. The fracture locus of the 780 XG3TM steel was experimentally characterized under various stress states including uniaxial tension, shear, plane strain and equi-biaxial stretch conditions. A process to calibrate the parameters in the GISSMO model was developed and successfully applied to the 780 XG3TM steel using the fracture test data for these stress states.

The modeling of plastic fuel tank systems for crash safety applications has been very challenging. The major challenges include the prediction of fuel sloshing in high speed impact conditions, the modeling of multilayer thermoplastic fuel tanks with post-forming (non-uniform) material properties, and the modeling of tank straps with pre-tensions. Extensive studies can be found in the literature to improve the prediction of fuel sloshing. However, little research had been conducted to model the post-forming fuel tank and to address the tension between the fuel tank and the tank straps for crash safety simulations. Hoping to help improve the modeling of fuel systems, the authors made the first attempt to tackle these major challenges all at once in this study by dividing the modeling of the fuel tank into eight stages. An ALE (Arbitrary Lagrangian-Eulerian) method was adopted to simulate the interaction between the fuel and the tank.

Finite element models of cast aluminum and stamped steel lower control arms (LCAs) were created to simulate subsystem tests of LCA with bushings and brackets. Several modeling methods were used to simulate the dynamic responses of cast aluminum LCAs, and the advantages and disadvantages of each method are discussed. Factors that are essential for modeling stamped steel components found in previous studies [1, 2] including strain rate, forming, and welding effects are incorporated in the stamped steel LCA models. Difficulties in modeling LCAs subsystem, possible remedies, and further improvements are also discussed in this paper.

Strain rate effects have been identified as one of the most critical factors for the modeling of vehicle components in many previous investigations. The strain rate data available to the authors have been processed to obtain the input decks of a required material law in prior investigations. With the application of strain rate modeling, the strain rate database needs to be expanded. In order to continuously improve the safety CAE quality and efficiency, especially the prediction of a vehicle's pulse in a crash event, the effort has been made to include more strain rate data and extend the material database for safety CAE applications. In this study, strain rate data provided by Ispat Inland Inc. for AISI/DOE Technology Roadmap Program are processed. The material processed in this study include HSS590-CR, 440W-GA, BH300-GI, HSLA350-GI, DP600-HR, TRIP590-EG, TRIP600-CR, TRIP780-CR.

The dent resistance of an automotive body panel has been used as one of key design parameters for automotive body panels. Quasi-static dent testing procedures have been well documented in North America using A/SP Standard Dent Resistance Test Procedures and numerous publications in static denting are also available. However, test procedures under dynamic denting are not very well documented and limited data exist on dynamic denting performance of automotive body panels. In this paper, dynamic dent tests are carried out using different impact velocities and different test procedures. The advantages and disadvantages of test procedures are discussed. Different ways to characterize the dynamic dent test results are investigated and discussed. Due to higher impact velocity during the dynamic dent testing, the acceleration effect must be considered in the data analysis. Experiments were carried out on a hydraulic controlled dynamic dent tester.

The conventional forming limit curve (FLC) has been widely and successfully used as a failure criterion to detect localized necking in stamping. However, in stamping advanced high strength steels (AHSS), under certain circumstances such as stretching-bending over a small die radius, the sheet metal fails much earlier than predicted by the FLC. This type of failure on the die radius is commonly called “shear fracture.” In this paper, the laboratory Stretch-Forming Simulator (SFS) and the Bending under Tension (BUT) tester are used to study shear fracture occurring during both early and later stages of stamping. Results demonstrate that the occurrence of shear fracture depends on the combination of the radius-to-thickness (R/T) ratio and the tension/stretch level applied to the sheet during stretching or drawing. Based on numerous experimental results, an empirical shear fracture limit curve or criterion is obtained.

Forming Limit Diagrams (FLD) have been widely and successfully used in sheet metal stamping as a failure criterion to detect localized necking, which is the most common failure mechanism for conventional steels during forming. However, recent experience from stamping Dual-Phase steels found that, under certain circumstances such as stretching-bend over a small die radius, the sheet metal fails earlier than that predicted by the FLD based on the initiation of a localized neck. It appears that a different failure mechanism and mode are in effect, commonly referred to as “shear fracture” in the sheet metal stamping community. In this paper, experimental and numerical analysis is used to investigate the shear fracture mechanism. Numerical models are established for a stretch-bend test on DP780 steel with a wide range of bend radii for various failure modes. The occurrences of shear fracture are identified by correlating numerical simulation results with test data.

In this study fatigue tests of GMAW (Gas Metal Arc Welding) welded joints were conducted on both 1.6mm body sheet (DQSK-GA, DP590-GA, DP780-GI, and TRIP 780-GI) and 3.4mm frame materials (SAE1008 HR 240MPa, HSLA420 HR, DP600 HR, and uncoated Boron). Further, mixed thickness joints were tested which combined 3.4mm SAE1008 HR with each of the 1.6mm separately – with the exception of DQSK. A number of different joint configurations were tested including single and double lap-shear, start-stop lap shear, butt weld, and perch mount. Great care was taken in this study to ensure that the geometry of the welds was consistent, not only within a given material lay-up, but between all of the specimens of a given type – this effort was made in order to substantially reduce life scatter and provide a better understanding of the role base material plays in the fatigue life of GMAW joints.

This study is a systematic investigation of the body mounts' dynamic characteristics in component, sub-system and full system levels and its application in the frontal impact analysis of a body-on-frame (BOF) vehicle. Concluded from the component study, the body mount is modeled by non-linear spring with built-in damage and rupture properties. The sub-system study reveals the importance of modeling the interaction between the body mount and its surrounding structure. A general-purpose interaction modeling is developed to provide a realistic CAE simulation of this interaction behavior. The full system is mainly for methodology validation. Four 90-degree frontal and the one IIHS offset frontal crash tests are used to evaluate the performance of the body mount in low and high speeds and its capability of predicting the body mount and the floor pan failures.

The frontal rail is one of the most important components of a vehicle in determining crash performance, especially for a body on frame vehicle. Prior research [1] has shown that the frontal rail absorbs a significant amount of impact energy in a crash condition. In order to optimize crash performance, a component level sensitivity study was conducted to determine the effect different types of triggers would have on the performance of the frontal rail. The objective of this study is to determine the sensitivity of trigger size, trigger shape, and trigger orientation as well as to improve corresponding trigger modeling methodology by comparing crushed components to crushed CAE models. In this sensitivity study, the location of the triggers was held fixed, while the size, shape, and orientation were varied. The metric that will be used to compare the performance of these different trigger shapes is the overall stiffness of the frontal rail.

Edge fracture of advanced high strength steels (AHSS) can occur in both the stamping process and the crash event. Fracture due to poor sheared edge conditions in the stamping process was reduced with a recently developed optimal shearing process for AHSS. Currently, the improvement in the energy absorption due to the improved edge condition during crashes performed under different loading conditions had not been closely verified. The purpose of this study is to design and build a miniature component of AHSS and a three-point bending test for investigating the influence of various conditions of the sheared edge on the energy absorption in crashes. AHSS including DP600, TRIP780, DP980 and DP1180 were selected in the study. A small channel component was developed and fabricated using DP980 to simulate key features of the B-pillar. The exposed non-constrained, as-sheared edge was subject to stretch bending forces in three-dimensional space during the three-point bending test.

Practical evaluation and reduction of edge cracking are two challenging issues in stamping AHSS for automotive body structures. In this paper, the effects of the shear clearance and shear rake angle on edge cracking were investigated with three different grades of AHSS; TRIP780, DP 980, and DP 1180. Five different shear clearances, between 5% and 25% of material thickness, were applied to the flexible shearing machine to generate samples for the half specimen dome test (HSDT). The shear loads and the shear edge quality were thoroughly characterized and compared. The HSDT created the edge forming limits as compared to the base material forming limit diagram. The load-displacement curve was acquired by the load-cell and the strain distribution was measured using a digital image correlation (DIC) system during the dome test.

In the first part of this paper, a previously published acceleration compensation methodology for dynamic dent testing [1] was successfully applied to calculate dent loads and applied energy in dynamic dent testing. This procedure was validated utilizing a hydraulic controlled dynamic dent tester on a number of low carbon and bake hardenable steels. In the second part of this study, the impact of strain rate on material bending and hardening in high-speed dynamic dent resistance testing was studied. Previous work [2] investigated these factors in static dent resistance. The procedure utilized in that research was further developed and adapted for high speed testing and used as a basis for a new, single loading incremental dynamic dent test. This new test was used to investigate the effects of material bending and hardening in high-speed dynamic dent resistance. Testing incorporated laboratory produced stretch dome panels with 2% biaxial strains as test specimens.

A standardized quasi-static dent test has been used in evaluating the dent resistance of automotive body panels for many years. In order to predict the onset of a visible dent, cyclic loading with small load increments was adopted into standard automotive test procedures. Although researchers have investigated the effects of sheet thickness, yield strength, strain aging and prestrain on the static dent resistance of sheet steel in the past, material bending and hardening effects on static dent resistance were assumed to be inconsequential, and were therefore largely ignored. In this study, the impacts of material bending and hardening on static dent resistance are investigated. A fixed load, single loading condition was carefully designed for different materials and incorporated into the quasi-static dent test. For comparison, the incremental quasi-static loading condition is also examined.

Different die surface polish conditions result in a noticeable effect on material flow in stamping, which can lead to splitting, wrinkling, or other surface stretching issues associated with different friction conditions. These occurrences are not only limited to the non-coated dies, but also nitrided and chrome plated dies. To ensure quality control of the stamped parts, the die conditions corresponding to different polishing procedures need to be developed based on measurable parameters such as surface roughness (Ra). The intent of this study is to investigate the effects of nitrided and chrome plated die surface roughness on friction. The Bending-Under-Tension (BUT) test was conducted to simulate the stamping process due to the test’s versatility and flexibility in changing test parameters. The test involves moving sheet metal across a 3/8-inch diameter pin, which substitutes for a die surface. The pin can be modified by material, heat treatment, coating, and surface roughness.