Advanced high strength steels (AHSS) offer a good balance of strength, durability, crash energy absorption and formability. Applications of AHSS for lightweight designs of automotive structures are accelerating in recent years to meet the tough new CAFE standard for vehicle fuel economy by 2025. At the same time, the new generation pickup cargo box is to be designed for a dramatic increase in payload. Upgrading the box material from conventional mild steels to AHSS is necessary to meet the conflicting requirements of vehicle light weighting and higher payload. In this paper, typical AHSS grades such as DP590 and DP780 were applied to selected components of the pickup cargo box for weight reduction while meeting the design targets for fatigue, strength and local stiffness.

Exposure in ISO 26262 is defined as the state of being in an operational situation that can be hazardous if coincident with the failure mode under analysis. An operational situation is defined as a scenario that can occur during a vehicle's life with examples given such as driving, parking, or maintenance. Accurately predicting exposure is one of the more difficult tasks in the ASIL determination. ISO 26262 Part 3 attempts to provide guidance in Annex B through tables of potential operational situations and associated exposure levels. However, the contents of these tables may not allow for an accurate prediction of exposure and may lead to an exposure value that is too high or too low. In this paper, we describe a potential method for determining exposure that considers a potential mishap scenario as a composition of multiple coincident operational situations rather than considering a single operational situation as indicated in the tables in Annex B of Part 3.

Dang Van (Dang Van et al., 1982 and Dang Van, 1993) states that for an infinite lifetime (near fatigue limit), crack nucleation in slip bands may occur at the most unfavorable oriented grains, which are subject to plastic deformation even if the macroscopic stress is elastic. Since the residual stresses in these plastically deformed grains are induced by the restraining effect of the adjacent grains, it is assumed that the residual stresses are stabilized at a mesoscopic level. These stresses are currently approximated by the macroscopic hydrostatic stress defined by the normal stresses to the faces of an octahedral element oriented with the faces symmetric to the principal axis; mathematically they are equal to each other and they are the average of the principal stresses.

Fuel Tank Straps very often get different durability fatigue test results from different types of durability testing such as shaker table vibration, road test simulator (RTS) vehicle testing and proving ground vehicle durability testing. One test produces good durability results and other may indicate some durability risk. A special study was conducted to address this inconsistency. It was found that fuel level in the tank plays a big role in fuel tank strap durability. Higher fuel levels in a tank produce higher loads in straps and lower fatigue life. This paper will use a CAE fuel tank strap model and acquired proving ground strap load data to study fuel level influence in fuel tank strap durability. The fuel level study includes a full tank of fuel, 3 quarters tank of fuel, a half tank of fuel and one quarter tank of fuel.

In order to take into account the local material non-linear elastic-plastic effects generated by notches, Glinka proposed the equivalent strain energy density (ESED) Criterion which has been widely accepted and used in fatigue theory and calculation for the last few decades. In this paper, Glinka's criterion is applied to structural optimization design for elastic-plastic correction to consider material non-linear elastic-plastic effects. The equivalent (fictitious) stress was derived from Glinka's Criterion equation for the commonly used Ramberg-Osgood and bi-linear stress and strain relationships. This equivalent stress can be used as the stress boundary constraint threshold in structural optimization design to control the elastic-plastic stress or strain in nonlinear optimization.

This paper introduces a methodology to calculate confidence bounds for a normal and Weibull distribution using Monte Carlo pivotal statistics. As an example, a ready-to-use lookup table to calculate one-sided lower confidence bounds is established and demonstrated for normal and Weibull distributions. The concept of one-sided lower tolerance limits for a normal distribution was first introduced by G. J. Lieberman in 1958 (later modified by Link in 1985 and Wei in 2012), and has been widely used in the automotive industry because of the easy-to-use lookup tables. Monte Carlo simulation methods presented here are more accurate as they eliminate assumptions and approximations inherent in existing approaches by using random experiments. This developed methodology can be used to generate confidence bounds for any parametric distribution. The ready-to-use table for the one-sided lower tolerance limits for a Weibull distribution is presented.

Two on-line algorithms have been developed to acquire driveline component loads in terms of revolutions at torque and rainflow cycle counting matrix. These algorithms have been implemented in real-time on a standard engine controller unit and have been optimized for fast run-time and low memory requirements. The revolutions at torque algorithm is intended to count the number of driveshaft revolutions in each torque level for each gear and store the number of counts in the engine controller memory. The rainflow cycle counting algorithm is intended to count driveshaft torque cycles and to store the number of counts in a two dimensional “from-to” matrix format in the engine controller memory. The revolutions at torque histogram data and the rainflow cycle counting matrix are then downloaded from the vehicle using the data collection device. Download occurs when the vehicle is serviced at a dealership.

Two finite element optimization techniques are presented for minimizing automotive engine air induction structural radiated noise and mass. Air induction systems are generally made of thin wall plastic which is exposed to high levels of pulsating engine noise. Weak air induction system walls vibrate excessively creating noise that can be heard by the driver. The conventional approach is to add ribs (many times through trial and error) which increase part weight or by adding “kiss-offs,” which restrict air flow. The finite element optimization methods considered here are shape optimization and topometry optimization. Genesis, a fully integrated finite element analysis and optimization package by Vanderplaats Research & Development, was used to perform finite element optimization. Choice of optimization method is primarily dependent on several factors which are appearance, part interference and flow restriction requirements.

In this paper, the development of random vibration testing schedules for durability design verification of engine mounted products is presented, based on the equivalent fatigue damage concept and the 95th-percentile customer engine usage data for 150,000 miles. Development of the 95th-percentile customer usage profile is first discussed. Following that, the field engine excitation and engine duty cycle definition is introduced. By using a simplified transfer function of a single degree-of-freedom (SDOF) system subjected to a base excitation, the response acceleration and stress PSDs are related to the input excitation in PSD, which is the equivalent fatigue damage concept. Also, the narrow-band fatigue damage spectrum (FDS) is calculated in terms of the input excitation PSD based on the Miner linear damage rule, the Rayleigh statistical distribution for stress amplitude, a material's S-N curve, and the Miles approximate solution.

Elastomers have large reversible elastic deformation, good damping and high energy absorption capabilities. Due to these characteristics along with low cost of manufacturing, elastomeric components are widely used in many industries and applications, including in automobiles. These components are typically subjected to complex multiaxial and variable amplitude cyclic loads during their service life. Therefore, fatigue failure and life prediction are important issues in the design and analyses of these components. Availability of an effective CAE technique to evaluate fatigue damage and to predict fatigue life under complex loading conditions is a valuable tool for such analysis. This paper discusses a general CAE analytical technique for durability analysis and life prediction of elastomeric components. The methodology is then illustrated and verified by using experimental fatigue test results from an automobile cradle mount.

An accurate representation of proving ground loading is essential for nonlinear Finite Element analysis and component fatigue test. In this paper, a rainflow counting based multiple blocks loading development procedure is described. The procedure includes: (1) Rainflow counting analysis to obtain the relationship between load range and cumulative repeats and the statistical relationship between load range and mean load; (2) Formation of preliminary multiple loading blocks with specified load range, mean load, and the approximate cycle repeats, and construction of the preliminary multiple loading blocks; (3) Calibration and finalization of the repeats for preliminary multiple loading blocks according to the equivalent damage rule, meaning that the damage value due to the block loads is equivalent to that from a PG loading.

Reliable testing of a mechanical system requires the procedures used for the evaluation to be repeatable and reproducible. However, it is never possible to exactly repeat or reproduce the tests that are used for evaluation. To overcome this limitation, a statistical evaluation procedure can generally be used. However, most of the statistical procedures use scalar values as input without the ability to handle vectors or time-histories. To overcome these limitations, two numerical/statistical methods for determining if the impact time-history response of a mechanical system is repeatable or reproducible are evaluated and elaborated upon. Such a system could be a vehicle, a biological human surrogate, an Anthropometric Test Device (ATD or dummy), etc. The responses could be sets of time-histories of accelerations, forces, moments, etc., of a component or of the system. The example system evaluated is the BioRID II rear impact dummy.

Traditional warm forming of aluminum refers to sheet forming in the temperature range of 200°C to 350°C using heated, matched die sets similar to conventional stamping. While the benefits of this process can include design freedom, improved dimensional capability and potentially reduced cycle times, the process is complex and requires expensive, heated dies. The objective of this work was to develop a warm forming process that both retains the benefits of traditional warm forming while allowing for the use of lower-cost tooling. Enhanced formability characteristics of aluminum sheet have been observed when there is a prescribed temperature difference between the die and the sheet; often referred to as a non-isothermal condition. This work, which was supported by the USCAR-AMD initiative, demonstrated the benefits of the non-isothermal warm forming approach on a full-scale door inner panel. Finite element analysis was used to guide the design of the die face and blank shape.

The common practice in finite element based fatigue calculation with multiple channels of road load is to perform a set of unit load static stress analysis and conduct stress time history construction later during fatigue calculation. The main advantage of this so-called quasi-static finite element based fatigue calculation is to avoid time-consuming dynamic stress analysis and also reduce static stress analysis from millions of real load cases to a few dozens unit-load cases. The main disadvantage of this quasi-static finite element based fatigue calculation is the absence of vibration-induced stresses in stress time history construction and fatigue analysis. A decade ago, a modal transient finite element based fatigue calculation was proposed to introduce vibration-induced stresses into finite element based fatigue calculation. The idea is to add vibration-induced modal stresses to load-induced instant stresses in stress time history construction and fatigue calculation.

During component development of multiple fastener bolted joints, it was observed that one or two fasteners had a higher potential to slip when compared to other fasteners in the same joint. This condition indicated that uneven distribution of the service loads was occurring in the bolted joints. The need for an optimization tool was identified that would take into account various objectives and constraints based on real world design conditions. The objective of this paper is to present a method developed to determine optimized multiple fastener locations within a bolted joint for achieving evenly distributed loads across the fasteners during multiple load events. The method integrates finite element analysis (FEA) with optimization software using multi-objective optimization algorithms. Multiple constraints were also considered for the optimization analysis. In use, each bolted joint is subjected to multiple service load conditions (load cases).

Most manufacturing and assembly processes like stamping, clamping, interference fits introduce a pre-stress condition in components or assemblies. Very often these stresses are high enough and alter the mean stress state resulting in significant effect on fatigue life performance and thus cannot be ignored. If the pre-stress is compressive, it will increase the allowable stress range and improve fatigue life performance; on the other hand if these stresses are tensile, they will decrease the allowable stress range resulting in a degradation of fatigue life. At times it becomes critical to effectively introduce the pre-stress condition in order to accurately represent the stress state in an FEA based durability simulation. Accounting for the pre-stress state in FEA based constant amplitude loading fatigue life simulation is relatively straight forward, but when it comes to random variable amplitude multi-channel loads simulation, the problem becomes more complicated.

The air induction system (AIS), which provides clean air to the engine for combustion, is very important for engine acoustics. A practical CAE procedure to predict AIS inlet noise is presented in this paper. GT-Power, a commercially available software program can be used to simulate the engine performance and predict air induction noise. The accuracy of GT-Power is dependent on many variables, such as: proper duct discretization size, proper number of flow splits to model the air box and the capturing of the correct resonator geometry for tuning frequency. Since GT-Power is based on a 1D assumption, several iterations need be performed to model the complex AIS components, such as, irregular shaped air box, resonator volume, porous ducts and perforated pipes. Because of this, the GT-Power AIS model needs to be correlated to test data using transmission loss data.

Contacts or interactions commonly exist between adjacent components in automotive structures, and most of the time they dominate stress status of the components. However, when the routine pseudo stress approach is employed in fatigue life estimations, simulating contacts present special challenges. This may result in coarse stress status and corresponding coarser fatigue life estimations at the contact locations. In this paper, concept, development and procedures of two techniques to consider contacts in fatigue life estimations of automotive structures are described in detail. One is still pseudo stress approach based, but employs additional 1-D connection elements to simulate contacts. The other is nonlinear stress approach based, but equivalent constantly repeating cyclic critical load cases are introduced and utilized. The contacts are simulated by interface setup provided in the software.

A body mount joint is a typical clamped joint that is under severe loading conditions, due to its structural function services as a gateway of load path between body and frame of an automotive vehicle. Stresses/strains on durability concerned components at the joint cannot be captured accurately by using the pseudo stress analysis approach because of the complexity of stress state generated by the pre-stress from clamp load, contacts between the components and nonlinear material properties. In this paper, development of a technique for fatigue life estimation of the joint is described in detail.

Fatigue analysis in the time domain using the rainflow cycle counting algorithm is considered the most accurate method for estimating damage. Dirlik's method has been found to be very accurate for damage estimation in the frequency domain. Previous studies have demonstrated the usefulness of Dirlik's method for ocean engineering and wind turbines but few have shown how well Dirlik performs in automotive applications. This study compares Dirlik's method with the rainflow cycle counting and with other frequency domain methods. The study analyzes measured data for an automotive component subjected to five test track load conditions. In addition, fourteen of Dirlik's original spectra and seven additional spectra which combine sine and random spectra are studied. It was found that Dirlik's method predicts more damage than the rainflow cycle counting method when applied to the original data used in creating the method.