Search Results

The die wear up to 80,800 hits on a prog-die setup for bare DP1180 steel was investigated in real production condition. In total, 31 die inserts with the combination of 11 die materials and 9 coatings were evaluated. The analytical results of die service life for each insert were provided by examining the evolution of surface wear on inserts and formed parts. The moments of appearance of die defects, propagation of die defects, and catastrophic failure were determined. Moreover, the surface roughness of the formed parts for each die insert was characterized using Wyko NT110 machine. The objectives of the current study are to evaluate the die durability of various tooling materials and coatings for flange operations on bare DP 1180 steel and update OEM tooling standards based on the experimental results. The current study provides the guidance for the die material and coating selections in large volume production for next generation AHSSs.

Traditional warm forming of aluminum refers to sheet forming in the temperature range of 200°C to 350°C using heated, matched die sets similar to conventional stamping. While the benefits of this process can include design freedom, improved dimensional capability and potentially reduced cycle times, the process is complex and requires expensive, heated dies. The objective of this work was to develop a warm forming process that both retains the benefits of traditional warm forming while allowing for the use of lower-cost tooling. Enhanced formability characteristics of aluminum sheet have been observed when there is a prescribed temperature difference between the die and the sheet; often referred to as a non-isothermal condition. This work, which was supported by the USCAR-AMD initiative, demonstrated the benefits of the non-isothermal warm forming approach on a full-scale door inner panel. Finite element analysis was used to guide the design of the die face and blank shape.

Generally linear finite element analysis (FEA) is used to predict fatigue life of spot welded joints in a vehicle body structure. Therefore, the effect of plastic deformation at the vicinity of the spot welded joints is not included on fatigue prediction. This study introduces a simple technique to include the plastic deformation effect without performing elastic-plastic finite element analysis. The S-N curve obtained from fatigue test results is modified to consider this effect. Tensile strength test results of spot welded joint specimens were utilized to find the load range for FEA equivalent to the applied load range for fatigue tests. To demonstrate the proposed approach, fatigue test results of advanced high strength steels (AHSS) for lap-shear and coach peel specimens were used. Both the specimen types were tested at various constant amplitudes with the load ratios of R=0.1 and 0.3.

An extruded Mg-Al-Mn (AM30) magnesium alloy was subjected to uniaxial compression along the extrusion direction (ED) and the extrusion radial direction (RaD) at 450 °C and different strain rates. The microstructure and texture of the AM30 alloy under different deformation conditions were examined. Texture evolution was characterized by electron backscatter diffraction (EBSD). The activity of different deformation modes including twinning were simulated using the visco-plastic self-consistent (VPSC) and the simplistic Sachs polycrystal plasticity models. The results show that the microstructure and the mechanical property of the Mg alloy strongly depend on the strain rate, with twinning activated at strain rates >0.5 s−1. Dynamic recrystallization and twinning interacted with each other and affected the final microstructure and mechanical property of the magnesium alloy.

This paper investigates changes in fuel economy of a mid-size sedan at various engine cooling fan power levels and front grille opening areas. A full vehicle model was built using MATLAB Simulink to calculate the fuel economy (MPG). The model utilized inputs from aerodynamic wind tunnel testing as well as FTP and MVEG dynamometer tests results. Simulation and testing was carried out at three front opening areas and three engine cooling fan power levels. The results provide a guideline for optimizing the front grille opening vs. engine cooling fan power combination at various driving conditions.

Temperature effects on the deformation and fracture of a commercially produced transformation-induced plasticity (TRIP) steel subject to a two-step quenching and partitioning (Q&P) heat treatment are investigated. Strain field evolution at room temperature is quantified in this 980 MPa grade Q&P steel with a stereo digital image correlation (DIC) technique from quasi-static tensile tests of specimens with 0°, 45°, and 90° orientations. Baseline tensile properties along with the variation of the instantaneous hardening index with strain were computed. Variations of the bake-hardening index were explored under simulated paint bake conditions. Tensile properties were measured at selected temperatures between -100°C and 200°C and the TRIP effect was found to be temperature-dependent due to stress-induced martensitic transformation at lower temperatures versus strain-induced transformation at higher temperatures.

Conventional HVAC systems adjust the position of a temperature door, to achieve a required air temperature discharged into the passenger compartment. Such systems are based upon the fact that a conventional (non-hybrid) vehicle's engine coolant temperature is controlled to a somewhat constant temperature, using an engine thermostat. Coolant flow rate through the cabin heater core varies as the engine speed changes. EREVs (Extended Range Electric Vehicles) & PHEVs (Plug-In Hybrid Electric Vehicles) have two key vehicle requirements: maximize EV (Electric Vehicle) range and maximize fuel economy when the engine is operating. In EV mode, there is no engine heat rejection and battery pack energy is consumed in order to provide heat to the passenger compartment, for windshield defrost/defog and occupant comfort. Energy consumption for cabin heating must be optimized, if one is to optimize vehicle EV range.

Evaluating spot weld separation is one of the most challenging tasks in a quasi-static simulation. There are several factors that exist in modeling welds analytically that can influence correlation to physical test. This paper presents 4 specific factors: spot weld representation, weld thickness, weld strength, and metal forming effects around spot welds. There are many ways in which a spot weld can be modeled within an FEA model from mesh independent beams to mesh dependent hex clusters. While each modeling technique comes with its unique sets of advantages and disadvantages, a method is chosen to best balance correlation, model setup timing and computation time. Dependent on the way the thickness of the spot weld is represented, artificial moments can be induced which misrepresents structural behavior. The assigned yield strength of the spot weld influences the behavior of the joint.

Magnesium and aluminum alloys offer lightweighting opportunities in automotive applications. Joining of dissimilar materials, however, generally requires methods that do not involve fusion. This paper explores the use of self-pierce riveting (SPR) to join magnesium to aluminum alloys for structural and closure applications. The preliminary results indicate that SPR is a viable option for joining aluminum extrusions to magnesium die castings, as well as stamped sheet aluminum to quick-plastic-formed (QPF) sheet magnesium.

Experimental decklids for the Cadillac STS sedan were made with Al AA5083 sheet outer panels and Mg AZ31B sheet inner panels using regular-production forming processes and hardware. Joining and coating processes were developed to accommodate the unique properties of Mg. Assembled decklids were evaluated for dimensional accuracy, slam durability, and impact response. The assemblies performed very well in these tests. Explicit and implicit finite element simulations of decklids were conducted, and showed that the Al/Mg decklids have good stiffness and strength characteristics. These results suggest the feasibility of using Mg sheet closure panels from a structural perspective.

This paper describes rationale for determining the apportionment of variable or ‘shuttered’ airflow and non-variable or static airflow through openings in the front of a vehicle as needed for vehicle cooling. Variable airflow can be achieved by means of a shutter system, which throttles airflow through the front end and into the Condenser, Radiator, and Fan Module, (CRFM). Shutters originated early in the history of the auto industry and acted as a thermostat [1]. They controlled airflow as opposed to coolant flow through the radiator. Two benefits that are realized today are aerodynamic and thermal gains, achieved by restricting unneeded cooling airflow. Other benefits exist and justify the use of shutters; however, there are also difficulties in both execution and practical use. This paper will focus on optimizing system performance and execution in terms of the two benefits of reduced aerodynamic drag and reduced mechanical drag through thermal control.

A comprehensive experimental and theoretical approach was undertaken to understand the phenomenon of pre-ignition and to assess parameters to improve or even eliminate it completely. Oil mixing with fuel was identified as the leading theory of self ignition of the fuel. End of compression temperature has to meet a minimum level for pre-ignition to take place. In this work a comprehensive list of parameters were identified that have a direct and crucial role in the onset of pre-ignition including liner wetting, injection targeting, stratification, mixture motion and oil formulation. Many secondary effects were identified including ring dynamics, ring tension, spark plug electrode temperature and coolant temperature. CFD has been extensively used to understand test results including wall film, A/F ratio distribution and temperature at the end of compression when looked at in the context of fuel evaporation and mixing.

During sheet metal forming, the friction and surface roughness change as the sheet slides, bends and stretches against the tools. This study assessed evolution of friction and surface roughness changes on aluminum sheet with two surface finish conditions, mill finish (MF) and electron discharge texture (EDT), in both the longitudinal and the transverse rolling directions of the sheet. The sheets were tested using a three pin Draw Bead Simulator (DBS). Surface roughness of the sheet evolved as a result of bending at the first shoulder, reverse bending at the middle pin, bending at the second shoulder and unbending at the exit. Stretching conditions and sheet-pin contact were also varied to see the impact on surface roughness. In general, the largest surface roughness change for the transverse direction was observed at the convex side of the exit shoulder pin and on the convex side of the first shoulder for the longitudinal direction.

Aluminum sheet is commercially available in three surface finishes, mill finish (MF), electric discharge texture (EDT), and dull finish (DF). This surface finish impacts the friction behavior during sheet metal forming. A study was done to compare ten commercially available sheet samples from several suppliers. The friction behavior was characterized in the longitudinal and transverse directions using a Draw Bead Simulator (DBS) test, resulting in a coefficient of friction (COF) value for each material. Characterization of the friction behavior in each direction provides useful data for formability analysis. To quantitatively characterize the surface finish, three-dimensional MicroTexture measurements were done with a WYKO NT8000 instrument. In general, the MF samples have the smoothest surface, with Sa values of 0.20-0.30 μm and the lowest COF values. The EDT samples have the roughest surface, with Sa values of 0.60-1.00 μm, and the highest COF values.

The preform annealing process is a two-stage stamping method for shaping non age-hardenable (i.e. 5000 series) aluminum sheet panels in which the panel is heat treated in between the two steps to improve overall formability of the material. The intermediate annealing heat treatment eliminates the cold work accumulated in the material during the first draw. The process enables the ability to form more complex parts than a conventional aluminum stamping process. A demonstration of local annealing for this process was conducted to form a one-piece aluminum liftgate inner panel for a large sport utility vehicle using the steel product geometry without design concessions. In prior work, this process was demonstrated by placing the entire panel in a convection oven for several minutes to completely anneal the cold work.

It is important to understand the accuracy level of the formability analysis for any new process so that correct predictions can be made in product and die design. This report focuses on the formability analysis methodology developed for the preform anneal process. In this process, the aluminum panel is partially formed, annealed to eliminate the cold work from the first step, and then formed to the final shape using the same die. This process has the ability to form more complex parts than conventional aluminum stamping, and has been demonstrated on a complex one-piece door inner and a complex one-piece liftgate inner with AA5182-O3. Both panels only required slight design modifications to the original steel product geometry. This report focuses on the formability analysis correlation with physical panels for the liftgate inner, considering both full panel anneal in a convection oven and local annealing of critical areas.

The sealing of a lift gate hinge to the body structure is necessary to avoid both the onset of corrosion and to avoid water intrusion into the interior compartment. The hinge-to-body interface typically involves horizontal metal-to-metal surface contact, creating the perfect environment for moisture entrapment and corrosion initiation. The choice of body panel material (uncoated (bare) steel vs. coated (galvanized) steel) drives different sealing approaches especially when considering corrosion avoidance.

Polyacetals have high strength, modulus, and chemical resistance with good dimensional stability. Because of these properties, they are used in a number of automotive applications. The injection molding process used for the molding of these components is complex and requires the adjustment of multiple process parameters to produce parts. Typically, physical tests are used to confirm that tensile strength is achieved in processing. A study was undertaken with an impact modified carbon powder filled, acetal copolymer to determine the effect of variation in process parameters on other material properties in addition to tensile strength. These material properties were measured dry as-molded and after exposure to heat and to a test fluid. It was determined that in the case of this specific polymer, the barrel temperature, and to a lesser extent the cooling time during processing, affected the strain at break.

Current manufacture of alternative energy sources for automobiles, such as fuel cells and lithium-ion batteries, uses repeating energy modules to achieve targeted balances of power and weight for varying types of vehicles. Specifically for lithium-ion batteries, tens to hundreds of identical plastic parts are assembled in a repeating fashion; this assembly of parts requires complex dimensional planning and high degrees of quality control. This paper will address the aspects of dimensional quality for repeated, injection molded thermoplastic battery components and will include the following: First, dimensional variation associated with thermoplastic components is considered. Sources of variation include the injection molding process, tooling or mold, lot-to-lot material differences, and varying types of environmental exposure. Second, mold tuning and cavity matching between molds for multi-cavity production will be analyzed.

Coolant pipes are a prime connection units present in any engines that facilitates the flow of coolant and thereby keeping the engine under its optimum operating condition. Among the several influencing factors that deteriorate engines performance, the coolant leak is also one of the contributors. This could be caused primly due to leakage issues that arises from the pipe press fit zones. Henceforth it is very important to understand the root cause of this press-fit connection failure. The present study deals with press-fit between the pipe and housing in an engine which is subjected to extreme thermal loads (min of -40°C to a max temperature of +150°C) thereby causing the press-fit loosening effect.