Due to improvements in vehicle powertrain performance, friction material fade performance is becoming an important topic. For this reason, needs for studies to improve thermal characteristics of the brake system is increasing. Methods for improving the fade characteristics have several ways to improve the thermal characteristic of friction materials and increase disc capacity. However, increasing disc capacity(size) have some risk of weight and cost rise, and friction factor improvements in friction material tend to cause other problems, such as increasing squeal wire brush noise and increasing metal pick up on disc surface. Therefore, a slot disc study is needed to overcome the problems discussed previously. Currently, there is few research history for slot disc related to fade and metal pickup improvements.

Fuel tank in vehicle must hold the fuel in a stable way under any driving condition. However, the fuel tank might not conserve the fuel firmly in case a crack emerged while the fuel tank is exposed to different driving condition. Basically, when the engine is in purging at a normal ambient temperature before fuel boiling, the pressure inside the fuel tank decreases. However, the pressure inside a fuel tank increases while a vehicle is driven at extreme hot ambient temperature as fuel is boiling. This repetitive pressure change in the fuel tank comes with fuel tank’s physical expansion and shrink, which would cause a damage to the fuel tank. The main purpose of this research is to investigate the root cause of why fuel tank cracks at a fatigue point. We also aim to set up the method of how to test durability of the fuel tank in association with the pressure inside the tank.

Numerical durability analysis is the only approach that can be used to assess the durability of vehicles in early stages of development. In these stages, where there are no physical prototypes available, the road wheel forces (or spindle forces) for durability testing on Belgian PG (Proving Ground) must be predicted by VPG (Virtual Proving Ground) or derived from the measured forces of predecessor vehicles. In addition, the tuning parts and geometry are not fixed at these stages. This results in the variation of spindle forces during the development stages. Therefore, it is not reasonable to choose the forces predicted at a specific tuning condition as standard forces. It is more reasonable to determine the standard forces stochastically using the DB of the measured forces of predecessor vehicles. The spindle forces measured or predicted on Belgian PG are typically stationary random.

Due to technological evolutions and social demands, motor vehicles are requested to be enhanced in terms of occupant safety and comfort. As a result, many countries are reinforcing crash regulations and new car assessment programs. Automotive seats are essential parts for providing passenger safety and comfort and have become most important. Many automotive companies concentrate on optimization of the seat structure. This paper presents an overview of the recent evolution of the seat structures and gives a development procedure covering seat frame design, optimization and validation. Through the study, a competitive frame design is drawn as a case result and a design guideline and a standard development procedure is established

Anti-vibration rubbers in vehicle play an important role in restricting vibration generated from engine and road. But, degradation occurs when rubber is exposed for a long time to heat, light, ozone and etc. These make the rubber hard and lose its initial properties. The rubber change makes N.V.H performance of vehicle the worse, and gives the discomfort to the passengers. To reduce the change of rubber properties, sulfur-donor and heat stable cross-linking co-agent vulcanization system have been introduced in the developed natural rubber compounds of the anti-vibration rubber parts. These lead to a reduction of degradation of material properties, maintenance of the initial properties and increase of the fatigue life.

This paper presents an in-vehicle information system, AVICS in development. With AVICS, the driver could get the various information on traffic, news, weather, restaurants, and so on, which the AVICS information center provides via mobile telecommunication network. The driver requests the information to operator in center by voice with hands-free system or by handling the menu offered in the form of web-page. The in-vehicle unit for AVICS is designed to interface with wireless network with a built-in RF MODEM, to control NAVI system, and to display the information on the LCD monitor of AV system. The Internet browser is customized to parse specific HTML tags, application software is realized on 32-bit RISC processor. In this paper, we will overview the concept of AVICS and focus on development of in-vehicle unit of AVICS.

The effects of tempering on carburized Cr-Mo gear steel were investigated through mechanical and fatigue tests. Specimens were carburized at 900°C for 180 minutes, and then oil quenched at 150°C for 10 minutes of holding time and cooled to room temperature. The subsequent tempering process was performed to 160°C for 90 minutes. Surface hardness and residual compressive stress were decreased by tempering treatment, whereas tensile strength, yield strength and impact energy were increased. Bending fatigue endurance limits for both tempered and untempered specimens were same as 779MPa. The strength of roller contact fatigue is also not greatly influenced by tempering treatment. Thermal distortion for carburized transfer driven gear before and after tempering exhibited a similar distribution. Microstructural changes during tempering were also discussed.

The banded microstructure of pearlite and ferrite in normalized alloy steel is susceptible to thermal distortion during carburizing process due to its unidirectional orientation parallel to rolling direction. The planetary gears with material of banded microstructure have been experienced in high thermal distortion during carburizing and quenching process and result in uneven surface hardness and effective case depth at the inside of pinion gear after honing. These defects played failure initiation site roles in durability test during development of new automatic transmission. The galling between the contacting components in severe lubricating system was the main failure mechanism. Double normalizing at 920 °C was designed to resolve the banded microstructure of normalized alloy steel. The microstructure and grain size of the double heated steel became equiaxed and fine due to homogenizing and recrystallization through double heat treatment.

An automobile's structure is generally connected by spot welding the sheets together. Sometimes more than three layers of sheets can be used in a certain location for spot welding due to the limits of design conditions. Static strength and the fatigue life characteristics can be changed according to the welding conditions, which depend on the material, the thickness, and the number of sheets. Setting the appropriate conditions of multi-layer spot welding can be determined by analyzing static strength and fatigue life. For converting multi-layer spot welding to that of twofold layer with equal strength, the converting method can be suggested from static and fatigue test results. The increasing rate of static strength is larger than that of fatigue life, so it is reasonable to use fatigue life for limit condition.

The objective of this study is to investigate mechanical properties and fatigue crack propagation behavior in hybrid metal matrix composites by squeeze infiltration method (15% Al2O3 + SiCw/6061Al). The mechanical properties of Al2O3+SiCw/Al composites including tensile strength, yield strength, Young's modulus, were improved compared with those of unreinforced alloy and Al203/Al composites. The hybrid composites were more ductile than Al2O3/Al composites. Fatigue crack propagation rates of both Al2O3/Al and Al2O3+SiCw/Al composites showed a similar behavior in region II. Their propagation rates were higher in entire ▵K region compared with that of 6061 Al alloy. From the crack path morphology, fatigue cracks propagated linearly and smoothly in 6061 Al alloy. However, in the metal matrix composites cracks tend to avoid the reinforcements promoting crack deflection. It was observed that crack deflection enhanced crack closure due to wedging phenomenon.

Vehicle body structures are formed by thousands of spot welds, and fatigue failure of vehicle structures occur near the spot welds after driving a long way at a durability test road. It is necessary to know accurately the reason of the fatigue failure of the spot weld in the developing stage in order to reinforce it. Many investigations have been done regarding the strength of spot welded joints, contributing to understand its fatigue strength. In the developing process, a fatigue failed spot welded area can be repaired by CO2 welding or another method to continue the test. To know the effect of reinforcing these welds, several methods of welding were analyzed and compared to spot welding. With the results of this test, the appropriate repair method can be used instead of spot welding during the development of a new car and the best design guide can be given for the strength.

The paper describes an engineering project carried out to optimize the crashworthiness of an existing passenger car for frontal crash using a procedure relying on numerical simulation. An optimization target is defined in terms of an ideal acceleration pulse at the seats anchors. The acceleration time history and structural members are scanned in parallel to correlate the local acceleration peaks to specific structural members. Members details are iteratively modified in order to alter the accelerations and get closer to the target.