This paper describes the design and analysis of a family of natural gas fueled, uncooled, two-stroke, lean burn, thermal-ignition engines. The engines were designed specifically to meet the requirements dictated by the commercial heat pump application. The engines have a power output ranging from 15 to 100 kW; a thermal efficiency of 36 percent; a mean time between failure greater than 3 years; and a life expectancy of 45,000 hours. To meet these specifications a family of very simple, uncooled, two-stroke cycle engines were designed which have no belts, gears or pumps. The engines utilize crankcase scavenging, lubrication, stratified fuel introduction to prevent raw fuel from escaping with the exhaust gas, use of and ceramic rolling contact bearings. The Thermal Ignition Combustion System (TICS) [1] is used for ignition to enable the engines to operate with a lean mixture and eliminate spark plug erosion.

The cylinder of the aluminum engine block without iron sleeve was coated directly with thin thermal barrier coatings of zirconia and chrome oxide. The cylinder head and valve face and the piston crown were also coated. These three engine components were tested individually and together. The fuel consumption performance of this 84 x 70 mm direct injection diesel engine improved 10% with only coated cylinder bore. When the fuel injection timing of the coated cylinder bore engine was retarded by about 2°CA, emissions characteristics were approximately the same level as for the baseline engine with 8% improvement in brake specific fuel consumption compared with the baseline engine. At constant fuel flow rate to the engine, the exhaust and cylinder head temperatures were higher for the insulated bore case. One can summarize the combustion temperature must have been higher and heat release rates were faster in the insulated case.

Significant reductions in valve and valve-seat insert wear have been demonstrated with the use of advanced materials for natural gas fueled engines. Total valve and insert wear was reduced by a factor of 10. It was demonstrated that the seat insert wear can be completely eliminated by using ceramic materials. All wear is then limited to the valve seat-face. The direct benefits to users of natural gas engines with advanced technology valve system materials can include reduced operating costs, greater convenience, and improved availability.

The trend toward lighter vehicles for improved performance has recently introduced the use of aluminum and plastic materials for vehicle bodies and drive trains. In particular, the aluminum alloy block for engine application is certain to reappear. The soft aluminum cylinder liner will require additional treatment before acceptance. Three possible approaches appear to solve the aluminum cylinder liner dilemma. These approaches are: 1. Use of high silicon aluminum such as the 390 aluminum. 2. Insert or cast steel liners into the aluminum engine block. 3. Ceramic coat the low cost standard aluminum engine block. Each has known advantages and disadvantages. It is the purpose of this paper to present the merits of Option 3, the ceramic coated aluminum cylinder bore from the standpoint of low weight, cost, and tribological effectiveness. The advantages of approaches (1) and (2) are obvious. High temperature after treatment of the ceramic engine components is not required.

The experimental emissions testing of a turbocharged six cylinder Caterpillar 3116 diesel engine converted to the Miller cycle operation was conducted. Delayed intake valve closing times were also investigated. Effects of intake valve closing time, injection time, and insulation of piston, head, and liner on the emission characteristics of the Miller cycle engine were experimentally verified. Superior performance and emission characteristic was achieved with a LHR insulated engine. Therefore, all emission and performance comparisons are made with LHR insulated standard engine with LHR insulated Miller cycle engine. Particularly, NOx, CO2, HC, smoke and BSFC data are obtained for comparison. Effect of increasing the intake boost pressure on emission was also studied. Poor emission characteristics of the Miller cycle engine are shown to improve with increased boost pressure. Performance of the insulated Miller cycle engine shows improvement in BSFC when compared to the base engine.

A previous paper (1)* described the performance improvements which can be obtained by using an “adiabatic” (uncooled) engine for military trucks. The fuel economy improved 16% to 37% (depending upon the duty cycle) and was documented by dynamometer testing and vehicle testing and affirmed by vehicle simulation. The purpose of this paper is to document a NATO cycle 400 hour durability test which was performed on the same model adiabatic engine. The test results showed that the engine has excellent durability, low lubricating oil consumption and minimal deposits.

This paper presents tribological modeling, experimental work, and validation of tribology parameters of a single cylinder turbocharged diesel engine run at various loads, speeds, intake boost pressures, and cylinder liner temperatures. Analysis were made on piston rings and liner materials, rings mechanical and thermal loads, contact pressure between rings and liner, and lubricant conditions. The engine tribology parameters were measured, and used to validate the engine tribology models. These tribology parameters are: oil film thickness, coefficient of friction between rings and liner, friction force, friction power, friction torque, shear rate, shear stress and wear of the sliding surfaces. In order to measure the oil film thickness between rings and liner, a single cylinder AVL turbocharged diesel engine was instrumented to accept the difference in voltage drop method between rings, oil film, and liner.

Thermal barrier coatings (TBC) are perceived as enabling technology to increase low heat rejection (LHR) diesel engine performance and improve its longevity. The state of the art of thermal barrier coating is the plasma spray zirconia. In addition, other material systems have been investigated for the next generation of thermal barrier coatings. The purpose of this TBC program is to focus on developing binder systems with low thermal conductivity materials to improve the coating durability under high load and temperature cyclical conditions encountered in the real engine. Research and development (R&D) and analysis were conducted on aluminum alloy piston for high output turbocharged diesel engine coated with TBC.

Adiabatics, Inc., with the support of the U.S. Army Tank Automotive Research & Development Engineering Center (TARDEC) has developed a low cost, durable ceramic composite cylinder bore coating for diesel engines operating under severe conditions. This bore coating is a ceramic composite consisting primarily of Iron Oxide, Iron Titanate and Partially Stabilized Zirconia. It is applied by unique chemical thermal bonding technology developed at Adiabatics, Inc. and is referred to as Low Temperature Iron Titanate (LTIT). This coating has been tested against a wide range of cylinder bore treatments ranging from hard chrome plate to hard Nickel Silicon Carbide (NikaSil) and found to provide a superior sliding wear surface. It is superior because it is compatible against most common piston ring materials and coatings.

Adiabatics, Inc. with the support of the U.S. Army Tank Automotive & Armaments Command has examined the feasibility of using Diamond Like Carbon (DLC) films and Iron Titanate (Fe2TiO5 or IT) for sliding contact surfaces in Low Heat Rejection (LHR) diesel engines. DLCs have long been a popular candidate for use in sliding contact tribo-surfaces where a perceived reduction of friction losses will result in increased engine efficiency [1]. There exists a broad range of technologies for applying DLC films. This paper examines several types of these technologies and their future application to automotive internal combustion engines. Our work focuses upon DLC use for LHR military diesel engines where operating temperatures and pressures are higher than conventional diesel engines. However, a direct transfer of this technology to automotive diesel or gasoline engines exists for these thin films.

This paper deals with the analysis of heat release characteristics of an insulated turbocharged, six cylinder, DI contemporary diesel engine. The engine is fully insulated with thin thermal barrier coatings. Effect of insulation on the heat release was experimentally verified. Tests were carried over a range of engine speeds at 100%, 93%, 75% and 50% of rated torque. Fuel injection system was instrumented to obtain injection pressure characteristics. The study shows that rate of heat release, particularly in the major portion of the combustion, is higher for the insulated engine. Improvement in heat release and performance are primarily attributed to reduction in heat transfer loss due to the thin thermal barrier coating. Injection pressure at the rated speed and torque was found to be 138 MPa and there was no degradation of combustion process in the insulated engine. Improvements in BSFC at 93% load are 3.25% and 6% at 1600 and 2600 RPM, respectively.

A high output experimental single cylinder diesel engine that was fully coated and insulated with a ceramic slurry coated combustion chamber was tested at full load and full speed. The cylinder liner and cylinder head mere constructed of 410 Series stainless steel and the top half of the articulated piston and the cylinder head top deck plate were made of titanium. The cylinder liner, head plate and the piston crown were coated with ceramic slurry coating. An adiabaticity of 35 percent was predicted for the insulated engine. The top ring reversal area on the cylinder liner was oil cooled. In spite of the high boost pressure ratio of 4:1, the pressure charged air was not aftercooled. No deterioration in engine volumetric efficiency was noted. At full load (260 psi BMEP) and 2600 rpm, the coolant heat rejection rate of 12 btu/hp.min. was achieved. The original engine build had coolant heat rejection of 18.3 btu/hp-min and exhaust energy heat rejection of 42.3 btu/hp-min at full load.

Lubrication of advanced high temperature engines has been one of the greatest obstacles in the development of the Adiabatic engine. Liquid lubricants which gave lubricating properties as well as heat removal function can no longer carry out this duty when piston ring top ring reversal temperatures approach 540°C. Solid lubricants offer some hope. Since solid lubricants cannot perform the heat removal function, its coefficient of friction must be very low, at least <0.10, in order to prevent heat build up and subsequent destruction to the piston rings and cylinder liners. The Hybrid Piston concept developed in the U.S. Army Advanced Tribology program offers some hope, since the top solid lubricant ring slides over the bottom hydrodynamic lubricant film section during each stroke. This paper presents the progress made with the solid lubricant top ring in the Hybrid Piston. Four materials have shown promise in the laboratory to fullfil its mission.

This paper investigates theoretically the benefits of the Miller cycle diesel engine with and without low heat rejection on thermodynamic efficiency, brake power, and fuel consumption. It further illustrates the effectiveness of thin thermal barrier coatings to improve the performance of military and commercial IC engines. A simple model which includes a friction model is used to estimate the overall improvement in engine performance. Miller cycle is accomplished by closing the intake valve late and the engine components are coated with PSZ for low heat rejection. A significant improvement in brake power and thermal efficiency are observed.

Thermal barrier coatings are becoming increasingly important in providing thermal insulation for heat engine components. Thermal insulation reduces in-cylinder heat transfer from the engine combustion chamber as well as reducing component structural temperatures. Containment of heat also contributes to increased in-cylinder work and offers higher exhaust temperatures for energy recovery. Lower component structural temperatures will result in greater durability. Advanced ceramic composite coatings also offer the unique properties that can provide reductions in friction and wear. Test results and analysis to evaluate the performance benefits of thin thermal barrier coated components in a single cylinder diesel engine are presented.

Experimental results focused towards developing tribological surface coatings coupled with liquid lubricant boundary layer effects, for advanced high temperature military diesel engine applications are presented. The primary focus of this work is in the area of advanced, low heat rejection (LHR) high output diesel engines, where high temperature boundary lubrication between the piston ring and the cylinder liner wall surface is critical for successful engine operation. The target temperature focused upon in our research is an operating top ring reversal (TRR) temperature of approximately 538°C. The technology advancement used for this application involves treating porous iron oxide/titanium oxide (Fe2O3/TiO2) and molybdenum (Mo) based composite thermal sprayed coatings with chemical binders to improve coating strength, integrity, and tribological properties. This process dramatically decreases open porosity to form an almost monolithic appearing coating at the surface1.

The two newest internal combustion engine technologies which have demonstrated the most promise in the last 25 years are the direct-injection stratified-charge (DISC) rotary engine [1] and the adiabatic diesel engine [2]. The (DISC) engine is particularly attractive for aviation applications [3] because of its light weight, multi-fuel capability and potential for low fuel consumption. However, one disadvantage with the DISC engine is the weight and size of the liquid cooling system. NASA Lewis Research Center has supported a technology enablement program to advance the DISC rotary engine for general aviation applications and recognizes the importance of improvement in fuel consumption and reductions in the coolant system weight [4].

A new generation of Wankel rotary engines that can offer multifuel capability, increased fuel economy, and improved performance and reliability could have a profound influence on the design of future power plants for aircraft, automotive and other applications. The recent advances in adiabatic diesel engine technology have potential to improve the Wankel rotary engine. In this paper, the potential benefits of adiabatic Wankel engine and advanced concepts like- advanced turbochargers, high compression ratio, faster combustion, and reduced leakage have been assessed. A Wankel simulation model was used to predict performance of the adiabatic Wankel engine with these advanced concepts- predicting an overall improvement of 25.5% in ISFC and 34.5% in power output. Also, excellent multifuel capability of adiabatic Wankel engine is expected.

Valve wear has been identified as a major durability problem in natural gas fueled reciprocating engines. Over the years, progress has been made to alleviate this problem through improved valve design and materials development. Recently high performance ceramics have shown promise for wear component applications. This paper presents the results of a valve train component materials investigation supported by the Gas Research institute. Testing tools and methods are described. The testing program culminated in a 300 hour component test in a full size turbocharged natural gas engine. Results of the engine test appeared to confirm preceding laboratory tests. Sintered silicon nitride valve seat inserts and Stellite 6 coated 21-12 stainless steel valves appeared to be the most promising material combination evaluated.