Spot friction welding (SFW) is a cost-effective spot joining technology for aluminum sheets compared with resistance spot welding (RSW) [1]. In this study, coated mild steel was spot friction welded to 6000 series aluminum using a tool with shoulder diameter of 10 mm and welding conditions of 1500-2000 rpm and time of 5 s. Testing showed that tensile shear strength increased as the solidus temperature of the coating on the steel decreased. Microstructure characterizations of steel/Al joint interfaces showed that zinc from the coatings was incorporated into the stir nuggets and that intermetallic phases may have formed but not in continuous layers. Some Al-Zn oxides that appeared to be amorphous were also found in the joint interfaces.

A method of fatigue life prediction of spot welded joint under multi-axial loads has been developed by fatigue life estimation working groups in the committee on fatigue strength and structural reliability of JSAE. This method is based on the concept of nominal structural stress ( σ ns) proposed by Radaj and Rupp, and improved so that D value is not involved in stress calculation. The result of fatigue life estimation of actual vehicle with nominal structural stress which was calculated through newly developed method had very good correlation with the result of multi-axial loads fatigue test carried out with test piece including high strength steel.

Galvannealed steel sheet (GA) is very extensively used for vehicle panels. However ζ-phase (FeZn13) in GA coat causes poor stamping formability. Previously, there were no easy methods to evaluate the influence of ζ-phase on the frictional characteristics other than the X-ray diffraction method. This study will discuss the development of a new testing method: Dr. STAMP Method that is both efficient and convenient with pin-on-disc tester.

Tensile testing technique for the small sample was newly developed. Small tensile specimens with gage length of 1mm were taken from spot welds of high tensile strength steel sheets, and stress-strain relationships and ductility of base metal, heat affected zone including corona bond and nugget were individually measured. Finite element analyses of spot-welded joints under the conditions of static and dynamic tensile-shear loading were carried out with these local mechanical properties to predict the fracture mode and strength of the joints. It was clarified that the effects of both nugget diameter and class of steels were evaluated with good accuracy.

In recent years, improving fuel efficiency and collision safety are important issue. We have worked on a new construction method to develop body structure which is light weight and strong/stiff. We adopt multi type Tailor-Welded Blanks (TWB) which is formed after welding several steel sheets for ATENZA (MAZDA 6), NEW DEMIO (MAZDA 2), and RX-8. This is a technology to consistently improve of such product properties and to reduce costs. Laser welding is a common TWB welding method, but for further equipment cost reductions and productivity improvements, we have developed a higher welding speed and robust plasma welding and introduced this to mass production. We introduce this activity and results in this report.

This paper describes the lap welding of Zinc-coated steel sheet using a high power continuous wave YAG laser. The well-known problem of welding the Zinc-coated sheet is related to the low boiling point of zinc compared with the melting point of steel. During lap welding, zinc coating at the interface vaporize rapidly and causes defects1)2). In this study, therefore, lap welding was performed by YAG laser. The effects of type of coating layer, welding conditions, tensile strength and corrosion resistance after electro-deposition was examined. It was found that the weldability of coated steel is different by type of coating. Zn-Ni coated steel showed good weldability, but galvanealed steel inevitably pore pits with no gap set up. These defects not only lower the strength of joint, but also produce irregular bead where easily corroded after electro-deposition.

Disk brake rotors require reduced unsprung weight and improved cooling ability for improved fade performance. Automotive brake rotors made from aluminum metal matrix composites (MMC) were evaluated by dynamometer and vehicle tests for the required improvement. The friction and wear performance and the thermal response during fade stops were compared with those of commercially produced gray cast iron (GCI) rotors. It was proved that MMC is a very effective material to replace GCI for brake rotor application, as it reduces unsprung weight and decreases maximum operation temperature of the brake system.

Magnesium has the lowest specific gravity of all metals used for structural members. The application of magnesium for a road wheel leads to improved vehicle handling and drivability because of the reduction of an unsprung weight. The authors have developed new magnesium alloy which shows excellent mechanical properties and attained a magnesium forged road wheel that is 30% lighter than aluminum wheels.

A method was studied for simultaneous zinc phosphating on aluminum and steel surfaces to obtain high corrosion resistance on aluminum surfaces, which conventional phosphatic processing could not provide with sufficient corrosion resistance. Since aluminum is protected by an oxide film on its surface, it has poor processability with zinc phosphating solutions applied to steel. An appropriate quantity of fluoride was therefore added to improve processing, and the coating film, aluminum composition and surface conditions were optimized to suppress filiform corrosion, which is characterized by string-like blisters of paint film starting from a paint defect. In addition, in view of the actual production environment, the corrosion resistance of the ground area made for readjustment after stamping was studied for the optimization of the processing solution.

In order to investigate the corrosion resistance of organic composite-coated steel sheets ( OCS ) in a real automotive environment, many kinds of corrosion tests were performed on test pieces and real automotive doors. Tests with a corrosive solution including iron rust were introduced to simulate the real corrosive environment of automotive doors. The relationship between the components of OCS and the corrosion resistance in the rust-including tests was examined. In addition, electrochemical studies were performed. Results indicate OCS has much better corrosion resistance than plated steel sheets with heavier coating weight in all tests. OCS shows excellent corrosion resistance in rust-free corrosive solution, however, some types of OCS do have corrosion concerns in rust-including tests. It became clear that these OCS types have an organic coating with lower cross-linking.

A wider usage of hot rolled high strength steels (HRHSSs) are intensively studied for more complicated underbody structural parts of cars now. With an emphasis placed on the improvement of sheared-edge flangeability, we have developed new types of HRHSSs ranging from 440N/mm2 to 690N/mm2 in ultimate tensile strength (UTS). The microstructure and chemistry of these steels were controlled: The hard second phase in the polygonal ferrite matrix was controlled both by adjusting the chemical composition, mainly, silicon-content, and by applying thermomechanical treatment to a hot strip mill. Compared to conventional high strength steels such as a high-carbon, low-silicon steel and a niobium-bearing steel, various formability-performances of the developed steels were found to be good.

Recently, many kinds of coated steel sheets are developed and used for automobile panels. Some of them show higher coefficient of friction and poorer formability than a cold rolled steel sheet. New polymer lubricating films are developed and proved to improve frictional characteristics of coated steel sheets in this study. The developed polymer lubricating films are applied to Electro Galvanized steel sheet and Hot Dip Galvannealed steel sheet, and coefficient of friction and formability of them are measured by using model dies. Different coefficients of friction are obtained by a change in a combination of components in a polymer lubricating film. As a result, the most suitable coefficient of friction is able to chose in forming conditions by the developed polymer lubricating films.

For the automotive exposed panels, several types of 350N/mm2 grade bake-hardenable sheet steel have been developed and actually applied. However for further weight reduction of automotive body panels, especially inner panels, a 450N/mm2 grade sheet steel with excellent formability has been required. For this demand a new 450N/mm2 grade sheet steel has been developed. As the result it was found, that by the co-addition of Mn and P to ultra-low carbon interstitial free steel the recrystallization texture favorable for deep drawability can be formed, accompanied with the increase in tensile strength, when hot band coiled temperature is lower than 773K. In order to improve the property of the 450N/mm2 grade steel, the effect of Si content has been studied. It was found that the deep drawability is not deteriorated by the addition of Si into the Mn and P co-added ultra-low carbon IF-steel.

As a demand for vehicles of higher functionality grows, automakers and material suppliers are devoting increasing efforts to develop technologies for greater safety, lighter weight, higher corrosion resistance, and enhanced quietness. The resin-sandwiched vibration damping steel sheet (VDSS), developed as a highly functional material for reducing vehicle vibration and noise, has been used for oil pans1) and compartment partitions2). First applied for a structural dash panel of the new Mazda 929, a Zn-Ni electroplated VDSS which allows direct electric welding has contributed to greater weight reduction as well as improved quietness.

Two types of TS 450 to 600 MPa grade hot rolled high strength steels have been developed whose strength increases by a post-deformation heat treatment. One is a nitrogen added steel, produced by a low temperature coiling method. This steel shows an increase in tensile strength by about 60 to 90 MPa after a conventional baking treatment. The other is a Cu-bearing steel, produced also by a low temperature coiling method. This steel shows much larger increase in tensile strength by about 200 MPa due to the precipitation hardening of copper, but it requires an additional heat treatment at a relatively high temperature such as 600° C.

Vibration damping steel sheets (VDSS), which have sandwich structures with intermediate layers of resin, have been studied. The most important characteristics of VDSS for inner panels of automotive vehicles are the vibration damping properties, press formability and spot weldability. Vibration damping properties, which are quantified by loss factor,η, were influenced by both tanδ, which indicates damping capacity of resins, and elastic modulus of core resin. From a view point of vibration damping properties, resins with larger tanδ and relatively lower elastic modulus were favorable. Because these mechanical characteristics vary considerably with temperature, it is important to select the most suitable resin for the service temperature range. The relationship between noise reduction effect and loss factor of VDSS were also studied. It was experimentally confirmed that noise reduction effect of VDSS is proportional to the logarithm of their loss factor.

An Advanced driving simulator has been developed at Mazda Yokohama Research Center. The primary use of this simulator is to research future driver-vehicle systems. In an emergency situation, a driver must respond rapidly to perceived motion and visual stimulus to avoid an accident. In such cases, because the time delay associated with the perception of motion cues is shorter than visual and auditory cues, the driver will strongly rely upon perceived motion to control the vehicle. Hence, a driving simulator to be used in the research of driver-vehicle interactions in emergency driving must include a high performance motion system capable of large amplitude lateral motion. The Mazda simulator produces motion cues in four degrees of freedom, provides visual and auditory cues, and generates control feel on the steering wheel. This paper describes the merit of the large amplitude motion system and the features of this newly developed driving simulator.

To coat flexible parts such as R-RIM Urethane Fascia baked at low temperatures, a different painting approach from one for steel parts is employed. Since paint color differences between the fascia and the body would downgrade the product, a color matching technique is required. For better color matching, matching of color shades was attempted with improvement of paint resin, optimal pigment blending and analysis of how color is affected by varying conditions. Application of a primer for finishing has brought about the desired paint film distinctness. Introduced was also the high weatherablilty paint for plastic parts. All such techniques were utilized on R-RIM Urethane Fascia to achieve high-grade color matching.

In order to help the gauge reduction of wheels and chassis parts of automobiles, a form-able and weldable hot rolled steel of 550 MPa grade, named FDP-55, has been developed. FDP-55 is an 0.14% C, 0.1% Si, 1.1% Mn and Nb free A1-killed steel obtained by controlled-cooling to a low coiling temperature on a runout table, and it is featured by ferrite-degenerated pearlite microstructure. Results of co-operative works with automotive makers showed that FDP-55 was successful in the application to wheels and chassis parts attaining the large weight reduction. This paper reports the metallurgical features and characteristics of the steel.

In order to attain the gauge reduction of outer body panels without spoiling the dent-resistance and formability, a bake-hardenable Al-killed steel sheet, named RBH-35, and has been developed in the conventional box-annealing process. RBH-35 is an 0.01% carbon, low manganese and rephosphorized Al-killed steel sheet retaining solute carbon of about 10 ppm. The steel exhibits high r-value, bake-hardenability of 40 MPa, ultimate tensile strength of above 350 MPa and substantially non-aging property. Results of stamping test of door outer panel showed that RBH-35 is the most suitable steel sheet for the thinning of outer body panels by about 10%. This paper reports the metallurgical features, mechanical properties and applications of the steel.